Hydrothermal synthesis of CuO@MnO2 on nitrogen-doped multiwalled carbon nanotube composite electrodes for supercapacitor applications

Vijay Kakani 1, Sivalingam Ramesh 2, H M Yadav 3, Chinna Bathula 4, Praveen Kumar Basivi 5, Ramasubba Reddy Palem 6, Heung Soo Kim 2, Visweswara Rao Pasupuletti 7,8, Handol Lee 9,✉, Hakil Kim 10,✉
PMCID: PMC9489798  PMID: 36127493

Abstract

Nitrogen-doped multiwalled carbon nanotubes (N-MWCNTs) have been used to fabricate nanostructured materials for various energy devices, such as supercapacitors, sensors, batteries, and electrocatalysts. Nitrogen-doped carbon-based electrodes have been widely used to improve supercapacitor applications via various chemical approaches. Based on previous studies, CuO@MnO2 and CuO@MnO2/N-MWCNT composites were synthesized using a sonication-supported hydrothermal reaction process to evaluate their supercapacitor properties. The structural and morphological properties of the synthesized composite materials were characterized via Raman spectroscopy, XRD, SEM, and SEM–EDX, and the morphological properties of the composite materials were confirmed by the nanostructured composite at the nanometer scale. The CuO@MnO2 and CuO@MnO2/N-MWCNT composite electrodes were fabricated in a three-electrode configuration, and electrochemical analysis was performed via CV, GCD, and EIS. The composite electrodes exhibited the specific capacitance of ~ 184 F g−1 at 0.5 A g−1 in the presence of a 5 M KOH electrolyte for the three-electrode supercapacitor application. Furthermore, it exhibited significantly improved specific capacitances and excellent cycling stability up to 5000 GCD cycles, with a 98.5% capacity retention.

Subject terms: Chemical synthesis, Supercapacitors

Introduction

Recently, electronic devices for storage applications comprising nanometer-scale materials with excellent capacitance and cyclic stability are being rapidly developed. Numerous methods for fabricating electrode materials for practical applications have been reported in various supercapacitor, battery, and fuel-cell studies1–4. In particular, supercapacitors have received considerable attention owing to their excellent life cycles and high-power density results. Supercapacitors can be categorized as electric double-layer capacitors (EDLC) and pseudocapacitors, depending on their complex electrochemical reaction. In the case of the EDLCs, energy is collected by the electrostatic adsorption of charges on the electrode surface in the parallel plate capacitor. In pseudocapacitors, energy is collected via reversible Faradaic responses on the material electrode surface5–8.

Carbon-based electrode materials are an appropriate choice for supercapacitor applications because of their excellent specific capacitance and power density9–11. An alternative approach is to use potential electrode materials such as Co3O4, MnO2, NiO, CuO, Fe3O4 and V2O5, which have been widely used in supercapacitor applications12–15. The higher specific capacitance of these materials is because of the presence of metal oxides, which exhibit more pronounced redox behavior than the carbon in carbon-based electrodes; thus, a specific capacitance and excellent electrochemical stability are realized via irreversible reactions16–18. Notably, copper is an excellent electrode material because it is nontoxic, abundantly available, low-cost, and easy to fabricate into an electrode for supercapacitor applications17–19. Zhang et al. reported that flower-like CuO nanostructured materials yielded a capacitance value of 134 F g−1 in the presence of a 1 M KOH electrolyte18. In addition, mesoporous copper oxide nanoribbons were fabricated on nickel foam electrodes, with a capacitance of 137 F g−1. Wang et al. fabricated nanosheets with a capacitance of ~ 569 F g−119.

