Antiviral role of nanomaterials: a material scientist's perspective

Muhammad Aanish Ali; Nagina Rehman; Tae Joo Park; Muhammad Abdul Basit

doi:10.1039/d2ra06410c

. 2022 Dec 21;13(1):47–79. doi: 10.1039/d2ra06410c

Antiviral role of nanomaterials: a material scientist's perspective

Muhammad Aanish Ali ¹, Nagina Rehman ², Tae Joo Park ^3,^✉, Muhammad Abdul Basit ^1,^✉

PMCID: PMC9769549 PMID: 36605642

Abstract

The present world continues to face unprecedented challenges caused by the COVID-19 pandemic. Collaboration between researchers of multiple disciplines is the need of the hour. There is a need to develop antiviral agents capable of inhibiting viruses and tailoring existing antiviral drugs for efficient delivery to prevent a surge in deaths caused by viruses globally. Biocompatible systems have been designed using nanotechnological principles which showed appreciable results against a wide range of viruses. Many nanoparticles can act as antiviral therapeutic agents if synthesized by the correct approach. Moreover, nanoparticles can act as carriers of antiviral drugs while overcoming their inherent drawbacks such as low solubility, poor bioavailability, uncontrolled release, and side effects. This review highlights the potential of nanomaterials in antiviral applications by discussing various studies and their results regarding antiviral potential of nanoparticles while also suggesting future directions to researchers.

An overview of applications of nanoparticles and their combinations with a variety of antiviral drugs.

1. Introduction

The modern world faces serious challenges due to viral infections and their outbreaks in the form of epidemics and pandemics. Viruses are basically small obligate parasites and are non-living things residing outside of the host cell. These viruses interact with cells via various mechanisms such as receptor–ligand interactions. Among these, respiratory viruses pose a crucial threat to all sorts of demographics. Researchers continue to work on their treatment and suppression by utilizing nano-based options such as functional metallic nanoparticles (NPs) and nano-enabled drug delivery systems. The drug delivery systems must be capable of dealing with inherent features of viral infections like their replication dynamics, level of drug resistance, and complex lifecycle stages. Frequent drug use causes enhancement of drug resistance against viruses and has now become a crucial health issue globally for nearly all sorts of drugs that are known to be effective against one or more specific viruses. The past two decades have witnessed the emergence of old viral infections and introduction of new types of viruses such as severe acute respiratory syndrome (SARS-CoV-2) which is a form of coronavirus.^1–4 The human body can contract these viruses via various routes such as ear, nose, mouth, and skin.⁵ Once a virus is contracted, it is difficult for the human body to develop an immune response against it. Due to larger categories of viruses than the number of treatment options available, there are still many infections for which there is either no effective treatment or treatment has not proved to be fully effective.⁶

Besides posing threat to human health and life, the viral outbreaks have affected human life in several ways ranging from disruption of daily life activities, economic collapse of societies, shortages of food and medical supplies, and mass-scale deaths.^7,8 A recent example is of COVID-19 pandemic in which the world witnessed the peak of these problems till the time when an adequate number of vaccine doses were administered globally to most of the population and the trends showed a decline in emergence of new cases and decrease in deaths due to increased immunity among people, thanks to these vaccines.

Research has previously shown that nanomaterials possess great potential in antiviral applications.⁹ Materials scientists and chemists have conducted extensive research to explore and synthesize newer, efficient nanomaterials which can successfully inhibit and treat a wide range of viruses. Different functional NPs and nanostructures have shown antiviral activities against a broad spectrum of viruses, each having its mechanism and viricidal activity. Every system comes with its limitations and benefits and hence it is important to employ the most suitable candidate for treatment of specific viruses.¹⁰Fig. 1 presents an outlook on the use of nanoparticles and nano-based drug delivery systems which have proved to be effective against many viruses.

Before the advent and advance of nanotechnology, antiviral drugs were extensively used for treatment of viruses. The efficiency of these drugs was limited due to their inherent low bioavailability, shorter half-life, cytotoxicity, uncontrolled release as well as serious side effects that limited their use.^11,12 Material scientists have developed nanoparticles that were capable of acting as delivery vehicles for these drugs, releasing a controlled amount of drug to the targeted site for the required amount of time. They showed appreciable entrapment of drug while increasing the efficacy and enhancing the viricidal effects. The key property of nano-enabled delivery systems is that due to their extremely smaller size and high surface areas, they facilitate better digestion, absorption, and penetration of drugs.^13,14 In this review, we have discussed well-known functional NPs which exhibit antiviral action, their synthesis, properties, and mechanism along with exhaustive and informative discussion of existing nano-enabled drug delivery systems which are known to have overcome the limitations of antiviral drugs such as low biocompatibility, cytotoxicity, hemocompatibility and difficulty in administration to patients, among various other issues associated with them which we have covered in this review.

2. Metal-based nanoparticles as effective antivirals

2.1. Ag-based NPs

Silver nanoparticles (AgNPs) have shown great potential in biomedical applications such as anti-bacterial and anti-cancer. However, there is only a handful of research on antiviral activity of Ag-based NPs. Results from recent studies show that AgNPs are quite effective against a wide range of viruses such as respiratory syncytial virus (RSV), enterovirus 71, herpesvirus (HSV-1 and HSV-2), poliovirus (PV), dengue virus (DENV), influenza (H1N1, H3N2), hepatitis (HSV-1, HAV-10, and CoxB4) and coronaviruses (porcine epidemic diarrhea virus (PEDV) and feline coronavirus (FCoV)).¹⁵

Morris et al. reported the first in vivo study to examine the antiviral nature of AgNPs against RSV infections. A significant decrease in pro-inflammatory cytokines and chemokines was recorded in the infected mice's lungs. AgNPs were able to effectively block the entry of RSV to host cells by binding to the surface of glycoproteins and inhibiting the spread of RSV. While the development of vaccines for RSV infections remains a challenge, employing AgNPs can be a novel strategy to treat RSV-infected patients.¹⁶ While small interfering RNA (siRNA) holds promise in antiviral activity against EV71, its major limitation is its inability to cross cell membranes. The study prepared surface-decorated AgNPs using polyethyleneimine (PEI) and siRNA and monitored for their antiviral activity. The accumulation of reactive oxygen species (ROS) was effectively inhibited, and EV71 was not able to infect the host cells.¹⁷ The potential of AgNPs against PV was monitored in vitro, as the electrochemically synthesized AgNPs played a key role in the disinfection of PV, a non-enveloped virus.¹⁸

The use of AgNPs in antiviral applications is generally limited since many AgNPs are synthesized in a liquid atmosphere, a technique not easily applicable. Recent studies have suggested numerous solutions to address this limitation. Szymańska et al. reported preparation of mucoadhesive hydrogel based on tannic acid (TA)-modified AgNPs (TA-AgNPs) as an effective route for treatment of HSV-1 and HSV-2.¹⁹ For enhancing the antiviral action, the NPs were encapsulated by a hydrogel called Carbopol 974P for effective delivery to the targeted site (ex vivo vaginal mucosa). The gelation (100% crosslinking) was facilitated by an initiator, thereby providing closer contact between drug carrier and the mucosal tissue. The size of nanoparticles was found to be between 13 and 54 nm as estimated from the micrographs of transmission electron microscope (TEM) (Fig. 2(a) and (b)). The antiviral efficacy of NP-based hydrogel was evaluated in vitro. To ensure that components of hydrogel do not affect the infectivity of HSV-1 and 2, placebo hydrogel and TA-AgNPs were simultaneously applied. The scheme of virus inhibition assay is illustrated in Fig. 2c(A). Both types of HSVs were considerably inhibited after a 24 h incubation period, which indicates the potential of prepared formulation against HSV infections. However, the inhibition was roughly 20% more for HSV-2 (Fig. 2c(B)). The results shown in Fig. 2c(C) and (D) indicate that inhibition of HSV-1 and 2 is greater in cells that were exposed to hydrogels as compared to the control cells, with more inhibition in case of HSV-2. It is pertinent to mention that inhibition rate of HSV-1 infection was dependent on the concentration of the NPs in hydrogel while concentration played no role in inactivation of HSV-2. Possible mechanisms of virus suppression may be due to NP interacting with HSV envelope and blockage of virus interaction with cells due to layer of hydrogel around them. The study further explored the mode of antiviral activity of prepared formulation by employing assays of virus attachment and penetration. The variables of both assays are shown in Fig. 2d(A). After 24 h post-infection, it was observed that around 85–90% inhibition for HSV-1 attachment to the cell surface with a considerable decrease in plaque numbers (greater than 60%) was recorded for HSV-2 (Fig. 2d(B)). This time the percentage of HSV-1 inhibition after treatment with H2/NP25 (Fig. 2d(B)) was found to be greater than the inhibition of HSV-2. The penetration assay showed that HSV-2 entry to HaCaT cells was suppressed by exposure to both hydrogels. Interestingly, both formulations of hydrogel showed lower inactivation for HSV-1 in contrast to attachment assay. NPs inside the cell could have played a vital role in inhibition. Hence cell-to-cell spread assays were conducted (Fig. 2e). It can be seen that the inhibitory effect of both hydrogels on the cells infected with HSV-2 is significantly greater than that of the control and placebo (Fig. 2e(C)). In contrast, the cell-to-cell spread was inhibited for HSV-1 infected cells only by the hydrogel with 50 ppm TA-AgNPs (Fig. 2e(D)). The Carbopol 974P provided two distinct properties; transporting antiviral (TA-AgNPs) to targeted site and inherent antiviral activity. Therefore, a synergistic effect of both hydrogel and NPs played a key role in suppression of HSV infection. The authors, however, suggested the need for future in vivo studies for further exploration and innovation of this novel route (readers are suggested to consult the cited literature for information about the specific composition of the H2/NP25 Hydrogel formulation).

Another study reported two algae, Oscillatoria sp. and Spirulina platensis, mediated by green Ag₂O|AgO-NPs and Au-NPs, respectively, and evaluated their effect on HSV-1 infection.²⁰ The spherical-shaped Ag₂O|AgO-NPs with smaller size (nm) than non-spherical AuNPs showed a greater reduction rate of HSV-1. The results indicate the potential of bio-synthesized NPs as suppressing agents for HSV-1 infection. Remarkable antiviral activity of green synthesized AgNPs of two plant extracts, L. coccineus and M. lutea, was shown against HSV-1, HAV-10, and CoxB4 virus.²¹

Sreekanth et al. reported virucidal effects of AgNPs, 5–15 nm in size, against influenza A virus with an easy, smooth, and convenient approach used for synthesis of AgNPs i.e., ultrasonication method. Green synthesized AgNPs were studied for in vitro cytotoxic and antiviral activities and showed to possess good antiviral action against H1N1 variant of Influenza A virus.²² Another study reported AgNPs (not green synthesized) as potential antiviral agents against H1N1.²³ The potential of AgNPs was shown against H3N2 variant of Influenza virus with the help of in vitro and in vivo studies.²⁴ For in vivo studies, the survival of mice was enhanced while in vitro studies showed that AgNPs were able to protect cells by inhibiting viral infections. The mechanism of antiviral action appeared to be the destruction of virus morphology by AgNPs.

2.2. NiO nanostructures (NONS)

The leading cause of the infection in cucumber crops is cucumber mosaic virus (CMV), resulting in a significant reduction in crop yield globally, especially in Egypt. Viral diseases are not usually countered by chemical pesticides, one of the reasons being their ineffectiveness resulting from repeated use.²⁵ Several studies have related the growth of plants with the amount of nickel (Ni) present. The need evolved to investigate the effect of Ni-based nanostructures against CMV.²⁶ NiO was fabricated via one-pot hydrothermal synthesis and the efficacy of NONS against CMV in cucumber plants was evaluated against reduction in disease severity, assessed via immunosorbent assay. NONS particles of about 15–20 nm in size with greater exposed surface area were administered via foliar spray or soil drench to infected plants. The nanostructures were characterized by FESEM, X-ray diffraction (XRD), and Raman spectroscopy, and results are shown in Fig. 3. FE-SEM images in Fig. 3a and b show stable morphological nanostructures of NiO. Semi-spherical head ends are composed of nanotubes aligned normally within body of head. The distribution of these nanotubes across the surface of head indicates that average size of tube is in between 15 and 20 nm. Moreover, thick distribution of nanotubes resembles tubular vessels resulting from carefully designed NONS. WA-XRD was employed to determine the crystal structure of NONS. Crystal planes are indicated at well-resolved and sharp diffraction peaks of NiO and indicated accordingly in Fig. 3c. Raman spectroscopy revealed the presence of pristine NiO as appeared peaks result from presence of two TO modes and two LO modes as indicated in Fig. 3d. In vivo study concluded that plants treated with NONS showed visible reduction in CMV compared to non-treated counterparts, showing potential for NONS to be used as antiviral agent against CMV.

2.3. Zirconia NPs

Zirconia NPs have shown promise in treatment of cancer in previous studies, but their antiviral activity was not reported previously. Huo and collaborators studied the antiviral effect of ZrO₂ NPs on H5N1 variant of influenza A virus.²⁷ The mice infected with H5N1 virus were treated with ZrO₂ NPs of about 200 nm in size and administered intraperitoneally. The in vivo study concluded that survival chances of mice were increased by about 85.7%, as the ZrO₂ NPs promoted the release of cytokines in mice. Thus, this novel strategy needs further exploration for future innovations.

2.4. ZnO NPs

The antiviral drugs currently employed for the treatment of influenza viruses are becoming insignificant as they cause adverse side effects with drug-resistant strains.²⁸ There is an urgent need to develop better and more efficient anti-influenza agents. A few advantages of using nanoparticles for the treatment of viral infections are that their synthesis is cheaper, they possess good antiviral efficacy, and can be tailored to improve properties via coating. ZnO-NPs have previously shown substantial antimicrobial and antibacterial activities.²⁹ However, a handful of research has been done to evaluate the antiviral efficacy of ZnO-NPs. Ghaffari et al. were the first to examine the antiviral efficacy of ZnO-NPs and PEGylated ZnO-NPs in vitro.³⁰ The size of NPs was reduced to a large extent as a result of massive ball milling. Scanning electron microscopy (SEM) confirmed the sizes of ZnO-NPs to be 20–50 nm and ZnO-PEG-NPs to be 16–20 nm (Fig. 4a). The SEM images show NPs to be of spherical morphology with uniform size distribution. The surface coating of ZnO-NPs was confirmed via TEM micrographs in Fig. 4b. The presence of ZnO-NPs was confirmed by XRD power diffraction pattern. When compared to the standard powder diffraction file (PDF), the peaks and their respective intensities of ZnO exhibit a similar pattern as depicted in Fig. 4c. Thermogravimetric analysis (TGA) was employed for weight loss measurements (Fig. 4f and g)). It can be seen that at a temperature of 400 °C, there is a significant decrease in weight (%) in the case of ZnO-PEG-NPs (Fig. 4g) while the weight loss is very small at the same temperature for ZnO (Fig. 4f). This gives a reasonable explanation for coating of PEG which resulted in greater weight loss. The key finding of the study was that the NPs cause antiviral action only after the virus has infected the cells. There was considerable inhibition when H1N1 virus was exposed after infection to ZnO-PEG-NPs as there was a significant reduction in virus titers in contrast to the virus control, as shown at concentrations of 75, 100, 200 μg mL⁻¹. The maximum concentration of ZnO-NPs alone could only result in 1.2 log10 TCID50 reduction which is much lower than reductions caused due to PEGylated ZnO-NPs. At its maximum non-toxic concentration, PEG alone could reduce by 0.7 log10 TCID50, which is even lower than ZnO-NPs. These results are schematically depicted in Fig. 4h. It was observed in quantitative real-time PCR tests that significant inhibition resulted by ZnO-PEG-NPs at concentrations of 75, 100, 200 μg mL⁻¹, which are much superior to ZnO-NPs inhibition rates at respective concentrations. However, it is quite interesting to note that oseltamivir was able to fully inhibit influenza at a concentration of 75 μg mL⁻¹. These results are summarized in Fig. 4e. While the precise antiviral mechanism of virus inhibition largely remained unexplored, PEGylating the surface of ZnO-NPs resulted in increased antiviral activity and can be employed as a novel strategy for improving the antiviral efficacy. Hence ZnO-PEG-NPs can be an effective antiviral agent against influenza viruses.

