Marginal integrity of classical and bulk-fill composite restorations in permanent and primary molars

Blend Hamza 1,✉, Marcus Zimmerman 2, Thomas Attin 2, Tobias T Tauböck 2
PMCID: PMC9372112  PMID: 35953552

Abstract

Bulk-fill composites enable timesaving and less technical-sensitive application of restorations. This study investigated and compared the marginal integrity of classical and bulk-fill composite restorations in primary and permanent molars before and after thermo-mechanical loading (TML). Two Class II cavities were prepared in each of 20 primary and 20 permanent molars. The molars were randomised in four groups for each molar type. Groups 1 and 5 were restored with a high-viscous bulk-fill composite (Tetric PowerFill), groups 2 and 6 were restored with a flowable bulk-fill composite (Tetric PowerFlow), groups 3 and 7 were restored with a high-viscous classical composite (Tetric Prime), and groups 4 and 8 were restored with a flowable classical composite (Tetric EvoFlow). In permanent molars, the flowable composites were covered with a 2-mm layer of high-viscous composite (groups 6 and 8). The restorations were subjected to TML in a custom-made chewing machine (5–50 °C, 2 min dwelling time, × 1000; 400 ,000 loading cycles, 1.7 Hz, 49 N), and quantitative marginal analysis was conducted using scanning electron microscopy. Marginal integrity of each restoration was calculated as a percentage of continuous margins before and after TML. The tested high-viscous bulk-fill restoration showed similarly high marginal integrity in primary and permanent molars as the classical restoration. The tested flowable bulk-fill restoration showed the lowest marginal integrity compared to all other restorations after TML. In contrast to flowable bulk-fill restorations, high-viscous bulk-fill restorations show similar marginal integrity as classical hybrid composite restorations after TML, in both primary and permanent molars.

Subject terms: Dental materials, Dental treatments, Paediatric dentistry, Restorative dentistry

Introduction

During the last few decades, resin-based composite restorations have increasingly pushed amalgam aside as the preferable restorative material in both permanent and primary molars1,2. Composite restorations exhibit good mechanical and tribological properties, which lead to low annual failure rate (1.1%) in vivo3–5. Classically, composite restorations were inserted in approximately 2-mm-thick layers into the tooth cavity, following the so-called “incremental layering technique”. This technique is, however, regarded as time-consuming and a possible source of air entrapment between the consecutive composite layers. To overcome the aforementioned shortcomings, bulk-fill composites, which can be inserted in up to 4–6 mm layers into the cavity, were introduced2,6. Similar to classical composite, bulk-fill composite materials are available in low- and high-viscosity forms. While some studies documented the superiority of bulk-fill composites to classical composites with regard to lower polymerisation shrinkage stress7–9 and higher marginal integrity10,11, other studies reported the opposite12,13.

The fact that bulk-fill composite materials can be inserted in large material volumes raised the concern about the resulting polymerisation shrinkage stress at the tooth-restoration interface. In addition to this volumetric shrinkage, another contributing factor to shrinkage stress is the viscoelastic behaviour of the material during polymerisation. To reduce interfacial shrinkage stresses, prepolymer stress relievers and stress-relaxant polymerization modulators have been integrated in bulk-fill composite materials. Applying an intermediate layer of low-modulus flowable composite material on the cavity walls has also been shown to reduce the shrinkage stress7,14.

It is logical to assume that the timesaving benefit, offered by bulk-fill composites, is even more advantageous when treating children compared to adults. Shorter treatment times might help achieve a better patient compliance15,16. The differences in the enamel structure between primary and permanent teeth (lower calcium and phosphate concentration, thinner thickness and occlusal direction of the cervical enamel rods for primary teeth) also lead to different behaviour when treated with adhesive systems17,18. Nevertheless, the performance of bulk-fill restorations in terms of marginal integrity and how this behaves on primary molars, in comparison to permanent molars, has not yet been investigated.

This in-vitro study was therefore carried out to investigate and compare the marginal integrity of classical and bulk-fill composite restorations in primary and permanent molars before and after artificial aging. The null-hypotheses of the study were that (1) there are no differences in the marginal integrity of the tested composite materials between primary and permanent teeth, and (2) there are no differences in the marginal integrity between the tested restorations in primary and permanent teeth.