MnO2 has emerged as a promising electrode material for supercapacitor applications owing to its high theoretical specific capacitance, high electrochemical activity, and environmental friendliness20–22. However, the low conductivity (10−5 to 10−6 S cm−1) and unstable structure of MnO2, which causes poor electrochemical cyclability, limits its application. To address these limitations and improve the electrochemical behavior of supercapacitors, several studies have attempted to design nano-MnO2 structures. It has been reported that the electrochemical performance of MnO2 depends on its morphology, surface area, and crystal structure. Zhang et al. reported MnO2-based electrodes for supercapacitors with different crystal structures and morphological behaviors synthesized via a hydrothermal process. Nano-a-MnO2 ball with a low degree of crystallinity exhibited a high specific capacitance of 200 F g−1 and excellent cyclic stability. Rusi et al. also synthesized a-MnO2 with a low-crystalline electrode via electrochemical deposition using a manganese acetate tetrahydrate electrolyte. The assembled MnO2 electrode, characterized via a cyclic voltammetry test in the Na2SO4 electrolyte at a scan rate of 1 mV s−1, exhibited a high specific capacitance of 238 F g−1 and excellent stability, with an 84% capacitance retention over 1900 cycles. By contrast, CuO, which is an active material that contributes to pseudocapacitance, possesses a high specific surface area, is highly conductive and environmentally friendly, and can be incorporated with MnO2. Furthermore, the synergetic effect also plays an important role in improving the performance of the MnO2–CuO composite on the carbon surface. Therefore, a material comprising both MnO2 and CuO will exhibit better electrochemical performance, conductivity, cycling stability, and morphological properties than individual MnO2 and CuO materials. Therefore, this study focused on CuO@MnO2 and CuO@MnO2/N-multiwalled carbon nanotube (MWCNT) composites synthesized via a hydrothermal reaction process using a three-electrode configuration for supercapacitor applications. The nanocrystalline structure and morphological properties of the resulting composites were investigated via FE-SEM. In addition, the electrochemical properties of the composite electrodes were analyzed using CV, GCD, and EIS in the presence of a 5M KOH electrolyte.

Experimental methods

Materials

MWCNTs, copper nitrate penta hydrate Cu(NO3)2·5H2O, potassium permanganate (KMnO4), manganese (II) acetate (C4H6MnO4), hydrochloric acid (HCl), sulfuric acid (H2SO4), phosphoric acid (H3PO4), ammonia (NH3, 30%), absolute ethanol (C2H5OH), N-methyl pyrrolidinone (NMP), and polyvinylidene fluoride (PVDF) were obtained from Sigma-Aldrich Chemicals, and the overall electrochemical experiments were performed using double distilled (DD) water.

Synthesis of CuO@MnO2/N-MWCNT composite

The required MWCNT and nitrogen-doped MWCNT syntheses are described in our previous reports20,21. In summary, to synthesize the CuO@MnO2 composite, 0.65 of N-MWCNTs was diffused in 200 mL of double DD water via sonication for 2 h to achieve complete dispersion of the tubes. For this, 0.3 moles of copper nitrate CuSO4·5H2O and 0.3M manganese acetate/KMnO4 were added, followed by 20 mL of 30% ammonia, and the solution was stirred at 90 °C for 12 h. At this point, the reaction mixture was transferred to an autoclave reactor, and the hydrothermal reaction was carried out at 200 °C for 8 h. The precipitated CuO@MnO2/N-MWCNT composite material was filtered and washed repetitively with a 1:1 solution of DD water/ethanol and purified at 90 °C for 12 h. The dried composite was stored in an airtight bottle and subjected to structural, morphological, and electrochemical analyses. A schematic of the CuO@MnO2/N-MWCNT composite synthesis is shown in Fig. 1.

Figure 1.

Figure 1

Open in a new tab

Schematic of the CuO@MnO2/N-MWCNT composite synthesis process.

Fabrication of electrodes for supercapacitor study

The composite was fabricated via a three-electrode configuration and its electrochemical properties were determined using CV, GCD, and EIS analyses. The material (85:15:5) was mixed with N-methyl pyrrolidinone (NMP) using a uniform paste. Subsequently, this composite paste was coated uniformly on a strip of a nickel wire (1 × 1 cm−2) current collector and vacuum-dried in an oven at 90 °C for 10 h. The fabricated working electrode, Pt electrode (counter electrode), and a reference electrode (Ag/AgCl) were used to study the electrochemical properties of the synthesized composite materials.

Materials characterization

The synthesized CuO@MnO2 and CuO@MnO2/NMWCNT composite materials were characterized using Raman, XRD, SEM, SEM–EDS, TEM, and CV analyses for supercapacitor application. XRD results of the composite materials were obtained using a Rigaku Rotaflex (RU-200B) X-ray diffractometer. The composite materials were analyzed using a He–Ne laser beam in the RM 200 Raman spectral microscope, and the morphological properties of the composite samples were determined using FE-SEM (JEOL) and SEM–EDX analyses. The electrochemical properties of the composite materials were determined based on CV, GCD and EIS results via CHI 7081C (CH Instruments, workstation Inc., USA).