2.5. TiO₂-based NPs

Broad bean stain virus (BBSV) infects seeds of many food crops. Faba bean crop is significant globally, especially in Egypt. They are quite sensitive to viral diseases like BBSV.³¹ Recent studies have proposed nanotechnology as a novel method to control pathogens in plants.³² The excellent property profile offered by TiO₂ allows it to be used in a variety of applications, including antiviral. However, the efficacy of TiO₂ is negatively affected by several factors such as its inherent crystallinity, unfavorable surface-to-size area ratio, and its surface morphology.³³ The material scientists have focused on developing new modes of synthesis of TiO₂ that induce functionalities that can prove effective in the treatment of plant-related diseases. The mechanism of antiviral action against plant viruses can be different and varies from material to material. For instance, it can include the direct effects of NPs against the virus which can result in death of virus or may also cause the defensive system of plants to become stronger and hence increase its inherent immunity to deal with virus.³⁴ One such study was done by Elsharkaway et al., who fabricated TiO₂ nanostructures (TDNS) and examined its antiviral efficacy against BBSV.³⁵ The approach used for synthesis was similar to that reported by Gomaa et al.³⁶i.e., direct mild hydrothermal synthesis, with slight changes. To determine the crystal structure of the synthesized NPs, wide-angle X-ray diffraction (WA-XRD) was utilized which shows a similar pattern as that for standard TiO₂ as seen in Fig. 5a. FE-SEM micrographs confirm the successful synthesis of TiO₂ structures as surfaces can be seen to be smooth from inside and rough from outside with a small thickness of walls (Fig. 5b). The further morphological examination also shows that size distribution was in the range of 3–5 μm for diameter, while 3–4 μm for length and width. Combining of a large number of TiO₂ nano-sheets can form a hollow shape as hydrogen from oleic acid bond to TiO₂ surface.³⁷ This can result in favorable exposed surface area for interaction between virus and TDNS with greater antiviral activity. Experimental results after a 14 days treatment are shown in Fig. 5c. The control leaves can be seen to be smaller and deformed while the leaves treated with TDNS exhibited great reduction in symptoms of BBSV. Outstanding reduction in disease severity of faba bean plants due to TDNS can be seen in Fig. 5d. Foliar spray method appeared to be more effective in decreasing the disease severity than soil drench technique. (In foliar spray, fertilizers (in our case TiO₂ nanostructures or TDNS) are sprayed on the plant leaves rather than pouring them in the soil. In contrast, soil drench technique involves pouring the chemicals mixed with water directly onto the soil). Moreover, concentration of BBSV in plants treated via foliar spray method is also lower than in soil drench. Plants treated with both approaches showed no significant difference in gene expression which was, however, much greater than control. Thus, due to TDNS inducing systematic resistance, there was a significant decrease in disease severity. Structural features of TDNS such as particle size and suitable shape were the governing factors for its good overall efficacy against BBSV. This study is only one of its kind which evaluated and suggested an eco-friendly approach to treating plants against BBSV.

Nakano et al. proposed use of TD thin film for photocatalytic inactivation of H1N1 Influenza. This can be attributed to the strong oxidation effect produced when TiO₂ is exposed to UV light.³⁸ The study demonstrated that TiO₂ substantially increases the disinfection rates of H1N1 by a strong oxidation effect which degrades viral proteins. A slight amendment in the ISO method was made for evaluating the anti-bacterial effects of TD which can prove beneficial for enhancing the antiviral activity. There are a few studies that relate the antiviral mechanism of action of TiO₂ to the best of our knowledge.

2.6. GO-Ag NPs

Nanomaterials are of key importance in treatment of viral infections. In this regard, AgNPs have shown good potential in antiviral actions against a variety of viruses, as discussed before in this review. Chen et al. reported that there have been no studies on the antiviral efficacy of nanomaterials against non-enveloped viruses.³⁹ Their study evaluated the antiviral activity of GO sheets and GO-AgNPs against both enveloped and non-enveloped viruses. The enveloped virus chosen was Feline Coronavirus (FCoV) while the non-enveloped virus was Infectious Bursal Disease Virus (IBDV). The particle size distribution (PSD) of Ag NPs was between 5–25 nm while thickness of each GO layer was 0.355 nm and there were 2 to 5 layers in total. The virus inhibition assay reported a significant reduction of FCoV (25%) and IBDV (23%) by GO-Ag NPs than GO sheets whose inhibition was restricted to merely 16%. The virus inhibition mechanism of GO-Ag NPs is illustrated schematically in Fig. 6.

2.7. Gold nanoparticles (AuNPs)

The exceptional property profile package offered by AuNPs such as exquisite quantum size effect, surface effect, and macroscopic quantum tunneling effect make them useful in nanomedical applications. Several studies have evaluated antiviral efficacy of AuNPs against a variety of viral infections. For example, Asim and his coworkers synthesized AuNPs of 7.86 ± 3.3 nm in size by sonication of gallic acid in a bath Sonicator and examined their antiviral mechanism of action.⁴⁰ They reported that AuNPs prevent the attachment and penetration of HSV. The amount of virus inhibited is dependent on the time of exposure of AuNPs and hence the method employed uses highly monodispersed AuNPs. Their bio-friendly nature makes them a strong candidate for prevention of HSV. Another study reported by Gianvincenzo et al. evaluated AuNPs antiviral efficacy against HIV.⁴¹ Two compounds used Au clusters of about 1.7 nm and 2.6 nm, respectively, which accommodated about 140 sulfated ligands and were enough to perform anti-HIV action. The in vitro study revealed that AuNPs do this by binding to glycoprotein (gp120). AuNPs can be coated with sulfate-ended ligands which in turn bind the HIV, causing its inhibition. This result opens doors of opportunities to tailor those surface ligands for development of more anti-HIV systems. The potential of AuNPs is not limited till here. Papp et al. have demonstrated in previous studies about the capability of AuNPs in the treatment of Influenza A Viruses (IAVs).⁴² They showed that sialic-acid coated glycerol dendrons when immobilized on 14 nm AuNPs caused an appreciable anti-influenza effect. Moreover, AuNPs were non-toxic under operating conditions. The AuNPs have also been found compatible with the treatment of Dengue virus (DENV). For instance, Paul and his collaborators have reported that biocompatible AuNPs can be used to improve the delivery and stability of siRNA.⁴³ When entered Vero cells, they decrease DENV-serotype 2 replication to a great extent by releasing infectious virions. Hence AuNPs can be used for DENV infection control in vitro.

2.8. Selenium NPs

There are no effective drugs for the treatment of EV-A71. Selenium (Se) is present in our body as a nutritional element that is responsible for protection against viral infections. Recent studies have reported that SeNPs have excellent bioavailability and lower side effects due to their smaller size^44,45 and hence have the potential to be used as an antiviral agent against EV71.

Li et al. investigated the effect of SeNPs on the suppression of EV-A71 virus as they interfere with JNK signaling pathways.⁴⁶ As seen in Fig. 7a(A), the SeNPs can pass through the cell membrane and suppress the generation of Reactive Oxide Species (ROS) by EV-A71. They interfered with and successfully inhibited JNK signaling pathways by mechanisms of caspase-8 and caspase-9-mediated apoptosis in the cells infected by the virus. They synthesized SeNPs via a simple method and were able to prepare uniform NPs of size roughly 100 nm, as confirmed by the TEM micrograph in Fig. 7a(B). Due to their smaller size, SeNPs were highly stable and able to penetrate the cells. The presence of Se and Cu was confirmed in energy dispersive X-ray spectroscopy (EDX) as they form the SeNPs and the copper grid (Fig. 7a(C)). Thiazolyl blue tetrazolium bromide (MTT) assay was employed to examine the cell viability with SeNPs. Cell viability can be seen to slightly decrease in Fig. 7a(D). The decrease can be attributed to the concentration of SeNPs. This indicates that SeNPs can inhibit the EV-A71 virus proliferation. The MTT assay also measured the antiviral activity of SeNPs (concentration maintained at 15.625 μM). The results show that cell viability was increased to 71% by SeNPs as compared to 59% when treated with EV-A71 virus (Fig. 7a(D)). This suggests good antiviral efficacy of SeNPs against EV-A71 virus.

For the treatment of EV-71 variant of enterovirus, oseltamivir (OT) is commonly used as an antiviral therapeutic agent. Although it has been approved for use by FDA, due to continuous usage, it has shown a decrease in antiviral efficacy.⁴⁷ To overcome this problem of inherent drug resistance against the virus, nanotechnology holds promise.⁴⁸ As discussed previously, Se is an important element in human body and hence its deficiency can result in increased susceptibility to virus infections.⁴⁹ Zhong et al. proposed a novel nanotechnological approach for increased antiviral efficacy against EV-71.⁵⁰ They fabricated a nano-sized functional antiviral system by loading OT on the surface of SeNPs and evaluated its antiviral activity. The cell model for this particular study was chosen to be a human astrocytoma cell (U251). To confirm the chemical bonding between the drug and the NPs, Fourier transform infrared spectroscopy (FTIR) was performed whose graph is depicted in Fig. 7b(A). The spectrum is same as that of oseltamivir and peaks corresponding to 3248, 1248, and 733 cm⁻¹ can be seen for SeNPs@OT which is an indication of successful formation of a nano-sized antiviral system. The mean size of this nanosystem is confirmed by TEM micrograph in Fig. 7b(B), which confirms it to be around 10 nm. EDX results can also be seen in Fig. 7b(C), which shows characteristic peaks corresponding to Se (from NPs), O, and C (from OT) which further confirms the success in the preparation of SeNPs@OT. The cell viability of model U251 cells was examined and in Fig. 7b(D), the viability is lowest for EV-71 infected cells which increased to a greater amount with OT than SeNPs. However, when the prepared nanosystem SeNPs@OT was used, the viability of the infected cells was the highest. A similar experiment was conducted after 48 hours post infection and results can be seen to be similar as in Fig. 7b(E). Hence SeNPs loaded onto OT suppressed the cell apoptosis caused by EV-71 virus via mitochondrial pathway and reduced the generation of reactive oxygen species. Table 1 shows a summary of different metallic NPs which exhibit antiviral activity against a wide category of viruses along with their key parameters.

Antiviral activity of different metallic and functional nanoparticles against a broad spectrum of viruses along with key parameters reported.

Nanoparticle(s)	Virus	Classification of virus	In vitro or in vivo	Size (nm)	Synthesis method	Mechanism	Reference
Ag₂O\|AgO-NPs and Au-NPs	Herpesvirus	HSV-1	In vitro	14.42–48.97 nm [Ag₂O–AgO-NPs]; 15.60–77.13 nm [Au]	Biosynthesis	—	20
Ag₂S nanoclusters	Coronavirus	Porcine epidemic diarrhea virus (PEDV)	In vitro, in vivo	3.7 nm and 5.3 nm	One-pot method	Prevents synthesis of viral negative-strand RNA and viral budding	51
AgNPs	Dengue virus	DENV	In vitro	100 nm	Biological (seed extract)	—	52
	Influenza	H3N2	In vitro, in vivo	9.5 nm	Oxidation-reduction method	Destruction of morphologic viral structures	24
		H1N1	In vitro	10 nm	—	—	23
		H1N1	In vitro	5–15 nm	Ultra-sonication method	—	22
	Enterovirus 71	EV71	In vitro	-	Simple method	—	17
	Respiratory syncytial virus	RSV infections	In vitro, in vivo	8–12 nm	—	Prevents entry of viral glycoproteins into the host cell	16
	Dengue virus	DENV	In vitro	30–70 nm	Biological (plant extract)	—	53
	Hepatitis	HSV-1, HAV-10 and CoxB4	Used design studio	8.91–27.89 nm	Biological (plant extracts)	—	21
	Herpesvirus	HSV-1 and HSV-2	In vitro, in vivo, ex vivo	13 to 54 nm	—	Affect viral attachment	19
	Poliovirus	PV	In vitro	7.1 nm	Electrochemical method	Cytopathic effect (CPE)	18
Au-MES NPs	Herpesvirus	HSV-1	—	4 nm [Au-MES NPs]	Solution-based method	Prevents virus from attaching, entering and spreading from cell to cell	54
AuNPs	Herpesvirus	HSV	—	∼7 nm	Gallic acid in a bath sonicator	Prevents the attachment/penetration of virus	40
	Human immunodeficiency virus	HIV-1	—	1.7 nm and 2.6 nm	—	Binding to gp120	41
	Influenza	Influenza A viruses (IAVs)	—	2 nm and 14 nm	—	Multivalent interaction with sialic-acid-functionalized AuNPs	42
AuNPs interfering RNA	Dengue virus	DENV	In vitro, in vivo	12.92–43.25 nm	Chemical	Release infectious virion	43
Carbon dots NPs	Human immunodeficiency virus	HIV-1	—	2 nm	Pyrolysis of citric acid	Suppressing the syncytium formation	55
Carbon quantum dots (CQDs)	Highly pathogenic coronavirus	HCoV	—	7.6 ± 0.2 nm	Hydrothermal carbonization	—	56
Copper(i) iodide NPs	Influenza	H1N1	—	160 nm	—	OH⁻ radicals are generated and viral proteins undergo degradation	57
Copper(i) iodide NPs	Feline calicivirus	FCV	—	100–400 nm	—	Cu⁺ ions generated followed by generation of ROS and capsid protein oxidation	58
Copper–graphene (Cu–Gr) nanocomposite	Influenza	Influenza A viruses (IAVs)	—	-	—	Inactivate the virion particles within a half hour, preventing entry to the host cell	59
CuO NPs	Herpesvirus	HSV-1	In vitro	40 nm	—	Production of ROS via Cu⁺ OR degradation of viral genome	60
Cuprous oxide NPs	Hepatitis	HCV	In vitro	45.4 nm	Solution phase	Inhibited entry of HCV pp	61
GO-Ag NPs	Feline coronavirus (FCoV): non-enveloped virus and infectious bursal disease virus (IBDV): Enveloped virus	FCoV and IBDV	—	5–25 nm	Hummers' method	—	39
Gold nanorod-based HR1 peptide	Coronavirus	SARS CoV-2	—	18 nm (diameter)	Chemical solid phase	Increases the immune indicators and decreases the inflammation indicators	62
Iron oxide NPs	Influenza	H1N1	In vitro	10–15 nm	Chemical reduction and magnetic separation	—	63
NiO nanostructures (NONS)	Cucumber mosaic virus	CMV	In vivo	15 to 20 nm	One-pot hydrothermal synthetic approach	Increase the expression of pod, pr1 and pal1 genes	26
Se@PEI@siRNA	Enterovirus 71	EV71	-	80 nm	—	Chances of SK-N-SH cells for staying in sub-G1 phase are reduced	64
SeNPs	Enterovirus 71	EV71	In vitro	10 nm	—	SeNPs@OT entered host cells by clathrin-associated endocytosis while suppressing EV71 proliferation	50
SeNPs	Enterovirus A71	EV-A71	—	100 nm	Simple method	Cytopathic effect	46
Ag NCs with SiO₂ composite sputtered coating	Coronavirus	SARS CoV-2	—	Less than 200 nm	Co-sputtering with argon at radio frequency	Coating possessed a virucidal effect	65
GO-Ag nanocomposite	Porcine epidemic diarrhea virus	PEDV	In vitro	17 ± 3.4 nm	Self-assembly via interfacial electrostatic force	Prevent entry of PRRSV to host cells	66
TiO₂ nanostructures (TDNS)	Broad bean stain virus	BBSV	—	—	Modified direct hydrothermal synthesis	Inducing systemic resistance	35
TiO₂ NPs	Influenza	H1N1	—	—	—	Strong oxidation effect	38
TiO₂ NPs	Influenza	H3N2	—	4–10 nm	—	Fragmentation of viral envelope	67
Tungsten carbide nanoparticles (WC NPs)	Poliovirus type-1, vaccinia virus ankara, human adenovirus type 5, Murine norovirus	PV-1, MVA, HAdV-5, MNV	In vitro	10–20 nm	Plasma atomization	—	68
Zirconia NPs	Influenza	H5N1	In vivo	200 nm	Two-step selective etching method	Promote the release of cytokines in mice	27
ZnO NPs and PEGylated ZnO NPs	Influenza	H1N1	In vitro	20–50 nm ZnO-NPs; 16–20 nm ZnO-PEG-NPs	Mechanical method	Virus inhibited once it enters the host cell	30