Materials and methods

Twenty sound primary and twenty sound permanent human molars were used in this in-vitro study. Molars were extracted due to periodontitis or orthodontic reasons and were stored in 0.1% thymol solution at 4 °C until use. All patients and/or legal guardians gave their written informed consent for the use of their teeth for research purposes and all molars were irreversibly anonymised immediately after extraction. The study was therefore carried out in accordance with the Federal Act on Research involving Human Beings (Human Research Act; article 2, paragraph 2) and the authorisation from the ethics committee was waived (Zurich cantonal ethics commission, BASEC-2021-00,635). To facilitate their handling, the roots of all molars were embedded in acrylic resin (Paladur, Heraeus Kulzer, Hanau, Germany) and mounted on custom-made holders. Two standardised Class II cavities were prepared mesially and distally in each molar (mesio-occlusal and disto-occlusal cavity). The proximal cavities in primary molars were 4 mm in width, 2 mm in axial depth and 3 mm in occlusal-gingival depth. The proximal cavities in permanent molars were 5 mm in width, 3 mm in axial depth and 4 mm in occlusal-gingival depth. The width, axial depth and mesio-distal depth of the occlusal cavities were kept at 2 mm in both primary and permanent molars. Cavity preparation was carried out using 80-µm cylindrical diamond burs (Universal Prep Set, Intensiv, Grancia, Switzerland) mounted on a high-speed contra-angle handpiece (Sirius, Micro-Mega, Besançon Cedex, France) rotating at 40,000 rpm. A new bur was used after the preparation of four cavities. All cavity margins ended within enamel. Any unsupported enamel was chiseled away and enamel margins were not further beveled. The prepared molars were then randomised into eight groups (n = 10 per group; groups 1–4: primary molars, groups 5–8: permanent molars) using a computer-generated randomisation table (Microsoft Excel). A recently conducted study was used as an orientation for the here used sample size11.

For restoration, each molar was mounted on a custom-made adjacent-tooth simulator (ZPZ laboratory, Center for Dental Medicine, Zurich, Switzerland). A stainless-steel matrix band (Omni-Matrix sectional, regular, Ultradent Products, South Jordan, UT, USA) was adapted on each cavity in conjunction with a wooden wedge, which was placed 1 mm below the gingival margin. A universal adhesive was applied on enamel and dentine in self-etch mode and scrubbed for 20 s (Adhese Universal, Ivoclar Vivadent, Schaan, Liechtenstein). The adhesive was thinned, and the solvent was evaporated with a gentle blow of air. Thereafter, the adhesive was light-cured for 10 s at 1200 mW/cm2 (Bluephase G4, Ivoclar Vivadent). The cavities were then restored based on their experimental group as shown in Fig. 1. Two bulk-fill composite materials (Tetric PowerFill “high viscous” and Tetric PowerFlow “flowable”) and two classical composite materials (Tetric Prime “high viscous” and Tetric EvoFlow “flowable”) were used to restore the molars. The composition of the tested composite materials is shown in Table 1. When permanent molars were to be restored with flowable composites (groups 6 and 8), a 2-mm layer of the respective high-viscous composite (classical or bulk-fill) was applied over the polymerised flowable composite layer. Each composite layer was light-cured for 10 s at 1200 mW/cm2 (Bluephase G4, Ivoclar Vivadent) according to the manufacturer’s instructions. Care was taken to always place the tip of the polymerisation light as near as possible to the surface to be polymerised. All molars received one bulk-fill composite filling on one proximal side and a classical composite filling on the other side randomly for the mesial and distal surface. The proximal fillings were finished and polished using Sof-Lex discs with decreasing grit sizes (Sof-Lex Pop-on, 3M ESPE, St. Paul, MN, USA) under constant water-cooling. The occlusal parts of the fillings were polished using the OptraGloss system (HP flame, Ivoclar Vivadent). Polishing was carried out under a stereo microscope (× 4) and the Sof-Lex discs were replaced after polishing four proximal fillings. After completing the polishing, each filling was given a code on its respective side of the acrylic holder (BH). The restored molars were then stored in an incubator at 37 °C in tap water in the dark for 7 d.

Figure 1.

Figure 1

Open in a new tab

Study design.

Table 1.

The tested composite materials and their compositions according to the manufacturer.