Results and discussion

Structural properties

Figure 2a shows the diffraction patterns of the CuO@MnO2/N-MWCNT composite material for supercapacitor applications. The peaks marked in green at 28.50°, 37.30°, 42.80°, 56.80°, 59.40°, and 72.50° corresponding to the (100), (101), (111), (113), (200), (220), (202), (400), (211), (220), (330), (400), and (420) planes of MnO2, respectively, matched with the data in PDF file no.44-0141. The 2θ peaks marked in red at 30.50°, 32.50°, 35.50°, 38.70°, 48.80°, 53.25°, 58.65°, 61.50°, 66.20°, 68.10°, 72.40°, and 75.20° corresponded to (110) (111) (202) (112), (020), (202), (113), (311), and (004) planes, respectively. The obtained results agreed with those of the CuO (JCPDS file no. 72-0629) monoclinic structure in the composite materials. In this XRD pattern, CuO@MnO2 was decorated on the N-MWCNT surface. Therefore, the MnO2/CuO in the composite materials was recognized as MnO2 with cubic and monoclinic CuO structure20,21.

Figure 2.

Figure 2

Open in a new tab

(a) XRD and (b) Raman spectra of the CuO@MnO2/N-MWCNT composite.

The Raman spectra of the composites are shown in Fig. 2b. The Raman shifts at ∼ 1343, ∼ 1570, and 2450 cm−1 were ascribed to the three distinct peaks of the N-MWCNT composite. The D band was assigned to the lattice defect of the phonon mode of vibration from the N-MWCNT surface. The G band signifies the C–C (vibrational modes) and double-degenerate phonon modes of E2g symmetry. The G band is associated with the vibrational modes of the sp2-bonded carbon atoms in the graphitic layer from the N-MWCNT, whereas the D band is associated with the breathing mode of sp2 bonding, which is present in disordered graphite. We observed that N doping enhanced the D-band intensity of the composite sample. The peak intensity ratio between the D and G bands (ID/IG) was 1.05 for the pristine N-MWCNT [ref], and 1.28 and 1.30, respectively, for the composite samples. This D enhancement indicates that N doping produces lattice defects in the graphitic layers11,22,23. The lower wave region of the metal oxides was formed with less intense Ag, Bg1, and Bg2 vibration modes, as discussed previously for metal oxide materials24–27.

Morphological properties of the CuO@MnO2 composite

The surface morphology of the composite was studied using SEM and SEM–EDS, and the results are shown in Figs. 3 and 4, respectively. The results revealed that the N-MWCNT tubes and CuO@MnO2 exhibited well-decorated nanotubes with an outer diameter of about ~ 20–30 nm and an inner thickness of ~ 10–20 nm (Fig. 4e). The SEM–EDS morphology of the composite is shown in (Supplementary Fig. S1). The results confirmed that C, O, N, Cu, and MnO2 were present in the synthesized composite materials. The morphological behavior of CuO- and MnO2-based materials has been previously reported in the literature28–30.

Figure 3.

Figure 3

Open in a new tab

(a–d) SEM morphology of the CuO@MnO2 composite.

Figure 4.

Figure 4

Open in a new tab

(a–e) SEM morphology of the CuO@MnO2/N-MWCNT composite.

Electrochemical properties of the composite electrodes

The electrochemical properties of MnO2 and CuO oxides, and carbon-based materials have been investigated in several studies31,32, as these materials have potential electrode properties and cyclic stability, rendering them suitable for supercapacitor applications. In this study, the fabrication of CuO@MnO2 and CuO@MnO2/N-MWCNT composites was examined using a three-electrode configuration in the presence of a 5 M KOH electrolyte, and the results are shown in Figs. 5 and 6. The CV results for the composite are presented in Figs. 5 and 6a. The redox peaks were clearly observed for the CuO@MnO2 and CuO@MnO2/N-MWCNT composites. The excellent redox behavior of the composites was attributed to the reversible redox reaction between the active electrode materials and the electrolyte. The altered scan rates applied from the (10 to 100) mV/s results indicate that a similar trend of the electrochemical behaviors and rate capabilities occurred in the presence of the 5 M KOH electrolyte. The obtained results became more pronounced with scan rates and peak shifts toward positive and negative potentials owing to the polarization effect and electron transfer rates between the Cu and Mn oxides on the carbon surface33–37. The improved electrochemical behavior was strongly related to the chemical composition and morphology of the synthesized composite or 5 M KOH electrolyte for supercapacitor applications38,39.

Figure 5.

Figure 5

Open in a new tab

Results of electrochemical CV analysis. (a) CV; (b) GCD; (c) variation of specific capacitance with current density; (d) cyclic stability; and (e) EIS of the CuO@MnO2 composite electrode.

Figure 6.

Figure 6

Open in a new tab

Results of electrochemical CV analysis. (a) CV; (b) GCD; (c) variation of specific capacitance with current density; (d) cyclic stability; and (e) EIS of the CuO@MnO2/N-MWCNT composite electrode.