Open in a new tab

3. Nanoparticles for enhancing the efficacy of antiviral drugs

3.1. Acyclovir

3.1.1. Oral delivery

Research is in progress to develop novel drugs for oral administration. Acyclovir (ACV) has issues of shorter half-life and poor permeability and hence patients' compliance is difficult. Mahmood et al. examined the effect of ACV in lipid polymeric particles and tested in vitro and ex vivo.⁶⁹ They aimed to enhance the controlled release of ACV via encapsulation with PEGylated Lipid Polymeric NPs. The NPs prepared via Box–Behnken Design (BBD) method were 187.7 ± 3.75 nm in size. Polymers and amphiphilic molecules are widely employed for the effective delivery of hydrophilic and lipophilic molecules.⁷⁰ Their study aimed to develop a PEGylated lipid polymeric NP system by employing CS, lecithin, and PEG 2000 which was supposed to produce NPs with high encapsulation efficiency, easy permeability with sustained release profile. PEGylated ACV-loaded lecithin-CS NPs (PALNs) were synthesized and drug release parameters were assessed. The mechanism of formulation of PALN is schematically illustrated in Fig. 8a. Polar ACV attracts hydrophilic lecithin⁷¹ which is followed by its addition to the CS solution. A stiff, stable nanostructure is hence obtained due to the formation of a CS shell around the NP.⁷² PEG is used in applications of drug delivery as it gives stealth properties along with biocompatibility. It surpasses the immune system and enhances circulation time.⁷³ Its grafting was facilitated by interaction between nitrogen of amide group of CS and hydroxyl and etheric oxygen of PEG.⁷⁴ Good percentage entrapment was recorded for all 17 tested formulations as shown in Fig. 8b. The formulation was stable for up to 60 days and showed controlled release of drug for 24 hours.

Similarly, Saifi and her collaborators employed bilosomes nanocarriers (NCs) to enhance the oral bioavailability of ACV.⁷⁵ The in vitro, ex vivo, and in vivo assessments showed that a vesicle size of 121.2 ± 3.21 nm was obtained via thin film hydration method (optimized via BBD) and showed 71.87–88.67% entrapment efficiency. The biocompatible bilosomes were found to be an effective drug carrier as they enhanced gut absorption of ACV at a considerably lesser amount dose than needed for a typical tablet.

3.1.2. Ocular delivery

Poorly soluble drugs are difficult to be administered via ocular route. Ocular bioavailability is markedly reduced due to the inherent anatomical and physiological barriers in eyes.^76,77 Despite the given constraints, ocular delivery is still a preferred route of administration. It was hypothesized that increasing the pre-corneal drug retention and enhancing its permeation can significantly improve the efficacy and bioavailability of these drugs.⁷⁸ Therefore, using NP-based delivery system could prove effective in overcoming the limitations associated with ocular delivery. Alkholief et al. employed biodegradable and biocompatible PLGA polymer stabilized with TPGS nanosystem for delivery ACV topically through eyes.⁸¹ One of the major considerations while developing a polymeric NP system for ocular delivery is the biodegradation of polymer and its subsequent drug release profile. In vitro release profile was monitored for two optimized ACV formulations as shown in Fig. 8c. A biphasic release pattern is observed which shows an initial burst release for nearly 8 h followed by a controlled release for 14 h and subsequent sustained release for 72 h. ACV release was not governed by the percentage of PLGA but rather by the types of stabilizers used. The initial burst release may be due to PLGA undergoing biodegradation which causes drug attached to the surface to contact the medium and quickly solubilizes as a result.⁷⁹ The concentration of ACV was detected at regular intervals in rabbit eyes as shown in Fig. 8d. ACV-AqS and PLGA-TPGS-NPs were administered topically to the eyes of rabbits. For rabbits treated with ACV-AqS, ACV concentration could not be detected after 6th hour. The rapid corneal and precorneal loss might have played role in ACV not being able to be detected. In contrast, PLGA-TPGS-NPs treated rabbits showed detectable ACV concentration up to 24th hour, indicating a potential for nanosystem for sustained release of ACV and hence its increased efficacy. The authors reported that PLGA-TPGS-NPs ability to fight ocular viral infections is yet to be confirmed, however, they are a promising candidate for efficient delivery of ACV to the eyes.

Poorly soluble drugs can be employed for ocular delivery if their resulting eye irritation is under tolerance. The approach employed by Suwannoi et al. examined the ocular delivery route of ACV-loaded with BSA NPs which were surface modified with transactivating transduction (TAT) peptide, to deal with viral-related keratitis.⁸⁰ About 200 nm-sized NPs showed less cytotoxic effects on HCE-T cells and resulted in the greatest ACV permeation in NPs. In vitro study showed that a novel formulation can be used for effective trans-corneal delivery of ACV.

3.1.3. Intravenous delivery

Vedula and his group employed precipitation method to prepare a formulation of ACV-carboxymethyl cellulose acetate butyrate NPs to overcome the inherent limitation of poor water solubility of ACV and to increase its efficacy in treatment of HSV.⁸² The in vitro study showed that particle size of formulation was between 125–450 nm which was administered via intravenous route. The results demonstrated drug loading efficiency of about 40% and 9.2 wt% of the ACV was successfully loaded into nano carriers. This shows the potential of NPs not only in effective drug entrapment but also in an improved dissolution of ACV with around 10 times more release than pure ACV. The authors called for a need for more investigation to evaluate the long-term stability of NPs.

3.2. Efavirenz (EFV)

3.2.1. Intravenous/intranasal delivery

Many ARVs are unable to completely eradicate HIV via CNS targeting and hence chitosan-g-HPbCD NPs of EFV were developed.⁸³ Belgamwar et al. prepared NPs of 198 ± 4.4 nm size via mild ionic gelation technique. The results showed sustained release (99.03 ± 0.30% in 8 h), greater permeability, improved CNS bioavailability, high drug targeting percentage, and entrapment efficiency of 38 ± 1.43%. The in vivo results of intravenous (i.v.) and intranasal (IN) administration to mice are shown in Fig. 9.

3.2.2. Oral delivery

Nano-delivery systems are a viable option to increase the therapeutic efficacy and reduce the side effects of drugs that show poor water solubility. The study by Hari et al. evaluated the effects of using a nano-delivery system for EFV on its bioavailability, distribution, and effectiveness. Eudragit E100 was used to prepare polymeric NPs of size 110 nm by emulsion solvent evaporation method and showed impressive 99% entrapment efficiency.⁸⁴ Another group led by Kumar formulated EFV-loaded Lf NPs for oral delivery via sol-oil protocol and achieved a particle size of 45–60 nm.⁸⁵ They demonstrated that EFV-Lf NPs showed 2× times improved anti-HIV-1 action compared to free EFV and enhanced the oral bioavailability and in vivo pharmacokinetics profile. The formulation was also free from any toxicity issues.

3.3. Zidovudine (AZT)

3.3.1. Intravenous delivery

AZT is an extensively used anti-HIV/AIDS drug but has an inherent shorter half-life, low aqueous solubility, and is stopped by physiological barriers which have limited its use for intravenous administration. It is worth mentioning the study of Joshy et al. which investigated a nanosystem composed of dextran and stearic acid for effective delivery of AZT.⁸⁶ They were able to synthesize NPs of three different formulations ranging from size 356 nm to 730 nm via double emulsion solvent evaporation method. NPs were found to be highly effective in delivery of AZT as they showed entrapment efficiency as high as about 93%. Another approach used AZT loaded with polyvinylpyrrolidone (PVP)/stearic acid (SA)–polyethylene glycol (PEG) nanoparticles (PSNPs) to address the shortcomings of AZT.⁸⁷ A similar synthesis method was used, and NPs of mean size 341 ± 4.34 nm were obtained. Out of three different formulations of PSNPs, the highest encapsulation efficiency shown was about 96% with roughly 79% drug loading capacity. Considerably high cellular internalization was recorded which indicates its in vivo potential. Their group also evaluated AZT-loaded with amide functionalized alginate NPs, prepared via the same route.⁸⁸ The novelty of this work was the preparation of NPs without chemical crosslinking. The particle size was considerably higher i.e., about 432 ± 11.9 nm, and showed a loading efficiency of 29.5 ± 3.2%. The system was biocompatible, showed sustained release, and hence can be incorporated as drug carriers for intravenous administration of AZT.

3.3.2. Oral delivery

Joshy's group also developed biocompatible, safe, and stable lipid NPs modified with polymer gelatin loaded as carriers of AZT, prepared via modified double emulsion solvent evaporation method.⁸⁹ The prepared nanocarrier system showed appreciable loading, controlled release profile, and good compatibility with blood. Encapsulation efficiency of 87.4 ± 0.58% was confirmed in vitro. Hence oral or topical route of administration is preferred for prepared formulation.

The ideal approach for treating many diseases by using the same delivery system is to employ multi-functional NPs. In another study, they prepared hybrid NPs of carboxy methyl cellulose–AZT core enclosed by a Compritol (Comp)–polyethylene glycol shell.⁹⁰In vitro study results showed that the system was biocompatible, cytocompatible, and showed appreciable loading coupled with controlled release of AZT drug and encapsulation efficiency of 82%. The results open doors for more opportunities for the development of LPNs as an efficient delivery vehicle of antiviral drugs.

3.3.3. Transdermal delivery

Two colloidal carrier systems (microemulsion (ME) and lamellar phase (LP) liquid crystal) were investigated for drug permeation capacity.⁹¹ Both in vitro and in vivo studies were conducted to examine the efficacy of the proposed system. The results showed ME showed 2 times higher permeation effect with tolerable skin irritation as evaluated in vivo. Hence ME proved to enhance permeation of drugs and cause negligible irritation to the skin.

3.3.4. Possible routes for aloe vera based administrations

Joshy and his collaborators developed AZT-loaded solid lipid nanoparticles (SLNs) of stearic acid (SA) modified with aloe vera gel via simple emulsion solvent evaporation method.⁹² The formulation was 265.61 ± 80.44 nm in size. The prepared system holds good stability at room and refrigerated temperatures. The study examined the SLN particles in vitro profile and showed enhanced growth and proliferation of cells without exhibiting any toxicity with an encapsulation efficiency of 74.92 ± 1.2%. The proposed combination can be used as an effective tool for the treatment of HIV.

Previous research has shown that Aloe vera can be administered to patients via oral, transdermal, and buccal drug delivery.⁹³ However, all these delivery routes for the application of Aloe vera gel have corresponding setbacks. For instance, when administered through oral route, although it is much easier for patient to intake the drug, however, drug administration is associated with poor bioavailability coupled with low absorption of proteins.⁹⁴ An alternate to oral delivery, buccal route of administration has been researched extensively.⁹⁵ A major drawback of buccal administration is the need for permeation enhancers which if absent would limit membrane permeation of some compounds across cheek mucosa and therefore cause unsuccessful delivery of Aloe vera. But perhaps the most effective route for administration, according to our perspective, is applying Aloe vera drug via skin or transdermal route. It has many positive outcomes associated which include but are not limited to successful avoidance of first-pass metabolism, comparatively and adequately greater surface area for absorption, less frequent doses required and its inherent noninvasive nature.⁹⁶ We suggest more research should be conducted on exploring the nanocarriers systems for achieving synergistic effects of Aloe vera gel and nanoparticles used for its transport to treat viral infections.

3.4. Lopinavir (LPN)

3.4.1. Oral delivery

Treatment of various diseases such as HIV and tuberculosis needs the administration of multiple drugs. Hence fixed-dose combinations were developed for adults which were in the form of tablets and capsules. The lack of child-friendliness of those adult formulations pushed the pharmacists to break the tablets and open the capsules. However, due to preservatives, bitter taste, low solubility, and stability associated with it, the practice lacked standardization with inaccurate doses and reduced clinical efficacy.^97,98 WHO recommended developing sachets and mixing them with liquids or adopting alternatives such as sprinkles to pour over food and tablets which quickly disintegrates once in mouth.⁹⁹ Novel approaches are hence required to develop pediatric formulations for drugs that show poor aqueous solubility. Pham et al. proposed employing nanotechnology to synthesize in situ self-assembly NPs (ISNPs).¹⁰⁰ They prepared a fixed-dose combination of ART drugs namely lopinavir (LPV) and ritonavir (RTV) ISNP granules as well as LPV ISNP granules via warn microemulsion precursors (with modification). The formulation had a size of about 158 nm which resulted in 95% entrapment efficiency for both drugs with 8 hours of stability. Fig. 10a schematically illustrates the preparation method for LPV/RTV granules and ISNPs. Both LPV and RTV were able to entrap in the ISNPs as soon as granules were introduced to water. Moreover, method of preparation is quite simple as it requires only one mixing step to give ISNP granules loaded with drugs having excellent flow properties. The physical stability of LPV and LPV/RTV ISNP granules was assessed in 37 °C physiological conditions. An 8 hour analysis of particle size did not show any apparent change in particle size. This essentially implies that prepared formulations of ISNPs are not affected by changes in pH, temperatures, and ionic strength. The graph of particle size against time (in hours) is shown in Fig. 10b. The dissolution profile was recorded by performing a two-stage dissolution test to monitor the release of LPV from LPV ISNP granules and LPV ISNP granules from LPV/RTV ISNP granules as shown in Fig. 10c. The initial burst release of LPV can be attributed to LPV attached on the surface of LPV, while sustained release afterwards is a result of good entrapment of LPV inside ISNPs. The release profile of LPV/RTV granules is quite like LPV ISNP granules which implies that incorporation of RTV did not affect the released of LPV. Efficacy of taste-masking was proven from results of Fig. 10d, where about 3% of LPV and RTV were released over a period of 1 hour at pH of 6.8. To further verify these results Astree e-tongue method was used. By comparing the distance between the Euclidean from formulations on placebo, taste of prepared formulations was examined. As shown in Fig. 10e, the cluster of LPV/RTV ISNP granules is closer to the placebo ISNP granules than LPV and RTV solutions which indicates effective taste-masking ability of ISNP granules. The results of biodistribution studies shown in Fig. 10f indicates that LPV concentration is fairly increased in liver, kidney, brain, lymph nodes and spleen. These results collectively indicate good potential of ISNP granules in overcoming bad taste of LPV and RTV drugs while exhibiting high entrapment efficiency and achieving pediatric compliance at large. The nanotechnology can be used to formulate a fixed-dose specification of drugs which are poorly water-soluble and are meant to be taken by children who must take multiple drugs for HIV treatment. This would reduce the pill burden and achieve increased children compliance.