Composite materials Monomers (wt%) Filler (wt%)

Tetric PowerFill

(high viscous bulk-fill)

Bis GMA, UDMA, Bis-EMA, Bis-PMA, DCP

(17–18%)

Ba-Al-Silicate glass, copolymer, ytterbium trifluoride, mixed oxide

(79–80%)

Tetric PowerFlow

(flowable bulk-fill)

Bis GMA, Bis-EMA, DCP,

(28–29%)

Ba-Al-Silicate glass, copolymer, ytterbium trifluoride

(71–72%)

Tetric Prime

(high viscous classic)

 Bis GMA, UDMA, Bis-EMA (19–20%)

Ba-Al-Silicate glass, copolymer, mixed oxide, ytterbium trifluoride

(79–80%)

Tetric EvoFlow

(flowable classic)

Bis GMA, UDMA, D3MA

(35–40%)

Ba-Al-Silicate glass, copolymer, mixed oxide, ytterbium trifluoride, silicone dioxide

(60–65%)
Open in a new tab

Bis GMA bisphenol A-diglycidyl dimethacrylate, UDMA urethane dimethacrylate, Bis-EMA ethoxylated bisphenol A dimethacrylate, Bis-PMA propoxylated bisphenol A dimethacrylate, DCP tricyclodecane-dimethanol dimethacrylate, D3MA Dicandiol dimethacrylate.

At the end of the 7-d storage time, A-silicon impressions were taken for each proximal filling (President Light Body, Coltène Whaledent, Altstätten, Switzerland). The impressions were poured out with epoxy resin (Epoxyharz L, R&G Faserverbundwerkstoffe, Waldenbuch, Germany) and fixed on aluminium holders (Cementit universal, Merz&Benteli, Niederwangen, Switzerland). The replicas were sputter-coated with gold (Sputter SCD 030, Balzers Union, Balzers, Liechtenstein) and quantitatively analysed for marginal integrity (baseline analysis) using scanning electron microscopy (SEM) at 20 kV and 200 × magnification (Amray 1810/T, Amray, Bedford, MA, USA). Marginal integrity was expressed as a percentage of the assessable continuous margins for each proximal restoration19,20. In groups where flowable composite restorations were covered with a layer of high-viscous composite, the whole proximal margin (including flowable and high-viscous composite) was analysed. This and the final margin analysis were conducted by a calibrated and experienced investigator (MZ) who was blinded to the groups and only had access to SEM images of each filling (file names = code set for each filling by BH).

After the baseline margin analysis, all fillings were subjected to simultaneous thermo- mechanical loading (TML) in a computer-controlled masticator (CoCoM 2, ZPZ, Zurich, Switzerland). The mesial and distal filling of each molar was mechanically loaded on the occlusal part (perpendicular on the mesial and distal groove) using two Empress CAD antagonists (cusp-shaped, one for each filling) for 400,000 loading cycles at 1.7 Hz and 49 N. The bath temperature inside the masticator was changed from 5 to 50 °C with 2 min dwelling time for 1000 times11.

After TML, A-silicon impressions were re-taken, and the fillings were subjected again to quantitative margin analysis (final analysis) using the same aforementioned protocol. Figure 1 summarises the study design and Fig. 2 depicts the marginal analysis of one restoration.

Figure 2.

Figure 2

Open in a new tab

SEM images (× 200) and illustration of the quantitative marginal analysis (below) for a restoration (group 1) before (left) and after thermo-mechanical loading (right). The green line indicates continuous margin segments, the red line non-continuous margin segments, and the yellow line non-assessable margin segments.

Statistical analysis

A mixed effect linear model was adopted to analyse the data. The marginal integrity was set as a target variable. The restoration material, the observation time (before vs. after TMC) and the tooth type (primary vs. permanent) were set as fixed variables and the restoration ID as a random intercept. The residual analysis did not show violations of the model assumption. Pairwise contrasts were estimated and corrected for multiple testing according to Tukey. The significance level was set at α = 0.05. Data were analysed using the statistical program R (The R Foundation for Statistical Computing; Vienna, Austria; www.R-project.org).

Results

Figure 3 depicts the percentage of the continuous margins (marginal integrity) for each experimental group.

Figure 3.

Figure 3

Open in a new tab

Mean and standard deviation of the percentage of continuous margins before and after thermo-mechanical loading (TML) for each experimental group. Same lower-case letters indicate no statistically significant difference within the same restoration material. Same capital letters indicate no statistically significant difference across all restoration materials (within the same molar type [primary or permanent] and the same observation time [before TML or after TML]).