GCD analysis was performed at current densities of 0.5, 1.0, 1.5, 2 and 2.5 A g−1 in the 0.0–0.6 V range, and the results are shown in Figs. 5b and 6b. The specific capacitance values were calculated using the equations reported in a previous study40,41. The composite electrodes exhibit triangular forms, which indicate reversible redox reactions in the electrochemical process. The outcome capacitance values of CuO@MnO2 were calculated as 61.54, 53.8, 46.15, 27.69 and 26.90 F g−1 at current densities of 0.5, 1.0, 1.5, 2, and 2.5 A g−1, respectively. The CuO@MnO2/N-MWCNT composite yields values of 184, 165,154, 125, and 116 F g−1 at the same current density. The variation of specific capacitance with current density is shown in Figs. 5c and 6c. The increase in specific capacitance was almost threefold owing to the interaction of the metal oxide nanoparticles with the nitrogen-doped carbon nanotubes. The cyclic stabilities of the composite electrodes prepared from the composites are shown in Figs. 5d and 6d. This result reveals that the GCD test was performed at a current density of 0.5 A g−1 for 5000 cycles. The specific capacitance of the composite electrode was 98.5% of its initial value, indicating the excellent stability retention and the performance of the composite electrode materials in terms of enhanced electrochemical properties with a 5 M KOH electrolyte. The unique morphologies of the synthesized composite materials may prevent aggregation and volume expansion during long-term cycling, which is useful for achieving structural stability of the electrodes42,43.

The results revealed that the synthesized composites exhibited superior specific capacitance values compared with those fabricated in previous studies (Table 1). The improvement in the specific capacitance of the CuO@MnO2 and CuO@MnO2/N-MWCNT composite electrodes resulted from the surface properties and improved morphological properties of the electrodes. The specific capacitances of the CuO@MnO2 and CuO@MnO2/N-MWCNT composite electrode materials were better than those of other electrodes with previously reported materials, as shown in Table 142,43. The improvement in the electrochemical properties depends on the Faradaic redox reactions of the Cu (I)/Cu(II) and Mn (Mn2+) transitions and increases the capacitances, facilitating supercapacitor applications43,44. Furthermore, the electrochemical behaviors of the synthesized CuO@MnO2 andCuO@MnO2/N-MWCNT composite electrodes were studied via impedance spectroscopy (EIS) analysis, and the fabricated electrodes of composite (EIS) results are presented in Figs. 5e and 6e. The composite showed excellent electrochemical properties in the lower frequency region in the presence of the electrolyte, indicating that the electrochemical capacitive behavior of the composite electrode materials determines the parameters that affect the electrochemical performances45–47. Furthermore, the Cu2+/Cu+ and Mn2+ to Mn+ redox reactions improve the electrochemical behavior of the electrode materials in the lower wave frequency region, making these composites potentially suitable for supercapacitor applications48–53.

Table 1.

Comparison of the electrochemical properties of the synthesized CuO@MnO2 and CuO@MnO2/N-MWCNT composite with those of composite materials reported in the literature.

Synthesized composites Fabrication methods Capacitance (F g−1) Cyclic stability Ref.
Cu2O/MOF carbon composite Simple one step polyol method 151 F g−1 at 1 10% loss after 2500 cycles 49
CuO/NIO/RGO composite Sonication assisted solvothermal process 395 F g−1 at 0.5 A g−1 11% loss after 5000 cycles 50
MWCNT/NiO/PPY composite Thermal reduction process 239.5 F g−1 at 0.5 A g−1 2.68% loss after 1000 cycles 51
MnO2/CuO core shell materials One step hydrothermal process 167.2 F g−1 at 0.3 A g−1 11.4% loss after 5000 cycles 52
Leaf like CuO-Cu2O electrode One step anodization method 1.954 F cm−2 at 2 A.g−1 19.5% loss after 2000 cycles 53
Flower like CuO Chemical precipitation method 133.6 F g−1 at 2 A g−1 5.2% loss after 200 cycles 54
MnO2/CNT/CP composite Chemical vapor deposition 200 F g−1 at 1 m A/cm2 1% loss after 1000 cycles 55
CuO@MnO2/N-MWCNT composite Sonication supported hydrothermal synthesis 184 F g−1 at 0.5A g−1 1.5% loss after 5000 cycles Current study
Open in a new tab

Conclusion

CuO@MnO2 and CuO@MnO2/N-MWCNT composites synthesized via a sonication-assisted process and hydrothermal reaction process exhibited excellent morphological properties and improved electrochemical behavior. The moreover, the CuO@MnO2/N-MWCNT composite electrodes exhibited excellent electrochemical properties with a high specific capacitance of 184 F g−1 at a current density of 0.5 A g−1 in the presence of 5 M KOH electrolytes. In particular, a capacity retention of 98.5% at 0.5 A g−1 was maintained over 5000 continuous GCD cycles. This enhancement in the electrochemical properties of the material was attributed to the surface properties and improved morphological behavior of the material. The synthesized composite electrodes exhibited excellent electrochemical, morphological, and cyclic stabilities, rendering them suitable for supercapacitor applications.