Ravi and Vats prepared SLNs-LPV formulation for enhanced HIV action by increased oral bioavailability, evaluated in vivo with a rat model.¹⁰¹ They employed warm oil-in-water (O/W) micro-emulsion technique and prepared NPs of 196.5 ± 3.5 nm size. Entrapment efficiency of 76.5 ± 3.5% was recorded. Another study also reported SLN-LPV formulation prepared via hot self nano-emulsification (SNE) method which achieved 180.6 ± 2.32 nm NP size and entrapment efficiency of 91.5 ± 1.3%.¹⁰² The results showed higher oral bioavailability and lymphatic drug transport. The novel synthesis method of SLN preparation was explored and can be used for the preparation of SLNs of higher fatty acids.

Another novel method for enhancing the oral delivery of LPV via Pullulan Acetate NPs was explored by Ravi et al. by employing Motozato's method and achieving a particle size of nearly 197 nm.¹⁰³ The prepared formulation was quite effective in the treatment of HIV infections by using LPV as an antiviral drug and pullulan acetate NPs as nanocarriers which enhanced the oral bioavailability and hence the effectiveness of the formulation against HIV. The bioavailability of LPV from NPs was about 2× greater compared to free LPV. Higher distribution of LPV-loaded NPs to lymphoid organs was recorded with an entrapment efficiency of 75%.

3.5. Saquinavir (SQV)

3.5.1. Oral delivery

SQV has inherent poor water solubility and thus has poor antiviral activity. For enhancing its antiviral efficacy, bioavailability, and biodistribution, Dodiya et al. incorporated SLNs into SQV.¹⁰⁴ They used hot high-pressure homogenization (HPH) method for the preparation of 215 ± 9 nm [SQSLNs NPs] and 344 ± 16 nm [SNS NPs]. The results showed that bioavailability was increased to 37.39% [SNS] and 66.53% [SQSLN] from 18.87% of SQV micro-suspension. Enough drug was able to entrap as entrapment efficiency of 79.24 ± 1.53% was reported. The antiviral drug used was SQV and the nanosuspensions were of SQV too. The in vivo studies showed greater plasma level concentration than SMS. Thus, SLNs and nanosuspensions are promising candidates for the enhancement of oral bioavailability of drugs that exhibit poor aqueous solubility. A large fraction of drugs suffer from issues of poor aqueous solubility and low bioavailability. Studies have shown that nano-sized formulations have proven to be effective in overcoming this problem, as discussed above.

Yuan et al. examined the result of employing nanocrystal suspension on the oral bioavailability of SQV.¹¹⁶ Nanocrystals of SQV were prepared via the anti-solvent precipitation-high pressure homogenization method. The size of nanocrystals was 205.93 ± 3.74 nm having a narrow poly-dispersity index (PDI) of 0.1. The nanocrystals were hence uniformly distributed. The zeta potential showed a high negative value which is a representation of the good stability of the prepared formulation. The rod-shaped particles were confirmed from TEM micrographs. Fig. 11a shows the results of the cellular uptake study performed on Caco-2 cells. The higher fluorescent intensity of SAQ nanocrystals indicates high drug uptake in cells. Small red dots seen in the cytoplasm of cells after 2 h could potentially be the SQV nanocrystals. In contrast, there are only a few particles observed in the cytoplasm of SQV coarse crystals after a similar 2 h period and at the same level of excitation intensity. The level of fluorescence intensity after 0.5, 1, and 2 hours of SQV nanocrystals can be seen to be significantly higher than SQV coarse crystals which are in line with increased cellular uptake of nanocrystals in Caco-2 cells, as shown in Fig. 11b. The better cellular uptake profile of SQV nanocrystals can be linked to their lower crystallinity. As shown in Fig. 11c, SQV nanocrystals and coarse powder exhibit similar degrees of crystallinity. The drug release study was performed on both coarse and nanocrystals. After a period of 2 h, roughly 20% coarse crystals were able to dissolve compared to 60% dissolution of nanocrystals. As expected, the dissolution of nanocrystals is much quicker than coarse crystals of SQV. A similar experiment was performed by monitoring the release profile of ethyl rhodamine B (RHD) from both coarse and nanocrystals. Release profiles exhibited a similar pattern as before with a greater percentage release from SQV nanocrystals. The RHD was entrapped in the crystal lattice of SQV nanocrystals and showed immediate release once nanocrystals dissolved. The effect of particle size of SQV on the drug transport across the Caco-2 cells monolayer from apical (AL) to basolateral (BL) side was assessed. As seen in Fig. 11d, the percentage of SQV in the receiving chamber (BL side) is increasing as time progresses. Yet again, a greater percentage of drug was able to pass through the monolayers when they were treated with nanocrystals, hence indicating faster drug transport for SQV nanocrystals than coarse crystals. The apparent coefficient of permeability (P_app) of SQV was determined by treating Caco-2 cells with both formulations. The greater permeability of SQV nanocrystals is seen as shown in Fig. 11e. All these results together indicate that SQV nanocrystals have enhanced oral drug absorption. A recent study by Krieser and her group aimed to improve the taste masking and stability of the SQV nanostructures developed for enhanced pediatric adherence.¹⁰⁵ They employed interfacial polymer technique and prepared SQV NPs of 136–158 nm average diameters. The prepared formulation exhibited sustained release, a high drug loading capacity of 80%, ability to encapsulate 97% of the drug with low dynamic viscosity. The in vitro studies showed that SQV NPs showed excellent stability and controlled release properties. The dose can be given in a liquid form to the children with a taste acceptable to them. This amounts to an appreciation for designing drug delivery systems to treat children suffering from HIV.

3.6. Indinavir (IDV)

3.6.1. Oral delivery

The use of biodegradable polymeric NPs for improved oral delivery is a unique approach. Indinavir is an anti-HIV agent which has limited aqueous solubility. The study reported increased drug loading and EE of the proposed system.¹⁰⁷ The strategy employed was the preparation of mPEG-PCL NPs to enhance bioavailability and increase aqueous solubility. They reported emulsification solvent evaporation method to prepare the NPs with an average size of 211 ± 10.12 nm. At a pH of 1.2 (PBS) after 96 hours, 60% drug release was recorded. The developed copolymer can self-assemble into NPs and has good drug loading and entrapment efficiencies. The results from in vitro studies show that mPEG-PCL and IDV system shows initial burst release which is then followed by sustained release. On other hand, in vivo studies showed that the drug administered to rat via oral route show an increase in plasma concentration, and appreciable cellular uptake by Caco-2 cell line with improved circulation was also reported. Hence a novel strategy was explored by using biodegradable polymeric NPs, surface modified to enhance oral bioavailability.

To treat children suffering from HIV, the dose being administered to them via oral route must be taste-masked and in liquid form to prevent difficulties in swallowing the tablets. A study reported the preparation of 155 ± 7 nm size NPs of formulation of Monoolein and IDV, using magnetic stirring and high-pressure homogenization method.¹⁰⁸ The incorporation efficiency of the formulation was 96% and IDV was able to remain in the same concentration for a month while exhibiting a sustained release profile. This combination was not only biocompatible but showed no irritation with improved taste-masking and the ability to overcome the bitter taste of the drug. Thus, it can be used for pediatric HIV treatment.

3.6.2. Intravenous delivery

One of the shortcomings of the IDV drug is that it has limited effectiveness in inhibition of virus due to efflux by P-gp at BBB. Employing Tween 80 containing LNEs for enhancing the delivery of IDV to brain was shown to be a viable strategy.¹⁰⁹In vivo studies show that brain uptake in mice was considerably improved. Further studies may prove IDV effectiveness in the reduction of viral load in brain.

3.7. Lamivudine

Glycyrrhizin LMW CS NPs can be used as an effective drug carrier system for liver targeting with decreased damage to tissues and sustained release of the drug. Glycyrrhizin has demonstrated antiviral activities against a broad spectrum of viruses.^110,111 Chitosan is a non-toxic, biocompatible, and biodegradable polymer that is widely used as a carrier molecule for various vaccines, genes, protein molecules, etc.^112–116 Mishra et al. investigated the controlled release of GL conjugated LMW CS-NPs in liver targeting. Model drug lamivudine was encapsulated within GL-CS-NPs and intravenously administered to a mouse to examine the targeting efficacy. Conjugation of GL was determined by FTIR spectrum as shown in Fig. 12a. The amino functionality (–NH₂) of CS has caused stretching of N–H at wave numbers 3346 cm⁻¹ and 3371 cm⁻¹ in Fig. 12a(A) and hence this spectrum is of CS-NPs. While in Fig. 12a(B), –NH deformation of –NH–CH₂ verifies the successful conjugation of GL with an amino group in NPs and hence this spectrum represents GL-CS-NPs. In vitro release profile of lamivudine from NPs was examined in PBS solution maintained at a pH of 7.4. The in vitro study showed that CS-NPs were able to release 59.2 ± 2.1% while GL-CS-NPs exhibited 42.9 ± 1.8% release of lamivudine after 72 hours. It is obvious from the graph that the release profile showed a biphasic fashion, with an initial burst followed by a sustained release. The reason for initial burst release can be the attachment of drug particles on the surface of NPs. Lower drug release from GL-CS-NPs can be attributed to the presence of structural features which could have resulted in a double barrier effect. The TEM micrographs showed a smoother surface for CS-NPs than GL-CS-NPs which can be due to the substitution of –NH₂ of LMWC by GL (Fig. 12b). The fluorescence micrograph of GL-CS-NPs showed a higher accumulation of hepatocytes cells than plain dye solution and dye-loaded CS-NPs. The fluorescence image of the liver shown in Fig. 12c shows that GL-CS-NPs were able to localize preferentially in the liver and hence greater percentage of lamivudine was seen in hepatocyte tissues with GL-CS-NPs as compared to plain drug. The results of the study indicate that loading lamivudine in GL combined with LMWC-NPs improves the resistance time and quantity of drugs in the liver. This can lead to a reduction in the dosage and quantity of each dose. Moreover, hepatic targeting and controlled release can decrease the toxicity associated with lamivudine. Hence, liver targeting via controlled release of GL-CS NPs can be an effective strategy for the treatment of HIV.

Another route employed the hot homogenization method to produce lamivudine-MLN (multiple lipid NPs) to enhance the oral administration of the formulation.¹¹⁸ The size reached after the combination of the drug and the NPs was about 450 nm. The simulation studies indicate that around 1.3% of MLN-lamivudine would be released in 4 hours in gastric fluid. The release profile showed sustained and controlled release for about 45 hours. The developed system can be applied as a topical drug or orally administered (after resuspension).

3.8. Tenofovir (TFV)

3.8.1. Vaginal route

Due to rising HIV cases, there is a need to develop nanotechnology-based microbicides for the effective prevention of HIV sexual transmission. Hence there is a need for the development of nanocarriers that can act as potential drug delivery vehicles to administer microbicides to the targeted site. Although topical pre-exposure prophylaxis (PrEP) with ARTs has been developed and showed appreciable results in the prevention of vaginal transmission of HIV, because of poor adherence by women undergoing clinical trials¹¹⁹ and concerns of non-biocompatibility, there is a need for the development of optimized microbicides. Machado et al. proposed incorporating PLGA/SA nanocomposite inside the tenofovir drug and its subsequent incorporation in hydroxypropyl methylcellulose (HPMC)/PVA-based film.¹²⁰ Nanocomposite with a mean size of 127 nm, prepared via double emulsion/solvent evaporation method, showed a drug association efficiency of 50%. The characterization of these films was performed by SEM and EDS techniques. The NPs can be seen to be uniformly embedded in the thin film as even at reasonably good magnification aggregates of particles are not visible as shown in Fig. 13a(A). This result was further confirmed by fluorescence microscopic imaging in Fig. 13a(B) where no visible difference can be observed for the film fracture surface and the film which essentially implies uniform distribution of particles. The thicknesses of NPs-in-film and the film were in general agreement with values 85 μm and 70 μm, respectively. Possible reason for this difference can be the presence of vacuum inside the SEM chamber which may have caused the film to retract. Further observations with SEM show surfaces of NP-in-film and the film were quite homogeneous with the exception to presence of some scales on the TFV-film (Fig. 13a(C and D)). The cause of precipitation can be the incomplete solubilization of free TFV during the drying process. Similarly, absence of scales for TFV-PLGA/SA NPs-in-film indicates effective solubilization thanks to incorporated particles. The elemental analysis results did not indicate the presence of phosphorous which is present in the phosphonate group of TFV (Fig. 13a(E)). This means that drug was so deeply embedded in the film that even incident electron beam was not able to detect it. Presence of TFV was detected on the TFV film by the same EDS analysis as seen in Fig. 13a(F). The release profiles were recorded for NPs-in-film, TFV film alone and for prepared NPs and they are shown in Fig. 13b. TFV film exhibited initial burst release by releasing about 80% of its drug in the first few minutes and then after 2 hours about 90% drug was released. This result was obvious as TFV is a highly water-soluble drug and has a quick disintegration time. Secondly, the films containing TFV-loaded NPs showed mild burst release at first by releasing about 30% of the drug in 15 minutes, followed by a controlled release. Total drug released after 24 h was nearly 60%. The release was initially rapid as TFV was present at the surface of NPs as observed also for TFV film (NPs not incorporated). The release profile for TFV-PLGA-SA NPs not incorporated in film is like that of NPs-in-film. However, the film matrix imposed a delaying effect on the release of TFV during film disaggregation for 24 h. This effect was enhanced by the presence of PVA/HPMC on the surface of NPs, providing further hindrance to drug release. This biphasic release pattern is beneficial in the sense that initial burst release creates high genital levels of TFV which provide immediate protection while assuring sustained release for many hours. To evaluate the in vivo safety of the prepared films regarding possible toxicity which may arise later, a 14 days study was conducted. Both TFV-film and NPs-in-film were subjected to daily vaginal administration. Mice given PBS washing or vaginally administered with Film or VCF® were taken as controls. No biological change which could indicate the toxic nature of films was recorded during the study as vaginal administration to mice did not show any adverse effect on health, size, or weight. Vaginal histology of mice showed change only in the case of VCF®, as seen in Fig. 13c. This mild thinning of epithelium was verified by assessment of an average number of epithelial cell layers as shown in Fig. 13d. The mouse model was used for the first time to determine the safety of vaginal films and they were found to be biologically safe to be administered to women (Fig. 13e). The vaginal films can also be a temporary substitute for rings for women requiring occasional protection as they showed quick disintegration once in contact with the simulated vaginal fluid (SVF).