Before TML: In primary molars, marginal integrity achieved by Tetric PowerFlow (88.8 ± 6.4%), Tetric Prime (86.7 ± 9.6%), Tetric PowerFill (82.4 ± 10.2%) and Tetric Evo Flow (76.5 ± 10.4%) were not statistically significantly different (p > 0.1). In permanent molars, marginal integrity achieved by Tetric EvoFlow (74.6 ± 12.7%), Tetric PowerFlow (73.6 ± 12.6%), Tetric PowerFill (72.3 ± 10.8%) and Tetric Prime (69.6 ± 7.9%), were also not statistically significantly different (p > 0.1). The marginal integrity in primary molars was always statistically significantly higher than that in permanent molars (p < 0.0001), regardless of the applied restoration.

After TML: All restorations showed a statistically significant reduction in their marginal integrity after TML. In primary molars, the achieved marginal integrity was as follows: Tetric PowerFill (60.1 ± 10.9%), Tetric Prime (58.0 ± 15.4%), Tetric EvoFlow (50.9 ± 13.2%) and Tetric PowerFlow (42.8 ± 12.8%). In permanent molars, the achieved marginal integrity was as follows: Tetric PowerFill (61.6 ± 10.0%), Tetric EvoFlow (59.0 ± 11.2%), Tetric Prime (52.0 ± 10.6%) and Tetric EvoFlow (46.7 ± 9.5%). In both tooth types (primary and permanent), restorations with Tetric PowerFlow showed statistically significantly lower marginal integrity compared to all other material groups (p < 0.05), which were not statistically significantly different from each other (p > 0.1).

Discussion

Bulk-fill restorations offer timesaving benefits, which enhance efficiency, and are especially advantageous when treating children. The marginal integrity of such restorations in primary molars, in comparison to permanent molars, still needed to be comprehensively investigated. The present study shows that the tested composite materials achieved similar marginal integrity in primary and permanent teeth after TML (the first null hypothesis cannot be rejected) and that only the investigated high-viscous bulk-fill restoration achieved similar marginal integrity compared to classical composite restorations in primary and permanent teeth (the second null hypothesis has to be rejected).

To the authors’ best knowledge, this is the first study to compare the marginal integrity of composite restorations in both primary and permanent molars in the same experimental setting. The cavity dimensions, especially in primary molars, were chosen to allow the application of two layers of the classical composites or one layer of the bulk-fill composites without the risk of exposing the pulp (which would clinically indicate the application of a stainless-steel crown in primary molars1,11). In permanent molars, flowable composite materials were covered with a layer of high-viscous composite to overcome the reduced mechanical properties of flowable composites, as recommended in earlier studies21–23. In all molars, enamel margins were not beveled, and a universal adhesive was applied in self-etch mode. This is also part of the whole less-steps timesaving-restoration concept. Nevertheless, it might be assumed that better marginal integrity would have been achieved in this study, had enamel been etched with phosphoric acid and/or had enamel margins been beveled24,25.

TML challenges the tooth-restoration interface and can induce the formation of marginal gaps or the progression of initially existing gaps due to the different coefficients of thermal expansion of dentine/enamel and the restoration material26. This gap formation (i.e., lack of marginal integrity) has been associated with higher risk of marginal discoloration and/or the development of secondary caries. However, this association has not yet been clinically confirmed and the development of secondary caries was reported to rather depend on patient-related factors27–29. Therefore, even if marginal integrity has been reported to be able to predict the clinical performance of a restoration to some extent, it should not be used as the only criteria to make such assumptions30.

Before TML, all groups showed higher marginal integrity in primary molars than in permanent molars. This could be attributed to the fact that the cavities in primary molars were 1 mm less deep and less wide than those in permanent molars. In case of high-viscous bulk-fill restorations, it might be assumed that a 3-mm layer (in primary molars) would produce less shrinkage stress than a 4-mm layer (in permanent molars), resulting in lower initial marginal gap formation31. In case of classical restorations, however, one might argue whether the small 0.5 mm difference in layer thickness between primary (1.5-mm layers) and permanent (2-mm layers) molars could be responsible for such finding. Here, the fact that the polymerisation light was closer to the restoration material might—better—explain the finding of superior marginal integrity. Another finding of the present study was that before TML, bulk-fill and classical restorations showed similarly high marginal integrity in each molar type. This was also previously reported for primary teeth by Paganini et al.11. Furthermore, no differences between the tested flowable bulk-fill composite and the high-viscous bulk-fill composite was noticed in terms of marginal integrity before TML. A similar finding in terms of interfacial gap was also reported in a previous study without mechanical loading of the tested bulk-fill composite materials32.