Supplementary Information

Supplementary Figure S1. (95.2KB, docx)

Author contributions

Conceptualization: V.K. and S.R.; draft preparation: V.K. and S.R.; execution: V.K. and S.R.; data analysis: H.M.Y., C.B., R.R.P., H.S.K., P.K.B., and V.R.P.; draft editing and review: V.K., S.R., and H.L.; validation and supervision: S.R., H.L., and H.K.

Data availability

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.

Competing interests

The authors declare no competing interests.

Footnotes

Publisher's note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Contributor Information

Handol Lee, Email: leehd@inha.ac.kr.

Hakil Kim, Email: hikim@inha.ac.kr.

Supplementary Information

The online version contains supplementary material available at 10.1038/s41598-022-16863-3.

References

  • 1.Lou XW, Archer LA, Yang Z. Hollow micro-/nanostructures: Synthesis and applications. Adv. Mater. 2008;20:3987–4019. doi: 10.1002/adma.200800854. [DOI] [Google Scholar]
  • 2.Wang G, Zhang L, Zhang J. A review of electrode materials for electrochemical super-capacitors. Chem. Soc. Rev. 2012;41:797–828. doi: 10.1039/C1CS15060J. [DOI] [PubMed] [Google Scholar]
  • 3.Ouyang L, Hsiao C-H, Chen Y-C, Lee CY, Tai NH. Fabrication of Ni-Mn LDH/Co3O4 on carbon paper for the application in supercapacitors. Surf. Interface. 2021;28:101574. doi: 10.1016/j.surfin.2021.101574. [DOI] [Google Scholar]
  • 4.Fan Z, et al. Asymmetric supercapacitors based on graphene/MnO2 and activated carbon nanofiber electrodes with high power and energy density. Adv. Funct. Mater. 2011;21:2366–2375. doi: 10.1002/adfm.201100058. [DOI] [Google Scholar]
  • 5.Ramesh S, et al. Core shell nanostructured of Co3O4@RuO2 assembled on nitrogen-doped graphene sheets electrode for an efficient supercapacitor application. J. Alloy. Compd. 2021;877:160297–160297. doi: 10.1016/j.jallcom.2021.160297. [DOI] [Google Scholar]
  • 6.Racik M, et al. Fabrication of manganese oxide decorated copper oxide (MnO2/CuO) nanocomposite electrodes for energy storage supercapacitor devices. Physica E. 2020;119:114033. doi: 10.1016/j.physe.2020.114033. [DOI] [Google Scholar]
  • 7.Lei Z, Zhang J, Zhao XS. Ultrathin MnO2 nanofibers grown on graphitic carbon spheres as high-performance asymmetric supercapacitor electrodes. J. Mater. Chem. A. 2012;22:153–160. doi: 10.1039/C1JM13872C. [DOI] [Google Scholar]
  • 8.Ramesh S, et al. Nanostructured CuO/Co2O4@ nitrogen doped MWCNT hybrid composite electrode for high-performance supercapacitors. Compos. B Eng. 2019;166:74–85. doi: 10.1016/j.compositesb.2018.11.116. [DOI] [Google Scholar]
  • 9.Bathula C, Rabani I, Ramesh S. Highly efficient solid-state synthesis of Co3O4 on multiwalled carbon nanotubes for supercapacitors. J. Alloy. Compd. 2021;887:161307–161307. doi: 10.1016/j.jallcom.2021.161307. [DOI] [Google Scholar]
  • 10.Li Q, et al. Design and synthesis of MnO2/Mn/MnO2 sandwich-structured nanotube arrays with high super capacitive performance for electrochemical energy storage. Nano Lett. 2012;12:3803–3830. doi: 10.1021/nl301748m. [DOI] [PubMed] [Google Scholar]
  • 11.Zhang H, Zhang M. Synthesis of CuO nanocrystalline and their application as electrode materials for capacitors. Mater. Chem. Phys. 2008;108:184–188. doi: 10.1016/j.matchemphys.2007.10.005. [DOI] [Google Scholar]
  • 12.Khan MA, Wahab Y, Muhammad R, Tahir M, Sakrani S. Catalyst-free fabrication of novel ZnO/CuO Core-Shell nanowires heterojunction: Controlled growth, structural and optoelectronic properties. Appl. Surf. Sci. 2018;435:718–732. doi: 10.1016/j.apsusc.2017.11.071. [DOI] [Google Scholar]