Another study examined a thermogelling system containing TFV-loaded with chitosan NPs synthesized via ionic gelation method.¹²¹ The biocompatible formulation reached a size of 545.1 ± 69.17 nm once the drug was incorporated into NPs. Gelation temperature of the gel was tolerable for the administration to women and the gelation starts once it is fully administered to the vagina. However, due to the high water solubility of TFV, the NPs showed very low encapsulation efficiency (6.8 ± 3.1%) and drug loading content of 1.86 ± 0.85%. The in vitro study showed that the initial burst release effect was reduced to 27% with the formulation. The prepared vaginal gel holds significance in ease of administration as well as effectiveness for the treatment of women suffering from HIV.

Meng et al. examined the effects of TFV loaded with CS-TGA NPs against HIV prevention.¹²² They used ionotropic gelation to prepare CS-TGA NPs of mean size between 240–252 nm. Greater encapsulation efficiency of 22.60% was recorded than the study quoted previously. Both NPs did not show any toxicity in 2 days. The percentage of mucoadhesion was five times greater in CS-TGA NPs than CS-NPs. This shows that the prepared NPs have the potential to increase the retention time of TFV, hence making it more effective in the treatment of HIV.

Thiolated chitosan (TCS) core/shell nanofiber (NF) can improve the loading capacity of TFV.¹²³ As stated previously, TFV is highly water-soluble. The coaxial electrospinning technique was utilized to prepare NFs having a core of PEO and shell composed of PLA/TCS. The NFs reached a mean diameter of 99.53 nm with smooth surface morphology. They were found to be safe for topical administration. A significant increase in drug loading capacity was recorded. At concentration of 1 mg mL⁻¹, NFs were non-cytotoxic. Their biocompatibility was proved from in vivo studies. Hence TCS core/shell NFs can be employed as a delivery vehicle of TFV. Table 2 presents a summary of various studies over the past decade showing well known antiviral drugs and their combinations with NPs along with other important parameters.

Results of various studies over the past decade showing efficacies of different drug carrier systems with relevant parameters. (EE₁: encapsulation efficiency, EE₂: entrapment efficiency).

Antiviral Drug	Nanoparticle(s)	Action against virus	Route of administration	In vitro/in vivo/ex vivo	Size (nm)	Polydispersity index [PDI]	Synthesis method	Efficiency	Reference
Acyclovir	SLNs	[HSV]-TK	—	In vitro	180 nm	—	Emulsification and low-temperature solidification method	78% EE₂%	124
	PEGylated lipid polymeric NPs	HSV-1 and HSV-2	Oral	In vitro, ex vivo	187.7 ± 3.75 nm	0.179 ± 0.03 to 0.429 ± 0.12	Box–Behnken design (BBD)	83.81 ± 1.93% EE₂%	69
	Bilosomes NCs	HSV-1, HSV-2, and varicella-zoster (VZV)	Oral	In vitro, in vivo, ex vivo	121.2 ± 3.21 nm	0.261 ± 0.023	Thin-film hydration technique. (Optimize by Box–Behnken statistical design)	71.87–88.67% EE₂%	75
	Gel nanoemulsions (NEs)	HSV	Ocular	In vitro, in vivo, ex vivo	28 nm to 34 nm	0.38 ± 0.04 to 0.47 ± 0.05	Low energy method	2.8× increase in drug permeation	125
	Bovine serum albumin (BSA) NPs	HSV	Transcorneal/Ocular	In vitro	173.0 ± 9.5 to 204.7 ± 15.5 nm	0.079 ± 0.023 to 0.226 ± 0.025	—	—	80
	PLGA polymer stabilized with TPGS nanosystem	HSV	Ocular	In vitro, in vivo, ex vivo	262.38 ± 11.85 nm	0.255 ± 0.011	—	58.42 to 80.15% EE₁%	81
	Carboxymethyl cellulose acetate butyrate NPs	HSV	Intravenous	In vitro	∼125–450 nm	—	Precipitation processes (one simple and other rapid)	Drug loading efficiency of 40%	82
	Eudragit RLPO® based NPs	—	Oral	In vitro	82 ± 3.83 nm to 532 ± 4.86 nm	0.308 ± 0.24 to 0.716 ± 0.25	Nanoprecipitation technique	79.34 ± 1.64% EE₂%	126
	Chitosan NPs	HSV	Topical delivery	In vitro	240.0 ± 62.4 nm	0.53 ± 0.12	Using cross-linked chitosan with tripolyphosphate (TPP)	16% EE₁%	127
	Chitosan NPs	OVI	Ocular	In vitro	200–495 nm	—	Ionic gelation technique	56 to 80% EE₁%	128
	Microemulsions (ME)	Herpes virus infections	Topical	In vitro	6.2 ± 0.2 nm to 15.1 ± 1.5 nm	—	Pseudo ternary phase diagrams	2× fold increase in ACV accumulation	129
	β-Cyclodextrin-poly(4-acryloylmorpholine) mono-conjugate (β-CD-PACM)	HSV-1	Oral	In vitro	150 nm (unloaded) and 200 nm when (loaded)	—	Solvent injection technique	83% EE₁%	130
	Liposomes	HSV	Intranasal	In vivo	1048.1 ± 101.3 nm and 627.4 ± 36.9 nm (for two methods)	—	Drug lipid film hydration method	43.20%	131
	Bovine serum albumin (BSA) NPs	HSV	Ocular	In vitro	∼200 nm	—	Desolvation method	84.59 ± 1.81 and 52.05 ± 2.03 EE₂%	132
Adefovir dipivoxil	SLNs	HBV	—	In vitro	389.4 ± 166.5	−0.371	Solvent diffusion method	15% EE₂%	133
Atazanavir	Eudragit RL100 NPs (ATV NPs)	HIV	Oral	In vitro, in vivo	465.59 nm	0.372	Nanoprecipitation method	41.3 to 56.9% EE₁%	134
Atazanavir and darunavir	LNPs	HIV	Subcutaneous	—	33.6–35.6 nm	—	Sonication of hydrated lipid–drug suspension	85.5 ± 8.2 [ATV], 85.1 ± 7.1 [RTV], and 6.1 ± 0.8% [TFV] EE₂%	135
Atazanavir, efavirenz, and ritonavir	Atazanavir, efavirenz, and ritonavir NPs (nano ART)	HIV-1	Parenteral administration	—	300–645 nm	—	High-pressure homogenization	—	136
Azidothymidine	Galactosylated liposomes	AIDS6	Intravenous	In vitro	120.01 ± 2.11 nm	—	Esterification of galactose	EE₂% (L1 to L4): 42.35 ± 0.38, 54.26 ± 3.25, 36.69 ± 3.10, 31.44 ± 2.22 (%)	137
Atazanavir and darunavir	Lipid polymer hybrid NPs (LPHNs)	HIV	Oral	In vitro	50 nm	—	One-step optimized nanoprecipitation method	62, 68.1 and 68.5% w/w EE₁%	138
Dolutegravir	Chitosan-based polymeric NPs	HIV	Oral	—	140–548 nm	—	3-Step process demineralization, deproteinization, and deacetylation	-	139
Dolutegravir sodium	β-Cyclodextrin-based NPs	Neuro-AIDS	Intranasal	In vitro, in vivo	72.47 ± 4.8 to 106.5 ± 5.6 nm	0.306 ± 0.002 and 0.475 ± 0.004	Cross-linking hydroxypropyl β-cyclodextrin (HPβCD) with diphenyl carbonate	77 ± 3.35% EE₂%	140
Efavirenz	Chitosan NPs	HIV	Oral	In vitro	±104 nm	—	Ionotropic gelation method	91.09% EE₂%	141
	Eudragit E100	HIV/AIDS	Oral	In vitro, in vivo	110 ± 5 nm	0.201 ± 0.05	Emulsion solvent evaporation method	99% EE₂%	84
	Lactoferrin NPs	HIV	Oral	In vitro, in vivo	45 ± 60 nm	<0.341	Sol-oil protocol	2× times improved anti-HIV-1 action compared to free EFV	85
	SLNs	HIV	Oral	In vitro, in vivo	168 nm	<0.220	Hot homogenization technique followed by ultrasonication method	60 ± 5% EE₂%	142
	SLNs	HIV	Oral	In vitro	124.5 ± 3.2 nm	0.234	—	86% EE₂%	143
	Poly(epsilon-caprolactone) (PCL) NPs	HIV/AIDS	Oral	In vitro, in vivo	200–250 nm	Narrow	Double-emulsion/spray-drying method	86–93% EE₁%	144
	Nanoemulsion of EFV	HIV/AIDS	Oral	In vitro, in vivo	Less than 30 nm	—	Phase inversion composition method	80% release within 6 hours	145
	Chitosan-g-HPβCD NPs	Neuro-AIDS	Intranasal	In vitro, in vivo	198 ± 4.4 nm	0.325 ± 0.004 to 0.675 ± 0.005	Ionic gelation method	38 ± 1.43% EE₂%	145
Efavirenz (EFV) and lopinavir/ritonavir (for boost)	PLGA NPs	HIV	Intracellular	In vitro	138.3–55.4 nm	—	High-pressure homogenization method	>79% EE₂%	146
Efavirenz and nevirapine	SLNs	HIV/AIDS	—	In vitro	128.7 nm to 182.2 nm	—	Modified emulsion/microemulsion procedure	EFV ∼98% and NVP ∼30% EE₂%	147
Elvitegravir	PLGA-EVG NPs	HIV-1	Intraperitoneally	In vitro, in vivo	Less than 200 nm	—	Nano-precipitation technique	∼95% loading efficiency of drug	148
Elvitegravir	PLGA-EVG NPs	HIV-1	—	In vitro	∼47 nm	-	Nano-precipitation technique	∼92% EE₁%	149
Enfuvirtide and protoporphyrin IX	Nano-liposome	HIV-1	Intravenous and intramuscular administration	In vitro	—	—	Surfactant-based nanoparticles A rapid extrusion procedure	—	150
Foscarnet	Chitosan NPs	HIV-1, herpesvirus DNA polymerase	Oral, topical	In vitro, in vivo	292 ± 5 nm to 497 ± 13 nm	0.26 ± 0.01 to 0.78 ± 0.21	—	—	151
Griffithsin (GRFT) (an anti-viral lectin)	mPEG-PLGA GRFT NPs	HIV-1, HSV-2	Topical	In vitro, in vivo	152 to 345 nm	—	Double emulsion solvent evaporation technique	85.6 ± 11.0 EE₁%	152
Indinavir	Lipid nanoemulsion (LNE)	HIV	Intravenous	In vitro, in vivo	200.1 ± 73.2 nm (lowest value)	0.05 ± 0.04	—	98.8%, 98.9% and 99.0% EE₂%	109
	Monoolein-based NPs	HIV	Oral	In vitro	155 ± 7 nm	0.16 ± 0.03	Magnetic stirring and high-pressure homogenization	96% drug incorporation efficiency	108
	mPEG-PCL NPs	HIV	Oral	In vivo	211 ± 10.12 nm (mean particle size)	0.22 to 0.68	Emulsification solvent evaporation method	60%, 40% and 15% drug release percent	107
Indinavir and lactoferrin	Nanoemulsion	HIV	Drug injection	In vitro, in vivo	112 ± 3.5 nm	0.20 ± 0.02	High-speed homogenization method	-	153
Ivermectin	Ivermectin NPs	ZIKV	Oral	In vitro, in vivo	∼65 nm	—	—	Conjugation efficiency of ∼60% for empty NPs and ∼40% for 20% IVM feed loaded NPs	154
Lamivudine	Chitosan NPs	HIV-1	Oral	In vitro, in vivo	120.7 ± 3.1 nm [CS-NPs]; 145.8 ± 4.2 [GL-LMWC-NPs]	0.09 ± 0.01 [CS-NPs]; 0.11 ± 0.06 [GL-LMWC-NPs]	Depolymerization followed by ionotropic gelation method	71.37 ± 1.19% EE₁%	117
Lamivudine	MLNs	—	Topical (semisolid) or oral (after resuspension)	In vitro	∼450 nm	<0.3	Hot homogenization method in conjunction with high shear and ultrasonication	—	118
Lopinavir	SLNs	HIV/AIDS	Oral	In vivo	196.5 ± 3.5 nm	0.11 ± 0.01	Warm oil-in-water (O/W) micro-emulsion technique	EE (%) 76.5 ± 3.5%	101
	In situ self-assembly nanoparticles (ISNPs)	HIV	Oral	In vitro, in vivo	Less than 158 nm	–	Warn microemulsion precursors with modification	95% EE₂%	100
	PLGA NPs	HIV/AIDS	Oral	In vitro, in vivo	142.1 ± 2.13 nm	–	Solvent diffusion (nanoprecipitation) method	93.03 ± 1.27% EE₂%	155
	Pullulan acetate NPs	HIV/AIDS	Oral	In vitro, in vivo	197 ± 4 nm (∼197 nm)	<0.2	Motozato's method	75% EE₂%	103
	Poly-e-caprolactone (PCL) nanoparticles (NPs)	HIV/AIDS	Oral	In vitro, in vivo, ex vivo	195.3 ± 2.3 nm	0.10 ± 0.01	Oil-in-water emulsion-solvent evaporation technique	93.9% EE₂%	156
	SLNs	HIV/AIDS	Oral	In vitro, in vivo	180.6 ± 2.32 nm	0.133 ± 0.001	Hot self-nano emulsification (SNE) technique	91.5 ± 1.3% EE₂%	102
	Compritol®-SLNs	HIV/AIDS	Oral	In vivo	156 nm	–	Hot homogenization method followed by ultrasonication	98.99% EE₂% (highest)	157
Lopinavir–ritonavir–tenofovir	Drug-combination nanoparticles (DcNPs)	HIV	Subcutaneous	In vitro	—	—	Aseptic technique	Highest drug association efficiency of 99 ± 8.2% for lopinavir, 92 ± 7.1% for ritonavir and 10 ± 0.8% for tenofovir	158
Nevirapine	Mesoporous silica nanoparticles (MSNPs)	HIV-1	—	In vitro	60 nm	—	Stober's method	—	159
	PS80-coated PCL NPs	HIV/AIDS	Intravenous	In vitro, in vivo	218.3 ± 7.3 nm	0.283 ± 0.038; 0.179 ± 0.00	Emulsion solvent evaporation technique	50.71% EE₂% (highest)	160
	Cellulose acetate butyrate (CAB) NPs	HIV/AIDS	—	In vitro	305.76 ± 5.7 nm	0.29 ± 0.03	Emulsification solvent evaporation method	75.89 ± 1.36% EE₁%	161
	Nanoliposomes	HIV/AIDS	—	In vitro	157 nm	—	Thin-film hydration	78.14% and 76.25% EE₁%	162
Oseltamivir	SeNPs	EV71	—	In vitro	10 nm	—	—	—	50
Raltegravir + efavirenz	PLGA NPs	HIV	Intravaginal	In vitro	81.8 ± 6.4 nm	—	Emulsion–solvent evaporation method	55.5% [RAL] and 98.2% [EFV] EE₁%	163
Ritonavir	SLNs	HIV-1	Oral	In vitro	170–250 nm	0.2	Solvent emulsification method and double emulsion method	53.2% EE₂%	164
	SLNs	HIV/AIDS	Oral	In vitro, in vivo	Less than 300 nm	0.361	Solvent evaporation followed by ultrasonication	53.20 ± 4.13 to 73.04 ± 2.85% EE₁%	165
	PLGA NPs	HIV/AIDS	—	—	42–102 nm	0.381	Solid-in-oil-in-water (s/o/w) solvent evaporation technique with some changes	75% EE₁%	166
	Lopinavir (LPN) NPs	HIV-1	Oral	In vitro, in vivo	∼320 nm	<0.2	Antisolvent precipitation and high-pressure homogenization techniques	—	167
Saliphenylhalamide (SaliPhe)	SiNPs	Influenza A viruses (IAVs)	Inhalation or intravenous (envisioned)	In vitro	129 ± 10 nm	0.112	—	—	168
Saquinavir	SQV NPs	HIV	Oral	In vitro	136–158 nm	—	Interfacial polymer technique	> 97% EE₁%	105
	SQV nanocrystals	HIV	Oral	In vivo, ex vivo	205.93 ± 3.74 nm	0.1	Anti-solvent precipitation high-pressure homogenization method	—	106
	Chitosan NPs	AIDS	—	In vitro	10–200 nm	—	Ionic gelation technique	72% EE₁%	169
	SLNs	HIV/AIDS	Intravenous	—	120 nm to 450 nm	—	—	—	170
	SLNs	HIV	Oral	In vitro, in vivo	215 ± 9 nm [SQSLNs]; 344 ± 16 nm [SNS]	0.196 ± 0.019 of SNS	Hot high-pressure homogenization (HPH) method	79.24 ± 1.53% EE₂%	104
Stavudine	Chitosan NPs	HIV	Oral	In vitro	212 nm (PSD)	—	Ionic gelation of chitosan with tripolyphosphate anions	85.8 ± 0.16% EE₂% (highest)	171
	SLNs	HIV-1/AIDS	Intravenous	In vitro, in vivo, ex-vivo	75 ± 1.22 nm	0.12	Homogenization	High labeling efficiency	172
	Mannosylated liposomes	HIV	Intravenous	In vitro, in vivo	120 ± 1.52 nm	—	Esterification of mannose	47.2 ± 1.57% EE₂%	173
Stavudine, delavirdine, and saquinavir	SLNs	HIV/AIDS	—	—	142–294 nm	—	Involves emulsion	—	174
Tenofovir	Thiolated chitosan (TCS) core/shell nanofiber (NF)	HIV-1	Topical	In vitro, in vivo	58.81 nm	-	Coaxial electrospinning technique	95% (in 5 hours)	123
	Chitosan NPs	HIV	Vaginal route	In vitro	545.1 ± 69.17 nm	0.663 ± 0.107	Ionic gelation	6.8 ± 3.1 EE₁%	121
	(PLGA)/stearylamine (SA) composite NPs	HIV	Vaginal route	In vitro, in vivo, ex vivo	127 ± 1 nm	0.27 ± 0.01	Double emulsion/solvent evaporation method	Drug association efficiency >50%	120
	Chitosan–thioglycolic acid-conjugated (CS–TGA) NPs	HIV/AIDS	Topical	In vitro	240.1 nm CS NPs; 252.3 nm CS-TGA-NPs	0.298 ± 0.002 [CS]; 0.317 ± 0.052 [CS-TGA]	Ionotropic gelation	22.60% EE₁%	122
	PLGA NPs loaded with efavirenz NPs or saquinavir NPs	HIV-1 BaL infection	Topical	In vitro	227 ± 1.8 nm [EFV]; 189 ± 96.3 nm [SQV]	0.05 [EFV]; 0.486 [SQV]	Emulsion or nanoprecipitation techniques	44.5 ± 2.7 [EFV] and 48.3 ± 15.2 [SQV]	175
Tenofovir, alafenamide and elvitegravir	TAF + EVG NPs	HIV	Subcutaneous	In vitro, in vivo	190.2 ± 2.3 nm	0.14 ± 0.01	Oil-in-water emulsion solvent evaporation technique	54.1 ± 3.6 [TAF] and 44.6 ± 2.4% [EVG] EE₁%	176
Tenofovir alafenamide	Emtricitabine (FTC) loaded NPs	HIV-1	Subcutaneous and oral	In vivo, ex vivo	233.2 ± 12.8 nm	0.11 ± 0.05	Oil-in-water emulsion solvent evaporation technique	69.2 ± 14.5% [TAF] and 65.9 ± 18.2% [FTC] EE₁%	177
Tenofovir disoproxil fumarate	Chitosan NPs	HIV/AIDS	Oral	In vitro, in vivo, ex vivo	156 ± 5 nm	0.16 ± 0.06	Ionic gelation technique	48.2 ± 1% EE₂%	178
Valacyclovir	PLA-PEG NPs	HSV	Oral	In vitro, in vivo	∼30 nm	—	Nanoprecipitation	11.4 ± 0.5 EE₂% (highest)	179
Valacyclovir	SLNs	HSV	Ocular	In vitro, in vivo, ex vivo	202.5 ± 2.56 nm	0.252 ± 0.06	Solvent emulsification/evaporation method	28.01 ± 1.89 to 58.82 ± 2.45% EE₂%	180
Zidovudine	NLCs	HIV	Oral	In vitro	100 to 300 nm	< 0.3	Hot ultrasonication and microwave assisted method	44 ± 3%, 22 ± 2% EE₂%	181
	Alginate NPs	HIV/AIDS	Intravenous	In vitro	432 ± 11.9 nm	—	Emulsion solvent evaporation method	Loading efficacy of 29.5 ± 3.2%	88
	Lipid NPs modified with polymer gelatin	HIV/AIDS	Oral and topical	In vitro	224 ± 31.2 nm [PLNs of SA]; 291.2 ± 38 nm [PLNs of comp]	—	—	87.4 ± 0.58% EE₁%	89
	Nanosized polyelectrolyte complexes (PECs)	HIV	—	In vitro	100–200 nm	0.125–0.305	—	Drug release of 38.1% at pH 4.5 and 31.2% at pH 7.4	182
	SLNs	HIV	Parenteral, oral, ophthalmic, and topical	—	222–227 nm [AZT-SA], 402 nm to 434 nm [AZT-SA-AV]	0.2 to 0.3 [AZA-SA], 0.38–0.45 [AZT-SA-AV]	Simple emulsion solvent evaporation method	74.92 ± 1.2% EE₁%	92
	Chitosan NPs	AIDS	Nasal	—	260 ± 1.70 nm, 330 ± 12.9 [NP1, NP2]; 406 ± 14.0 and 425 ± 14.5 for AZT-loaded NP1 and NP2	0.247, 0.329, 0.390, 0.381	Ionotropic gelation method	17.58% ± 1.48 and 11.02% ± 2.05 EE₂% for NP₁ and NP₂	183
	Lipid-polymer hybrid NP	HIV	—	In vitro	175 ± 2.5 nm	0.196	Melt emulsification-probe sonication technique	6.5 ± 0.50 to 49.26 ± 0.75% EE₂%	184
	PLA–PEG blend NPs	AIDS	Intranasal	In vivo	328.1 ± 8.6 nm	0.383	Double emulsion–evaporation method	52% EE₁%	185
	SLNs	AIDS	Oral	In vitro	621 nm	—	W/o/w double-emulsion solvent–evaporation method	27% EE₂%	186
	Dextran and stearic acid NPs	HIV/AIDS	Intravenous	In vitro, in vivo	356 nm to 730 nm	—	Double emulsion solvent evaporation method	93.46% EE₁%	86
	PVP/SA-PEG NPs (PSNPs)	AIDS	Intravenous	In vitro	341 ± 4.34 nm	0.3 ± 0.04	Emulsification-solvent evaporation method	37.19% to 79.2%	87
	Hybrid NPs of CMC-AZT core enclosed by shell of Comp-PEG	AIDS	Oral	In vitro	161.65 ± 44.06 nm	—	—	82% EE₁%	90
Zidovudine + efavirenz + lamivudine	Lactoferrin NPs	HIV	Oral	In vitro, in vivo	67 nm	—	Sol-oil protocol	58 to 71% EE₁%	187