After TML, all experimental groups showed a reduction in their marginal integrity. The higher marginal integrity observed in primary molars before TML could not be preserved after TML. However, all groups still showed similarly high marginal integrity in primary and permanent molars. The tested high-viscous bulk-fill composite (Tetric PowerFill) offered similarly high marginal integrity as the classical restorations in primary and permanent molars. This performance of high-viscous bulk-fill restorations is well established and reported in previous studies with permanent teeth33. On the other hand, the tested flowable bulk-fill composite (Tetric PowerFlow) showed the lowest marginal integrity in primary and permanent molars. This could be explained by the inferior mechanical properties of this type of composites (e.g., lower surface hardness and lower modulus of elasticity)34. This finding in primary molars was also reported in an earlier study, where the placed flowable bulk-fill restorations also showed lower marginal integrity in comparison to high-viscous classical and bulk-fill restorations after TML11. The same finding was also reported in other studies in permanent molars35,36. Contrary findings, which reported similar marginal integrity of flowable bulk-fill composite restorations as classical and/or high-viscous bulk-fill restorations were, however, also reported34,37. Different cavity preparations, TML protocols and material properties could be responsible for these different observations.

Based on the results of this in-vitro study and within its limits, it can be concluded that the tested high-viscous bulk-fill composite shows comparable marginal integrity as classical composite materials in both primary and permanent molars, before and after thermo-mechanical loading. This does not apply to the flowable bulk-fill composite under investigation, which shows similarly high marginal integrity as the other composite materials only before thermo-mechanical loading. After TML, all restorations placed in primary teeth achieved similar marginal integrity as in permanent teeth, which adds to their suitability in paediatric dentistry.

Acknowledgements

This study and the tested materials were supported/offered by a grant from Ivoclar. The company had no influence on the conduction of the study, nor on the interpretation of its results.

Author contributions

B.H. Funding acquisition, methodology, investigation, writing—original draft; M.Z. methodology, investigation; T.A. Funding acquisition, conceptualization, methodology, writing—review & editing, supervision; T.T.: Funding acquisition, conceptualization, methodology, writing—review & editing, supervision.

Data availability

The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.

Competing interests

The authors declare no competing interests.