  • 13.Ramesh S, et al. Fabrication of nanostructured SnO2@Co3O4/nitrogen doped graphene oxide composite for symmetric and asymmetric storage devices. J. Mater. Res. Technol. 2020;9:4183–4193. doi: 10.1016/j.jmrt.2020.02.045. [DOI] [Google Scholar]
  • 14.Ramesh S, Karuppasamy K, Kim HS, Kim HS, Kim J-H. Hierarchical flowerlike 3D nanostructure of Co3O4@MnO2/N-doped graphene oxide (NGO) hybrid composite for a high-performance supercapacitor. Sci. Rep. 2018;8:16543. doi: 10.1038/s41598-018-34905-7. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 15.Zhang YX, Li F, Huang M. One-step hydrothermal synthesis of hierarchical MnO2-coated CuO flower-like nanostructures with enhanced electrochemical properties for supercapacitor. Mater. Lett. 2013;112:203–206. doi: 10.1016/j.matlet.2013.09.032. [DOI] [Google Scholar]
  • 16.Feng Q, Kanoh H, Ooi K. Manganese oxide porous crystals. J. Mater. Chem. 1999;9(2):319–333. doi: 10.1039/a805369c. [DOI] [Google Scholar]
  • 17.Zhou Y, Cheng X, Tynan B, Sha Z, Huang F, Islam MS, et al. High-performance hierarchical MnO2/CNT electrode for multifunctional supercapacitors. Carbon. 2021;184:504–513. doi: 10.1016/j.carbon.2021.08.051. [DOI] [Google Scholar]
  • 18.Toupin M, Brousse T, Bélanger D. Charge storage mechanism of MnO2 electrode used in aqueous electrochemical capacitor. Chem. Mater. 2004;16(16):3184–3190. doi: 10.1021/cm049649j. [DOI] [Google Scholar]
  • 19.Gueon D, Moon JH. Nitrogen-doped carbon nanotube spherical particles for supercapacitor applications: Emulsion-assisted compact packing and capacitance enhancement. ACS Appl. Mater. Interfaces. 2015;7:20083–20089. doi: 10.1021/acsami.5b05231. [DOI] [PubMed] [Google Scholar]
  • 20.Huang M, Li F, Dong F, Zhang YX, Zhang LL. MnO2-based nanostructures for high-performance supercapacitors. J. Mater. Chem. A. 2015;3(43):21380–21423. doi: 10.1039/C5TA05523G. [DOI] [Google Scholar]
  • 21.Zhang Y, Guo WW, Zhang ZTX, Fan YX. Engineering hierarchical Di-atom@CuO@MnO2 hybrid for high performance supercapacitor. Appl. Surf. Sci. 2018;427:1158–1165. doi: 10.1016/j.apsusc.2017.09.064. [DOI] [Google Scholar]
  • 22.Guo XL, Li G, Kuang M, Zhang YL. Tailoring kirkendall effect of the KCu7S4 microwires towards CuO@MnO2 core-shell nanostructures for supercapacitors. Electrochim. Acta. 2015;174:87–92. doi: 10.1016/j.electacta.2015.05.157. [DOI] [Google Scholar]
  • 23.Wang JG, Huang YY, Kang ZH. Synthesis and electrochemical performance of MnO2/CNTs-embedded carbon nanofibers nanocomposites for supercapacitors. Electrochim. Acta. 2012;75:213–219. doi: 10.1016/j.electacta.2012.04.088. [DOI] [Google Scholar]
  • 24.Chavhan J, Rathod R, Tandon V, Umare S, Patel A. Structural and physico-chemical properties of electroactive polyamide/multi-walled carbon nanotubes nanocomposites. Surf. Interfaces. 2022;29:101765–101782. doi: 10.1016/j.surfin.2022.101765. [DOI] [Google Scholar]
  • 25.Deng MJ, et al. Facile electrochemical synthesis of 3D nano-architecture CuO electrodes for high-performance supercapacitors. J. Mater. Chem. A. 2014;2:12857–12865. doi: 10.1039/C4TA02444C. [DOI] [Google Scholar]
  • 26.Li Y, et al. Nanostructured CuO directly grown on copper foam and their supercapacitance performance. Electrochim. Acta. 2012;85:393–398. doi: 10.1016/j.electacta.2012.07.127. [DOI] [Google Scholar]