Open in a new tab

4. Conclusion

The established potential of nanotechnology in antiviral applications coupled with massive progress in designing wide categories of different nanomaterials-based antiviral drugs gives many expectations to the research community to explore their potential further to overcome their existing drawbacks. The nano-based systems can prove fruitful in overcoming the associated drawbacks with the current therapies such as low oral bioavailability, issues with hemocompatibility, chances for skin diseases due to topical exposure of drug, toxic nature of the drug, reduction in drug's effectiveness due to frequent administration, to name a few. However, as per the best of our knowledge, most of these nano-based systems designed to date are not approved for clinical use or are still under clinical trials, despite exhaustive and continued effort for more than 24 years. It is expected that in upcoming years, we shall witness more clinical approvals and applications of these nano-based systems which will definitely help overcome the health issues globally.

5. Future perspectives

Tuning at the nanoscale can give us interesting properties for a range of applications. In our review, we have covered many functional metallic NPs as well as a variety of drugs that can be tailored by using NPs as their delivery vehicles. However, in order to treat patients globally in vast numbers (such as with COVID-19 pandemic recently), it is not possible to develop antiviral drugs in such a short span of time and fully overcome their existing drawbacks. As we discussed earlier, frequent drug administration is itself counterproductive since it generates an immune response from body and increases its drug resistance resulting in a decline in the drug's efficiency. Moreover, the route of administration for each drug must be carefully chosen. There are associated disadvantages with the choice of each route. For instance, oral administration may not be feasible for children, ocular delivery could prove detrimental for eyes and topical exposure of drug to skin may cause skin diseases. On contrary, vaccines have proven to be a rather better option in fighting pandemics in the past century. However, vaccines also have associated shortcomings such as insufficient cellular immunity, risk of antibodies dependent enhancements (ADE) and lack of cross-permeation. Our discussion regarding the potential of nanomaterials in antiviral applications gives useful insight that they can be a good candidate in development of novel vaccines against various viral infections. We suggest the scientific community and interested researchers to also focus on further development of these “nanovaccines”, evaluate their potential against viruses, weigh their pros and cons, and explore methods for their cost-effective and large-scale manufacturing so that they can deal with current and upcoming global health challenges posed by such highly unpredictable viral outbreaks.

Author contributions

Muhammad Aanish Ali (drafting and paper writing); Dr Nagina Rehman (drafting and reviewing the paper); Dr Tae Joo Park (resources and supervision); Dr Muhammad Abdul Basit (conceptualization, resources and data analysis).

Conflicts of interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

Supplementary Material

Acknowledgments

The work is mainly done at Department of Materials Science and Engineering at Institute of Space Technology, Pakistan and supported by NEL, Hanyang University South Korea from Project No. 20010727 (Technology Innovation Program by Ministry of Trade, Industry and Energy Korea).

Biographies

Biography

Engr Muhammad Aanish received his bachelor’s degree in Materials Science and Engineering from Institute of Space Technology (IST), Islamabad, Pakistan in September 2022. He is an active researcher in the fields of development of Nanomaterials for various engineering applications such as photovoltaics and biotechnological treatment of waste water. He is currently a member of research group “Nanomaterials for Advanced Energy Applications” (NAEA) headed by Dr Basit at IST. He has participated in several review/research papers during his academic career so far. His key ambition is to conduct extensive and valuable research that could provide a good value to research community.

Biography

Dr Nagina Rehman graduated in Zoology from Bahauddin Zakariya University Multan, Pakistan in 2009. Then she joined University of Agriculture Faisalabad to accomplish her MPhil Zoology in 2013 with research specialization of biodiversity. Having PhD from Government College University Faisalabad Pakistan (2020), Dr Nagina chose a multidisciplinary research career in Nanotechnology for Zoological Species. She is currently working as Assistant Professor at Riphah University, Faisalabad (Campus) and motivated to investigate and research the toxicological effect/control of nanomaterials in human beings.

Biography

Dr Tae Joo Park is currently serving as Professor of Materials Science & Chemical Engineering at Hanyang University (HYU) Ansan, Republic of Korea. Dr Park has PhD from Seoul National University, Korea and research experience from University of Texas Dallas, USA. He established Nanodevice Engineering Laboratory at HYU and conducted many funded research projects in parallel to the research supervision of many local/international students in the domain of energyharvesting/storage/nanoelectronic/neuromorphic devices, film/particle ALD and 2D-electron gas. Owing to expertise in research and innovation, Dr Park has won many awards and honors from various firms including Samsung (2019) and Merck (2021) etc.

Biography

Dr Muhammad Abdul Basit is serving as Associate Professor at Department of Materials Science & Engineering at IST Pakistan, where he established: “Nanomaterials for Advanced Energy Applications” research group too. After having graduation from UET Lahore, Dr Basit joined BZU Multan as Lecturer and received MS-leading PhD scholarship by Higher Education Commission of Pakistan (2011–16) for his PhD from NEL-HYU, South Korea. In addition to post-doctoral research at HYU, he won intellectual capability awards from various agencies such as PCK (2012), DAAD-Germany (2017) etc. He holds reputable record for scientific publications/keynotes/book chapters as well as research in arts (Urdu Poetry/Iqbal).