Footnotes

Publisher's note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

References

  • 1.American Academy of Pediatric Dentistry. Pediatric Restorative Dentistry. The Reference Manual of Pediatric Dentistry. Chicago, Ill.: American Academy of Pediatric Dentistry 371–83 (2020).
  • 2.Arbildo-Vega HI, et al. Clinical effectiveness of bulk-fill and conventional resin composite restorations: Systematic review and meta-analysis. Polymers. 2020;12:1786. doi: 10.3390/polym12081786. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 3.Tauböck TT, Schmidlin PR, Attin T. Vertical bite rehabilitation of severely worn dentitions with direct composite restorations: Clinical performance up to 11 years. J. Clin. Med. 2021;10:1732. doi: 10.3390/jcm10081732. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 4.Pallesen U, van Dijken JW. A randomized controlled 30 years follow up of three conventional resin composites in Class II restorations. Dent. Mater. 2015;31:1232–1244. doi: 10.1016/j.dental.2015.08.146. [DOI] [PubMed] [Google Scholar]
  • 5.Loomans BAC, et al. Clinical performance of full rehabilitations with direct composite in severe tooth wear patients: 3.5 years results. J. Dent. 2018;70:97–103. doi: 10.1016/j.jdent.2018.01.001. [DOI] [PubMed] [Google Scholar]
  • 6.Kwon Y, Ferracane J, Lee IB. Effect of layering methods, composite type, and flowable liner on the polymerization shrinkage stress of light cured composites. Dent. Mater. 2012;28:801–809. doi: 10.1016/j.dental.2012.04.028. [DOI] [PubMed] [Google Scholar]
  • 7.Tauböck TT, Jäger F, Attin T. Polymerization shrinkage and shrinkage force kinetics of high- and low-viscosity dimethacrylate- and ormocer-based bulk-fill resin composites. Odontology. 2019;107:103–110. doi: 10.1007/s10266-018-0369-y. [DOI] [PubMed] [Google Scholar]
  • 8.Ilie N, Hickel R. Investigations on a methacrylate-based flowable composite based on the SDR™ technology. Dent. Mater. 2011;27:348–355. doi: 10.1016/j.dental.2010.11.014. [DOI] [PubMed] [Google Scholar]
  • 9.El-Damanhoury H, Platt J. Polymerization shrinkage stress kinetics and related properties of bulk-fill resin composites. Oper. Dent. 2014;39:374–382. doi: 10.2341/13-017-L. [DOI] [PubMed] [Google Scholar]
  • 10.Hirata R, et al. Shrinkage assessment of low shrinkage composites using micro-computed tomography. J. Biomed. Mater. Res. B Appl. Biomater. 2015;103:798–806. doi: 10.1002/jbm.b.33258. [DOI] [PubMed] [Google Scholar]
  • 11.Paganini A, Attin T, Tauböck TT. Margin integrity of bulk-fill composite restorations in primary teeth. Materials. 2020;13:3802. doi: 10.3390/ma13173802. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 12.Peutzfeldt A, Mühlebach S, Lussi A, Flury S. Marginal gap formation in approximal "bulk fill" resin composite restorations after artificial ageing. Oper. Dent. 2018;43:180–189. doi: 10.2341/17-068-L. [DOI] [PubMed] [Google Scholar]
  • 13.Van Ende A, De Munck J, Lise DP, Van Meerbeek B. Bulk-Fill composites: A review of the current literature. J. Adhes. Dent. 2017;19:95–109. doi: 10.3290/j.jad.a38141. [DOI] [PubMed] [Google Scholar]
  • 14.Braga RR, Ballester RY, Ferracane JL. Factors involved in the development of polymerization shrinkage stress in resin-composites: A systematic review. Dent. Mater. 2005;21:962–970. doi: 10.1016/j.dental.2005.04.018. [DOI] [PubMed] [Google Scholar]
  • 15.Aminabadi NA, Oskouei SG, Farahani RM. Dental treatment duration as an indicator of the behavior of 3-to 9-year-old pediatric patients in clinical dental settings. J. Contemp. Dent. Pract. 2009;10:E025–032. [PubMed] [Google Scholar]
  • 16.Katre AN. Assessment of the correlation between appointment scheduling and patient satisfaction in a pediatric dental setup. Int. J. Dent. 2014;2014:453237. doi: 10.1155/2014/453237. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 17.Wilson PR, Beynon AD. Mineralization differences between human deciduous and permanent enamel measured by quantitative microradiography. Arch. Oral Biol. 1989;34:85–88. doi: 10.1016/0003-9969(89)90130-1. [DOI] [PubMed] [Google Scholar]
  • 18.Cleghorn BM, Boorberg NB, Christie WH. Primary human teeth and their root canal systems. Endod. Top. 2010;23:6–33. doi: 10.1111/etp.12000. [DOI] [Google Scholar]
  • 19.Bortolotto T, Doudou W, Kunzelmann KH, Krejci I. The competition between enamel and dentin adhesion within a cavity: An in vitro evaluation of class V restorations. Clin. Oral Investig. 2012;16:1125–1135. doi: 10.1007/s00784-011-0623-y. [DOI] [PubMed] [Google Scholar]