  • 27.Wang G, Huang J, Chen S, Gao Y, Cao D. Preparation and supercapacitance of CuO nanosheet arrays grown on nickel foam. J. Power Sources. 2011;196:5756. doi: 10.1016/j.jpowsour.2011.02.049. [DOI] [Google Scholar]
  • 28.Subramanian V, Zhu H, Wei B. Nanostructured MnO2: Hydrothermal synthesis and electrochemical properties as a supercapacitor electrode material. Power Source. 2006;159:361–364. doi: 10.1016/j.jpowsour.2006.04.012. [DOI] [Google Scholar]
  • 29.Mishra AK, Das NAK, Pradhan AK. Microwave-assisted solvothermal synthesis of cupric oxide nanostructures for high-performance supercapacitor. J. Phys. Chem. C. 2018;122:11249–11253. doi: 10.1021/acs.jpcc.8b02210. [DOI] [Google Scholar]
  • 30.Deng L. Preparation and capacitance of graphene/multiwall carbon nanotubes/MnO2 hybrid material for high-performance asymmetrical electrochemical capacitor. Electrochim. Acta. 2013;89:191–198. doi: 10.1016/j.electacta.2012.10.106. [DOI] [Google Scholar]
  • 31.Yu L, Zhang G, Yuan C, Lou X. Hierarchical NiCo2O4@MnO2 core-shell heterostructure nanowire arrays on Ni foam as high-performance supercapacitor electrodes. Chem. Commun. 2013;49:137–139. doi: 10.1039/C2CC37117K. [DOI] [PubMed] [Google Scholar]
  • 32.Wei W, Cui X, Chen W, Ivey DG. Manganese oxide-based materials as electrochemical super-capacitor electrodes. Chem. Soc. Rev. 2011;40:1697–1721. doi: 10.1039/C0CS00127A. [DOI] [PubMed] [Google Scholar]
  • 33.Liu J. Co3O4 nanowire@MnO2 ultrathin nanosheet core/shell arrays: A new class of high-performance pseudocapacitive materials. Adv. Mater. 2011;23:2076–2081. doi: 10.1002/adma.201100058. [DOI] [PubMed] [Google Scholar]
  • 34.Guo CX, Wang M, Chen T, Li LXW, Li CM. A hierarchically nanostructured composite of MnO2/conjugated polymer/graphene for high-performance lithium-ion batteries. Adv. Energy Mater. 2011;1:736–741. doi: 10.1002/aenm.201100223. [DOI] [Google Scholar]
  • 35.Zhang Y. Crystallization design of MnO2 towards better supercapacitance. Cryst. Eng. Commun. 2012;14:5892–5897. doi: 10.1039/c2ce25610j. [DOI] [Google Scholar]
  • 36.Kim H, Popov BN. Synthesis and characterization of MnO2-based mixed oxides as supercapacitors. J. Electrochem. Soc. 2003;150:56–62. doi: 10.1149/1.1541675. [DOI] [Google Scholar]
  • 37.Gholivand MB, Heydari H, Abdolmaleki A, Hosseini H. Nanostructured CuO/PANI composite as supercapacitor electrode material. Mater. Sci. Semicond. Process. 2015;30:157–161. doi: 10.1016/j.mssp.2014.09.047. [DOI] [Google Scholar]
  • 38.Zhao Y, Jiang P, Xie SS. ZnO-template-mediated synthesis of three-dimensional coral-like MnO2 nanostructure for supercapacitors. J. Power Sources. 2013;239:393–398. doi: 10.1016/j.jpowsour.2013.03.176. [DOI] [Google Scholar]
  • 39.Kumar R, Manoj D, Santhanalakshmi DJ. Optimization of site-specific adsorption of oleylamine capped CuO nanoparticles on MWCNTs for electrochemical determination of guanosine. Sens. Actuator B Chem. 2013;188:603–612. doi: 10.1016/j.snb.2013.07.067. [DOI] [Google Scholar]
  • 40.Zhi M, Manivannan A, Meng F, Wu N. Highly conductive electrospun carbon nanofiber/MnO2 coaxial nano-cables for high energy and power density supercapacitors. J. Power Sources. 2012;208:345–353. doi: 10.1016/j.jpowsour.2012.02.048. [DOI] [Google Scholar]
  • 41.Ramesh S, et al. Sheet-like morphology CuCo2O4 bimetallic nanoparticles adorned on graphene oxide composites for symmetrical energy storage applications. J. Alloy. Compd. 2021;892:162182–162182. doi: 10.1016/j.jallcom.2021.162182. [DOI] [Google Scholar]