References

Kahn R. E., Ma W. and Richt J. A., in Influenza Pathogenesis and Control - Volume I, ed. R. W. Compans and M. B. A. Oldstone, Springer International Publishing, Cham, 2014, pp. 205–218 [Google Scholar]
Qasim M. Lim D.-J. Park H. Na D. J. Nanosci. Nanotechnol. 2014;14:7374–7387. doi: 10.1166/jnn.2014.9578. [DOI] [PubMed] [Google Scholar]
Wejse C. Patsche C. B. Kühle A. Bamba F. J. V. Mendes M. S. Lemvik G. Gomes V. F. Rudolf F. Int. J. Infect. Dis. 2015;32:128–134. doi: 10.1016/j.ijid.2014.12.015. [DOI] [PubMed] [Google Scholar]
Braden C. R. Dowell S. F. Jernigan D. B. Hughes J. M. Emerging Infect. Dis. 2013;19:864–869. doi: 10.3201/eid1906.130192. [DOI] [PMC free article] [PubMed] [Google Scholar]
Breitbart M. Rohwer F. Trends Microbiol. 2005;13:278–284. doi: 10.1016/j.tim.2005.04.003. [DOI] [PubMed] [Google Scholar]
Chen L. Liang J. Mater. Sci. Eng. C. 2020;112:110924. doi: 10.1016/j.msec.2020.110924. [DOI] [PMC free article] [PubMed] [Google Scholar]
Rivera A. Messaoudi I. ACS Infectious Diseases. 2015;1:186–197. doi: 10.1021/id5000426. [DOI] [PMC free article] [PubMed] [Google Scholar]
Schweitzer C. J. Liang T. J. ACS Infectious Diseases. 2016;1:416–419. doi: 10.1021/acsinfecdis.5b00060. [DOI] [PMC free article] [PubMed] [Google Scholar]
Aderibigbe B. A. Molecules. 2017;22:1370. [Google Scholar]
Galdiero S. Falanga A. Vitiello M. Cantisani M. Marra V. Galdiero M. Molecules. 2011;16:8894–8918. doi: 10.3390/molecules16108894. [DOI] [PMC free article] [PubMed] [Google Scholar]
Coen D. M. Whitley R. J. Curr. Opin. Virol. 2011;1:545–547. doi: 10.1016/j.coviro.2011.10.024. [DOI] [PMC free article] [PubMed] [Google Scholar]
Corsi F. Sorrentino L. Mazzucchelli S. Truffi M. Capetti A. Rizzardini G. Fiandra L. J. Pharm. Pharmacol. 2016;4:328–339. [Google Scholar]
Lembo D. Donalisio M. Civra A. Argenziano M. Cavalli R. Expert Opin. Drug Delivery. 2018;15:93–114. doi: 10.1080/17425247.2017.1360863. [DOI] [PubMed] [Google Scholar]
Calderón L. Harris R. Cordoba-Diaz M. Elorza M. Elorza B. Lenoir J. Adriaens E. Remon J. P. Heras A. Cordoba-Diaz D. Eur. J. Pharm. Sci. 2013;48:216–222. doi: 10.1016/j.ejps.2012.11.002. [DOI] [PubMed] [Google Scholar]
Huy T. Q. Hien Thanh N. T. Thuy N. T. Van Chung P. Hung P. N. Le A. T. Hong Hanh N. T. J. Virol. Methods. 2017;241:52–57. doi: 10.1016/j.jviromet.2016.12.015. [DOI] [PubMed] [Google Scholar]
Morris D. Ansar M. Speshock J. Ivanciuc T. Qu Y. Casola A. Garofalo R. Viruses. 2019;11:732. doi: 10.3390/v11080732. [DOI] [PMC free article] [PubMed] [Google Scholar]
Li Y. Lin Z. Xu T. Wang C. Zhao M. Xiao M. Wang H. Deng N. Zhu B. RSC Adv. 2017;7:1453–1463. [Google Scholar]
Huy T. Q. Hien Thanh N. T. Thuy N. T. Van Chung P. Hung P. N. Le A. T. Hong Hanh N. T. J. Virol. Methods. 2017;241:52–57. doi: 10.1016/j.jviromet.2016.12.015. [DOI] [PubMed] [Google Scholar]
Szymańska E. Orłowski P. Winnicka K. Tomaszewska E. Bąska P. Celichowski G. Grobełny J. Basa A. Krzyżowska M. Int. J. Mol. Sci. 2018;19:387. doi: 10.3390/ijms19020387. [DOI] [PMC free article] [PubMed] [Google Scholar]
El-Sheekh M. M. Shabaan M. T. Hassan L. Morsi H. H. Int. J. Environ. Health Res. 2020:1–12. doi: 10.1080/09603123.2020.1789946. [DOI] [PubMed] [Google Scholar]
Haggag E. G. Elshamy A. M. Rabeh M. A. Gabr N. M. Salem M. Youssif K. A. Samir A. Bin Muhsinah A. Alsayari A. Abdelmohsen U. R. Int. J. Nanomed. 2019;14:6217–6229. doi: 10.2147/IJN.S214171. [DOI] [PMC free article] [PubMed] [Google Scholar]
Sreekanth T. V. M. Nagajyothi P. C. Muthuraman P. Enkhtaivan G. Vattikuti S. V. P. Tettey C. O. Kim D. H. Shim J. Yoo K. J. Photochem. Photobiol., B. 2018;188:6–11. doi: 10.1016/j.jphotobiol.2018.08.013. [DOI] [PubMed] [Google Scholar]
xi Xiang D. Chen Q. Pang L. long Zheng C. J. Virol. Methods. 2011;178:137–142. doi: 10.1016/j.jviromet.2011.09.003. [DOI] [PubMed] [Google Scholar]
Xiang D. Zheng Y. Duan W. Li X. Yin J. Shigdar S. O'Connor M. L. Marappan M. Zhao X. Miao Y. Xiang B. Zheng C. Int. J. Nanomed. 2013;8:4103–4114. doi: 10.2147/IJN.S53622. [DOI] [PMC free article] [PubMed] [Google Scholar]
Gerhardson B. Trends Biotechnol. 2002;20:338–343. doi: 10.1016/s0167-7799(02)02021-8. [DOI] [PubMed] [Google Scholar]
Hamed Derbalah A. S. Elsharkawy M. M. J. Biotechnol. 2019;306:134–141. doi: 10.1016/j.jbiotec.2019.10.003. [DOI] [PubMed] [Google Scholar]
Huo C. Xiao J. Xiao K. Zou S. Wang M. Qi P. Liu T. Hu Y. Int. J. Nanomed. 2020;15:661–674. doi: 10.2147/IJN.S221667. [DOI] [PMC free article] [PubMed] [Google Scholar]
Makau J. N. Watanabe K. Mohammed M. M. D. Nishida N. J. Med. Food. 2018;21:777–784. doi: 10.1089/jmf.2017.4121. [DOI] [PubMed] [Google Scholar]
Siddiqi K. S. ur Rahman A. Tajuddin Husen A. Nanoscale Res. Lett. 2018;13(1):1–13. doi: 10.1186/s11671-018-2532-3. [DOI] [PMC free article] [PubMed] [Google Scholar]
Ghaffari H. Tavakoli A. Moradi A. Tabarraei A. Bokharaei-Salim F. Zahmatkeshan M. Farahmand M. Javanmard D. Kiani S. J. Esghaei M. Pirhajati-Mahabadi V. Ataei-Pirkooh A. Monavari S. H. J. Biomed. Sci. 2019;26:1–10. doi: 10.1186/s12929-019-0563-4. [DOI] [PMC free article] [PubMed] [Google Scholar]
BAILISS K. W. Senananyake S. Plant Pathol. 1984;33:185–192. [Google Scholar]
Hsueh Y. H. Lin K. S. Ke W. J. Te Hsieh C. Chiang C. L. Tzou D. Y. Liu S. T. PLoS One. 2015;10:e0144306. doi: 10.1371/journal.pone.0144306. [DOI] [PMC free article] [PubMed] [Google Scholar]
Adán C. Marugán J. Sánchez E. Pablos C. Van Grieken R. Electrochim. Acta. 2016;191:521–529. [Google Scholar]
Di Piero R. M. de Novaes Q. S. Pascholati S. F. Braz. Arch. Biol. Technol. 2010;53:269–278. [Google Scholar]
Elsharkawy M. M. Derbalah A. Pest Manage. Sci. 2019;75:828–834. doi: 10.1002/ps.5185. [DOI] [PubMed] [Google Scholar]
Gomaa H. Khalifa H. Selim M. M. Shenashen M. A. Kawada S. Alamoudi A. S. Azzam A. M. Alhamid A. A. El-Safty S. A. ACS Sustainable Chem. Eng. 2017;5:10826–10839. [Google Scholar]
Jia C. Yang P. Chen H. S. Wang J. CrystEngComm. 2015;17:2940–2948. [Google Scholar]
Nakano R. Ishiguro H. Yao Y. Kajioka J. Fujishima A. Sunada K. Minoshima M. Hashimoto K. Kubota Y. Photochem. Photobiol. Sci. 2012;11:1293–1298. doi: 10.1039/c2pp05414k. [DOI] [PubMed] [Google Scholar]
Chen Y. N. Hsueh Y. H. Te Hsieh C. Tzou D. Y. Chang P. L. Int. J. Environ. Res. Public Health. 2016;13:4–6. doi: 10.3390/ijerph13040430. [DOI] [PMC free article] [PubMed] [Google Scholar]
Halder A. Das S. Ojha D. Chattopadhyay D. Mukherjee A. Mater. Sci. Eng. C. 2018;89:413–421. doi: 10.1016/j.msec.2018.04.005. [DOI] [PubMed] [Google Scholar]
Di Gianvincenzo P. Marradi M. Martínez-Ávila O. M. Bedoya L. M. Alcamí J. Penadés S. Bioorg. Med. Chem. Lett. 2010;20:2718–2721. doi: 10.1016/j.bmcl.2010.03.079. [DOI] [PubMed] [Google Scholar]
Papp I. Sieben C. Ludwig K. Roskamp M. Böttcher C. Schlecht S. Herrmann A. Haag R. Small. 2010;6:2900–2906. doi: 10.1002/smll.201001349. [DOI] [PubMed] [Google Scholar]
Paul A. M. Shi Y. Acharya D. Douglas J. R. Cooley A. Anderson J. F. Huang F. Bai F. J. Gen. Virol. 2014;95:1712–1722. doi: 10.1099/vir.0.066084-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
Li Y. Lin Z. Guo M. Xia Y. Zhao M. Wang C. Xu T. Chen T. Zhu B. Int. J. Nanomed. 2017;12:5733–5743. doi: 10.2147/IJN.S140939. [DOI] [PMC free article] [PubMed] [Google Scholar]
Lin Z. Li Y. Gong G. Xia Y. Wang C. Chen Y. Hua L. Zhong J. Tang Y. Liu X. Zhu B. Int. J. Nanomed. 2018;13:5787–5797. doi: 10.2147/IJN.S177658. [DOI] [PMC free article] [PubMed] [Google Scholar]
Li Y. Xu T. Lin Z. Wang C. Xia Y. Guo M. Zhao M. Chen Y. Zhu B. ACS Omega. 2019;4:6720–6725. [Google Scholar]
Li Y. Lin Z. Guo M. Zhao M. Xia Y. Wang C. Xu T. Zhu B. Int. J. Nanomed. 2018;13:2005–2016. doi: 10.2147/IJN.S155994. [DOI] [PMC free article] [PubMed] [Google Scholar]
EA A. EB P. Int. J. Med. Inform. 2019;125:30–36. doi: 10.1016/j.ijmedinf.2019.02.005. [DOI] [PubMed] [Google Scholar]
Cheng Z. Zhi X. Sun G. Guo W. Huang Y. Sun W. Tian X. Zhao F. Hu K. J. Med. Virol. 2016;88:653–663. doi: 10.1002/jmv.24366. [DOI] [PMC free article] [PubMed] [Google Scholar]
Zhong J. Xia Y. Hua L. Liu X. Xiao M. Xu T. Zhu B. Cao H. Artif. Cells, Nanomed., Biotechnol. 2019;47:3485–3491. doi: 10.1080/21691401.2019.1640716. [DOI] [PubMed] [Google Scholar]
Du T. Liang J. Dong N. Lu J. Fu Y. Fang L. Xiao S. Han H. ACS Appl. Mater. Interfaces. 2018;10:4369–4378. doi: 10.1021/acsami.7b13811. [DOI] [PubMed] [Google Scholar]
Sujitha V. Murugan K. Paulpandi M. Panneerselvam C. Suresh U. Roni M. Nicoletti M. Higuchi A. Madhiyazhagan P. Subramaniam J. Dinesh D. Vadivalagan C. Chandramohan B. Alarfaj A. A. Munusamy M. A. Barnard D. R. Benelli G. Parasitol. Res. 2015;114:3315–3325. doi: 10.1007/s00436-015-4556-2. [DOI] [PubMed] [Google Scholar]
Jampílek J. and Král’ová K., in Nanotheranostics: Applications and Limitations, Nature Publishing Group, 2019, pp. 137–178 [Google Scholar]
Baram-Pinto D. Shukla S. Gedanken A. Sarid R. Small. 2010;6:1044–1050. doi: 10.1002/smll.200902384. [DOI] [PubMed] [Google Scholar]
Fahmi M. Z. Sukmayani W. Khairunisa S. Q. Witaningrum A. M. Indriati D. W. Matondang M. Q. Y. Chang J. Y. Kotaki T. Kameoka M. RSC Adv. 2016;6:92996–93002. [Google Scholar]
Łoczechin A. Séron K. Barras A. Giovanelli E. Belouzard S. Chen Y. T. Metzler-Nolte N. Boukherroub R. Dubuisson J. Szunerits S. ACS Appl. Mater. Interfaces. 2019;11:42964–42974. doi: 10.1021/acsami.9b15032. [DOI] [PMC free article] [PubMed] [Google Scholar]
Fujimori Y. Sato T. Hayata T. Nagao T. Nakayam M. Nakayam T. Sugamat R. Suzuki K. Appl. Environ. Microbiol. 2012;78:951–955. doi: 10.1128/AEM.06284-11. [DOI] [PMC free article] [PubMed] [Google Scholar]
Shionoiri N. Sato T. Fujimori Y. Nakayama T. Nemoto M. Matsunaga T. Tanaka T. J. Biosci. Bioeng. 2012;113:580–586. doi: 10.1016/j.jbiosc.2011.12.006. [DOI] [PubMed] [Google Scholar]
Das Jana I. Kumbhakar P. Banerjee S. Gowda C. C. Kedia N. Kuila S. K. Banerjee S. Das N. C. Das A. K. Manna I. Tiwary C. S. Mondal A. ACS Appl. Nano Mater. 2021;4:352–362. [Google Scholar]
Tavakoli A. Hashemzadeh M. S. J. Virol. Methods. 2020;275:113688. doi: 10.1016/j.jviromet.2019.113688. [DOI] [PubMed] [Google Scholar]
Hang X. Peng H. Song H. Qi Z. Miao X. Xu W. J. Virol. Methods. 2015;222:150–157. doi: 10.1016/j.jviromet.2015.06.010. [DOI] [PubMed] [Google Scholar]
Tang L. Jiang Y. Zhu M. Chen L. Zhou X. Zhou C. Ye P. Chen X. Wang B. Xu Z. Zhang Q. Xu X. Gao H. Wu X. Li D. Jiang W. Qu J. Xiang C. Li L. Front. Med. 2020;14:664–673. doi: 10.1007/s11684-020-0810-9. [DOI] [PMC free article] [PubMed] [Google Scholar]
Kumar R. Nayak M. Sahoo G. C. Pandey K. Sarkar M. C. Ansari Y. Das V. N. R. Topno R. K. Bhawna Madhukar M. Das P. J. Infect. Chemother. 2019;25:325–329. doi: 10.1016/j.jiac.2018.12.006. [DOI] [PubMed] [Google Scholar]
Lin Z. Li Y. Xu T. Guo M. Wang C. Zhao M. Chen H. Kuang J. Li W. Zhang Y. Lin T. Chen Y. Chen H. Zhu B. ACS Omega. 2020;5:12495–12500. doi: 10.1021/acsomega.0c01382. [DOI] [PMC free article] [PubMed] [Google Scholar]
Balagna C. Perero S. Percivalle E. Nepita E. V. Ferraris M. Open Ceram. 2020;1:100006. [Google Scholar]