  • 20.Frankenberger R, et al. Effect of proximal box elevation with resin composite on marginal quality of ceramic inlays in vitro. Clin. Oral Investig. 2013;17:177–183. doi: 10.1007/s00784-012-0677-5. [DOI] [PubMed] [Google Scholar]
  • 21.Tomaszewska IM, Kearns JO, Ilie N, Fleming GJ. Bulk fill restoratives: To cap or not to cap-that is the question? J. Dent. 2015;43:309–316. doi: 10.1016/j.jdent.2015.01.010. [DOI] [PubMed] [Google Scholar]
  • 22.de Assis FS, et al. Evaluation of bond strength, marginal integrity, and fracture strength of bulk- vs incrementally-filled restorations. J. Adhes. Dent. 2016;18:317–323. doi: 10.3290/j.jad.a36516. [DOI] [PubMed] [Google Scholar]
  • 23.Ilie N, Bucuta S, Draenert M. Bulk-fill resin-based composites: An in vitro assessment of their mechanical performance. Oper. Dent. 2013;38:618–625. doi: 10.2341/12-395-L. [DOI] [PubMed] [Google Scholar]
  • 24.Swanson TK, Feigal RJ, Tantbirojn D, Hodges JS. Effect of adhesive systems and bevel on enamel margin integrity in primary and permanent teeth. Pediatr. Dent. 2008;30:134–140. [PubMed] [Google Scholar]
  • 25.Fröhlich TT, Gindri LD, Soares FZM, de Oliveira Rocha R. Does the etching strategy influence the bonding of universal adhesive systems to primary teeth? A systematic review and meta-analysis of in vitro studies. Eur. Arch. Paediatr. Dent. 2021;22:1015–1022. doi: 10.1007/s40368-021-00639-w. [DOI] [PubMed] [Google Scholar]
  • 26.Ebaya MM, Ali AI, Mahmoud SH. Evaluation of marginal adaptation and microleakage of three glass ionomer-based class V restorations: In vitro study. Eur. J. Dent. 2019;13:599–606. doi: 10.1055/s-0039-3401435. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 27.Heintze SD. Systematic reviews: I. The correlation between laboratory tests on marginal quality and bond strength. II. The correlation between marginal quality and clinical outcome. J. Adhes. Dent. 2007;9(Suppl 1):77–106. [PubMed] [Google Scholar]
  • 28.Heintze SD. Clinical relevance of tests on bond strength, microleakage and marginal adaptation. Dent. Mater. 2013;29:59–84. doi: 10.1016/j.dental.2012.07.158. [DOI] [PubMed] [Google Scholar]
  • 29.Nedeljkovic I, Teughels W, De Munck J, Van Meerbeek B, Van Landuyt KL. Is secondary caries with composites a material-based problem? Dent. Mater. 2015;31:e247–277. doi: 10.1016/j.dental.2015.09.001. [DOI] [PubMed] [Google Scholar]
  • 30.Frankenberger R, Krämer N, Lohbauer U, Nikolaenko SA, Reich SM. Marginal integrity: Is the clinical performance of bonded restorations predictable in vitro? J. Adhes. Dent. 2007;9(Suppl 1):107–116. [PubMed] [Google Scholar]
  • 31.Par M, Marovic D, Attin T, Tarle Z, Tauböck TT. Effect of rapid high-intensity light-curing on polymerization shrinkage properties of conventional and bulk-fill composites. J. Dent. 2020;101:103448. doi: 10.1016/j.jdent.2020.103448. [DOI] [PubMed] [Google Scholar]
  • 32.Comba A, et al. Influence of curing mode and layering technique on the 3D interfacial gap of bulk-fill resin composites in deep class-I restorations: A micro-CT volumetric study. J. Adhes. Dent. 2021;23:421–428. doi: 10.3290/j.jad.b2000229. [DOI] [PubMed] [Google Scholar]
  • 33.Heintze SD, Monreal D, Peschke A. Marginal quality of class II composite restorations placed in bulk compared to an incremental technique: Evaluation with SEM and stereomicroscope. J. Adhes. Dent. 2015;17:147–154. doi: 10.3290/j.jad.a33973. [DOI] [PubMed] [Google Scholar]
  • 34.Gerula-Szymańska A, Kaczor K, Lewusz-Butkiewicz K, Nowicka A. Marginal integrity of flowable and packable bulk fill materials used for class II restorations: A systematic review and meta-analysis of in vitro studies. Dent. Mater. J. 2020;39:335–344. doi: 10.4012/dmj.2018-180. [DOI] [PubMed] [Google Scholar]
  • 35.Par M, et al. Rapid high-intensity light-curing of bulk-fill composites: A quantitative analysis of marginal integrity. J. Dent. 2021;111:103708. doi: 10.1016/j.jdent.2021.103708. [DOI] [PubMed] [Google Scholar]
  • 36.Jung JH, Park SH. Comparison of polymerization shrinkage, physical properties, and marginal adaptation of flowable and restorative bulk fill resin-based composites. Oper. Dent. 2017;42:375–386. doi: 10.2341/16-254-L. [DOI] [PubMed] [Google Scholar]
  • 37.Park KJ, et al. Evaluation of low-viscosity bulk-fill composites regarding marginal and internal adaptation. Odontology. 2021;109:139–148. doi: 10.1007/s10266-020-00531-x. [DOI] [PMC free article] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Data Availability Statement

The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.

Articles from Scientific Reports are provided here courtesy of Nature Publishing Group

RESOURCES