  • 42.Pendashteh A, Mousavi MF, Rahmanifar MS. Fabrication anchored copper oxide nanoparticles on graphene oxide nanosheets via an electrostatic co-precipitation and its application as supercapacitor. Electrochim. Acta. 2013;88:347–357. doi: 10.1016/j.electacta.2012.10.088. [DOI] [Google Scholar]
  • 43.Palem RSRR, et al. Enhanced super capacitive behavior by CuO@MnO2/carboxymethyl cellulose composites. Ceram. Int. 2021;47:26738–26747. doi: 10.1016/j.ceramint.2021.06.081. [DOI] [Google Scholar]
  • 44.Zhang YX, et al. Facile synthesis of mesoporous CuO nanoribbons for electrochemical capacitors applications. Int. J. Electrochem. Sci. 2013;8:1366–1381. [Google Scholar]
  • 45.Haldorai Y, Voit W, Shim J-J. Nano ZnO @ reduced graphene oxide composite for high performance supercapacitor: Green synthesis in supercritical fluid. Electrochim. Acta. 2014;120:65–72. doi: 10.1016/j.electacta.2013.12.063. [DOI] [Google Scholar]
  • 46.Ramesh KS, et al. Hierarchical Co3O4 decorated nitrogen-doped graphene oxide nanosheets for energy storage and gas sensing applications. J. Ind. Eng. Chem. 2021;101:253–261. doi: 10.1016/j.jiec.2021.06.007. [DOI] [Google Scholar]
  • 47.Purushothaman KK, Saravanakumar B, Babu IM, Sethuraman B, Muralidharan G. Nanostructured CuO/reduced graphene oxide composite for hybrid supercapacitors. RSC Adv. 2014;4:23485–23491. doi: 10.1039/c4ra02107j. [DOI] [Google Scholar]
  • 48.Ramesh S, et al. Hexagonal nanostructured cobalt oxide @nitrogen doped multiwalled carbon nanotubes/polypyyrole composite for supercapacitor and electrochemical glucose sensor. Colloids Surf. B Bio Interfaces. 2021;205:111840–111888. doi: 10.1016/j.colsurfb.2021.111840. [DOI] [PubMed] [Google Scholar]
  • 49.Yadav HM, et al. Nanorods to hexagonal nanosheets of CuO-doped manganese oxide nanostructures for higher electrochemical supercapacitor performance. Colloids Surf. B Biointerfaces. 2019;184:110500–110500. doi: 10.1016/j.colsurfb.2019.110500. [DOI] [PubMed] [Google Scholar]
  • 50.Karuppasamy K, et al. Highly porous, hierarchical microglobules of Co3O4 embedded N-doped carbon matrix for high performance asymmetric supercapacitors. Appl. Surf. Sci. 2020;529:147147–147147. doi: 10.1016/j.apsusc.2020.147147. [DOI] [Google Scholar]
  • 51.Reddy ALM, Ramaprabhu S. Nanocrystalline metal oxides dispersed multiwalled carbon nanotubes as supercapacitor electrodes. J. Phys. Chem. C. 2007;111:7727–7734. doi: 10.1021/jp069006m. [DOI] [Google Scholar]
  • 52.Kathalingam A, et al. Nanosheet-like ZnCo2O4@nitrogen doped graphene oxide/polyaniline composite for supercapacitor application: Effect of polyaniline incorporation. J. Alloy. Compds. 2020;830:154734–154734. doi: 10.1016/j.jallcom.2020.154734. [DOI] [Google Scholar]
  • 53.Liu C, Li F, Cheng MLP. Advanced materials for energy storage. Adv. Mater. 2010;22:28–62. doi: 10.1002/adma.200903328. [DOI] [PubMed] [Google Scholar]
  • 54.Abdullah A, Parveen N, Ahmad F, Alam MW, Ansari SA. Self-assembled cube-like copper oxide derived from a metal-organic framework as a high-performance electrochemical supercapacitive electrode material. Sci. Rep. 2019;9:1–10. doi: 10.1038/s41598-018-37186-2. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 55.Kakani V, et al. Facile synthesis of CuO/NiO/nitrogen doped rGO by ultrasonication for high performance supercapacitors. J. Alloy. Compd. 2020;847:156411–156421. doi: 10.1016/j.jallcom.2020.156411. [DOI] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Figure S1. (95.2KB, docx)

Data Availability Statement

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.