Du T. Lu J. Liu L. Dong N. Fang L. Xiao S. Han H. ACS Appl. Bio Mater. 2018;1:1286–1293. doi: 10.1021/acsabm.8b00154. [DOI] [PubMed] [Google Scholar]
Mazurkova N. A. Spitsyna Y. E. Shikina N. V. Ismagilov Z. R. Zagrebel’nyi S. N. Ryabchikova E. I. Nanotechnol. Russ. 2010;5:417–420. [Google Scholar]
Pfaff F. Glück B. Hoyer T. Rohländer D. Sauerbrei A. Zell R. Lett. Appl. Microbiol. 2019;69:302–309. doi: 10.1111/lam.13208. [DOI] [PubMed] [Google Scholar]
Mahmood S. Kiong K. C. Tham C. S. Chien T. C. Hilles A. R. Venugopal J. R. AAPS PharmSciTech. 2020;21:1–15. doi: 10.1208/s12249-020-01810-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
Ilk S. Saglam N. Özgen M. Artif. Cells, Nanomed., Biotechnol. 2017;45:907–916. doi: 10.1080/21691401.2016.1192040. [DOI] [PubMed] [Google Scholar]
Raut S. Bhadoriya S. S. Uplanchiwar V. Mishra V. Gahane A. Jain S. K. Acta Pharm. Sin. B. 2012;2:8–15. [Google Scholar]
Tan Q. Liu W. Guo C. Zhai G. Int. J. Nanomed. 2011;6:1621. doi: 10.2147/IJN.S22411. [DOI] [PMC free article] [PubMed] [Google Scholar]
Verhoef J. J. F. Anchordoquy T. J. Drug Delivery Transl. Res. 2013;3:499–503. doi: 10.1007/s13346-013-0176-5. [DOI] [PMC free article] [PubMed] [Google Scholar]
Mahmood S. Kiong K. C. Tham C. S. Chien T. C. Hilles A. R. Venugopal J. R. AAPS PharmSciTech. 2020;21(7):1–15. doi: 10.1208/s12249-020-01810-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
Saifi Z. Rizwanullah M. Mir S. R. Amin S. J. Drug Delivery Sci. Technol. 2020;57:101634. [Google Scholar]
Fangueiro J. F. Andreani T. Fernandes L. Garcia M. L. Egea M. A. Silva A. M. Souto E. B. Colloids Surf., B. 2014;123:452–460. doi: 10.1016/j.colsurfb.2014.09.042. [DOI] [PubMed] [Google Scholar]
Cholkar K. Patel S. P. Vadlapudi A. D. Mitra A. K. J. Ocul. Pharmacol. Ther. 2013;29:106–123. doi: 10.1089/jop.2012.0200. [DOI] [PMC free article] [PubMed] [Google Scholar]
Warsi M. H. Anwar M. Garg V. Jain G. K. Talegaonkar S. Ahmad F. J. Khar R. K. Colloids Surf., B. 2014;122:423–431. doi: 10.1016/j.colsurfb.2014.07.004. [DOI] [PubMed] [Google Scholar]
Bhosale U. V. Kusum Devi V. Jain N. J. Young Pharm. 2011;3:275–283. doi: 10.4103/0975-1483.90236. [DOI] [PMC free article] [PubMed] [Google Scholar]
Suwannoi P. Chomnawang M. Tunsirikongkon A. Phongphisutthinan A. Müller-Goymann C. C. Sarisuta N. J. Drug Delivery Sci. Technol. 2019;52:624–631. [Google Scholar]
Alkholief M. Albasit H. Alhowyan A. Alshehri S. Raish M. Abul Kalam M. Alshamsan A. Saudi Pharm. J. 2019;27:293–302. doi: 10.1016/j.jsps.2018.11.011. [DOI] [PMC free article] [PubMed] [Google Scholar]
Vedula V. B. Chopra M. Joseph E. Mazumder S. Appl. Nanosci. 2016;6:197–208. [Google Scholar]
Belgamwar A. Khan S. Yeole P. Artif. Cells, Nanomed., Biotechnol. 2018;46:374–386. doi: 10.1080/21691401.2017.1313266. [DOI] [PubMed] [Google Scholar]
Hari B. N. V. Narayanan N. Dhevendaran K. Ramyadevi D. Mater. Sci. Eng. C. 2016;67:522–532. doi: 10.1016/j.msec.2016.05.064. [DOI] [PubMed] [Google Scholar]
Kumar P. Lakshmi Y. S. Kondapi A. K. HIV Med. 2017;18:452–462. doi: 10.1111/hiv.12475. [DOI] [PubMed] [Google Scholar]
Joshy K. S. George A. Snigdha S. Joseph B. Kalarikkal N. Pothen L. A. Thomas S. Mater. Sci. Eng. C. 2018;93:864–872. doi: 10.1016/j.msec.2018.08.015. [DOI] [PubMed] [Google Scholar]
Joshy K. S. Snigdha S. Anne G. Nandakumar K. Laly A. P. Sabu T. Chem. Phys. Lipids. 2018;210:82–89. doi: 10.1016/j.chemphyslip.2017.11.003. [DOI] [PubMed] [Google Scholar]
Joshy K. S. Susan M. A. Snigdha S. Nandakumar K. Laly A. P. Sabu T. Int. J. Biol. Macromol. 2018;107:929–937. doi: 10.1016/j.ijbiomac.2017.09.078. [DOI] [PubMed] [Google Scholar]
Joshy K. S. Snigdha S. Kalarikkal N. Pothen L. A. Thomas S. Chem. Phys. Lipids. 2017;207:24–37. doi: 10.1016/j.chemphyslip.2017.07.002. [DOI] [PubMed] [Google Scholar]
Joshy K. S. Snigdha S. George A. Kalarikkal N. Pothen L. A. Thomas S. Cellulose. 2017;24:4759–4771. [Google Scholar]
Carvalho A. L. M. da Silva J. A. Lira A. A. M. Conceição T. M. F. Nunes R. de S. de Albuquerque Junior R. L. C. Sarmento V. H. V. Leal L. B. de Santana D. P. J. Pharm. Sci. 2016;105:2188–2193. doi: 10.1016/j.xphs.2016.04.013. [DOI] [PubMed] [Google Scholar]
Joshy K. S. Sharma C. P. Kalarikkal N. Sandeep K. Thomas S. Pothen L. A. Mater. Sci. Eng. C. 2016;66:40–50. doi: 10.1016/j.msec.2016.03.031. [DOI] [PubMed] [Google Scholar]
Laux A. Gouws C. Hamman J. H. Expert Opin. Drug Delivery. 2019;16:1283–1285. doi: 10.1080/17425247.2019.1675633. [DOI] [PubMed] [Google Scholar]
Gomez-Orellana I. Expert Opin. Drug Delivery. 2005;2:419–433. doi: 10.1517/17425247.2.3.419. [DOI] [PubMed] [Google Scholar]
Pather S. I. Rathbone M. J. Senel S. Expert Opin. Drug Delivery. 2008;5:531–542. doi: 10.1517/17425247.5.5.531. [DOI] [PubMed] [Google Scholar]
Prausnitz M. R. Langer R. Nat. Biotechnol. 2008;26:1261–1268. doi: 10.1038/nbt.1504. [DOI] [PMC free article] [PubMed] [Google Scholar]
Ernest T. B. Elder D. P. Martini L. G. Roberts M. Ford J. L. J. Pharm. Pharmacol. 2010;59:1043–1055. doi: 10.1211/jpp.59.8.0001. [DOI] [PubMed] [Google Scholar]
Cram A. Breitkreutz J. Desset-Brèthes S. Nunn T. Tuleu C. Int. J. Pharm. 2009;365:1–3. doi: 10.1016/j.ijpharm.2008.09.015. [DOI] [PubMed] [Google Scholar]
P. N.-W. D. Information and U. 2012, WHO Drug Information International Regulatory Harmonization
Pham K. Li D. Guo S. Penzak S. Dong X. J. Controlled Release. 2016;226:88–97. doi: 10.1016/j.jconrel.2016.02.001. [DOI] [PubMed] [Google Scholar]
Ravi P. R. Vats R. J. Pharm. Pharmacol. 2017;69:823–833. doi: 10.1111/jphp.12716. [DOI] [PubMed] [Google Scholar]
Negi J. S. Chattopadhyay P. Sharma A. K. Ram V. Eur. J. Pharm. Sci. 2013;48:231–239. doi: 10.1016/j.ejps.2012.10.022. [DOI] [PubMed] [Google Scholar]
Ravi P. R. Vats R. Balija J. Adapa S. P. N. Aditya N. Carbohydr. Polym. 2014;110:320–328. doi: 10.1016/j.carbpol.2014.03.099. [DOI] [PubMed] [Google Scholar]
Dodiya S. S. Chavhan S. S. Sawant K. K. Korde A. G. J. Microencapsulation. 2011;28:515–527. doi: 10.3109/02652048.2011.590612. [DOI] [PubMed] [Google Scholar]
Krieser K. Emanuelli J. Daudt R. M. Bilatto S. Willig J. B. Guterres S. S. Pohlmann A. R. Buffon A. Correa D. S. Külkamp-Guerreiro I. C. Mater. Sci. Eng. C. 2020;117:111315. doi: 10.1016/j.msec.2020.111315. [DOI] [PubMed] [Google Scholar]
He Y. Xia D. N. Li Q. X. Tao J. S. Gan Y. Wang C. Acta Pharmacol. Sin. 2015;36:1151–1160. doi: 10.1038/aps.2015.53. [DOI] [PMC free article] [PubMed] [Google Scholar]
Kurd M. Malvajerd S. S. Rezaee S. Hamidi M. Derakhshandeh K. Artif. Cells, Nanomed., Biotechnol. 2019;47:2123–2133. doi: 10.1080/21691401.2019.1616553. [DOI] [PubMed] [Google Scholar]
Bianchin M. D. Prebianca G. Immich M. F. Teixeira M. L. Colombo M. Koester L. S. de Araújo B. V. Poletto F. Külkamp-Guerreiro I. C. Drug Dev. Ind. Pharm. 2021;47:83–91. doi: 10.1080/03639045.2020.1862167. [DOI] [PubMed] [Google Scholar]
Prabhakar K. Afzal S. M. Surender G. Kishan V. Acta Pharm. Sin. B. 2013;3:345–353. [Google Scholar]
Pompei R. Flore O. Marccialis M. A. Pani A. Loddo B. Nature. 1979;281:689–690. doi: 10.1038/281689a0. [DOI] [PubMed] [Google Scholar]
Cinatl J. Morgenstern B. Bauer G. Chandra P. Rabenau H. Doerr H. W. Lancet. 2003;361:2045–2046. doi: 10.1016/S0140-6736(03)13615-X. [DOI] [PMC free article] [PubMed] [Google Scholar]
Chew J. L. Wolfowicz C. B. Mao H. Q. Leong K. W. Chua K. Y. Vaccine. 2003;21:2720–2729. doi: 10.1016/s0264-410x(03)00228-7. [DOI] [PubMed] [Google Scholar]
Wu Y. Yang W. Wang C. Hu J. Fu S. Int. J. Pharm. 2005;295:235–245. doi: 10.1016/j.ijpharm.2005.01.042. [DOI] [PubMed] [Google Scholar]
Depan D. Girase B. Shah J. S. Misra R. D. K. Acta Biomater. 2011;7:3432–3445. doi: 10.1016/j.actbio.2011.05.019. [DOI] [PubMed] [Google Scholar]
Depan D. Venkata Surya P. K. C. Girase B. Misra R. D. K. Acta Biomater. 2011;7:2163–2175. doi: 10.1016/j.actbio.2011.01.029. [DOI] [PubMed] [Google Scholar]
Yuan Q. Hein S. Misra R. D. K. Acta Biomater. 2010;6:2732–2739. doi: 10.1016/j.actbio.2010.01.025. [DOI] [PubMed] [Google Scholar]
Mishra D. Jain N. Rajoriya V. Jain A. K. J. Pharm. Pharmacol. 2014;66:1082–1093. doi: 10.1111/jphp.12235. [DOI] [PubMed] [Google Scholar]
Cavalcanti S. M. T. Nunes C. Lima S. A. C. Soares-Sobrinho J. L. Reis S. Pharm. Res. 2017;34:1204–1216. doi: 10.1007/s11095-017-2136-0. [DOI] [PubMed] [Google Scholar]
Woodsong C. Holt J. D. S. Adv. Drug Delivery Rev. 2015;92:146–154. doi: 10.1016/j.addr.2015.02.004. [DOI] [PubMed] [Google Scholar]
Machado A. Cunha-Reis C. Araújo F. Nunes R. Seabra V. Ferreira D. das Neves J. Sarmento B. Acta Biomater. 2016;44:332–340. doi: 10.1016/j.actbio.2016.08.018. [DOI] [PubMed] [Google Scholar]
Timur S. S. Şahin A. Aytekin E. Öztürk N. Polat K. H. Tezel N. Gürsoy R. N. Çalış S. Pharm. Dev. Technol. 2018;23:301–310. doi: 10.1080/10837450.2017.1329835. [DOI] [PubMed] [Google Scholar]
Meng J. Zhang T. Agrahari V. Ezoulin M. J. Youan B. B. C. Nanomedicine. 2014;9:1595–1612. doi: 10.2217/nnm.13.136. [DOI] [PMC free article] [PubMed] [Google Scholar]
Meng J. Agrahari V. Ezoulin M. J. Zhang C. Purohit S. S. Molteni A. Dim D. Oyler N. A. Youan B. B. C. Mol. Pharm. 2016;13:4129–4140. doi: 10.1021/acs.molpharmaceut.6b00739. [DOI] [PubMed] [Google Scholar]
Parthiban R. Shanmugapriya Indhu Sathishkumar Surendhar Prakash R. Drug Invent. Today. 2020;14:108–111. [Google Scholar]
Mahboobian M. M. Mohammadi M. Mansouri Z. J. Drug Delivery Sci. Technol. 2020;55:101400. [Google Scholar]
Gandhi A. Jana S. Sen K. K. Int. J. Biol. Macromol. 2014;67:478–482. doi: 10.1016/j.ijbiomac.2014.04.019. [DOI] [PubMed] [Google Scholar]
Calderón L. Harris R. Cordoba-Diaz M. Elorza M. Elorza B. Lenoir J. Adriaens E. Remon J. P. Heras A. Cordoba-Diaz D. Eur. J. Pharm. Sci. 2013;48:216–222. doi: 10.1016/j.ejps.2012.11.002. [DOI] [PubMed] [Google Scholar]
Rajendran N. Natrajan R. Kumar R. Selvaraj S. Asian J. Pharm. 2010;4:220–226. [Google Scholar]
Peira E. Chirio D. Carlotti M. E. Spagnolo R. Trotta M. J. Drug Delivery Sci. Technol. 2009;19:191–196. [Google Scholar]
Cavalli R. Donalisio M. Civra A. Ferruti P. Ranucci E. Trotta F. Lembo D. J. Controlled Release. 2009;137:116–122. doi: 10.1016/j.jconrel.2009.04.004. [DOI] [PubMed] [Google Scholar]
Alsarra I. A. Hamed A. Y. Alanazi F. K. Drug Delivery. 2008;15:313–321. doi: 10.1080/10717540802035251. [DOI] [PubMed] [Google Scholar]
Suwannoi P. Chomnawang M. Sarisuta N. Reichl S. Müller-Goymann C. C. J. Ocul. Pharmacol. Ther. 2017;33:743–752. doi: 10.1089/jop.2017.0057. [DOI] [PubMed] [Google Scholar]
Xing-Guo Z. Jing M. Min-Wei L. Sai-Ping J. Fu-Qiang H. Yong-Zhong D. J. Zhejiang Univ., Sci., B. 2008;9:506–510. doi: 10.1631/jzus.B0820047. [DOI] [PMC free article] [PubMed] [Google Scholar]
Singh G. Pai R. S. Drug Delivery. 2016;23:532–539. doi: 10.3109/10717544.2014.930760. [DOI] [PubMed] [Google Scholar]
Duan J. Freeling J. P. Koehn J. Shu C. Ho R. J. Y. J. Pharm. Sci. 2014;103:2520–2529. doi: 10.1002/jps.24046. [DOI] [PMC free article] [PubMed] [Google Scholar]
Nowacek A. S. McMillan J. Miller R. Anderson A. Rabinow B. Gendelman H. E. J Neuroimmune Pharmacol. 2010;5:592–601. doi: 10.1007/s11481-010-9198-7. [DOI] [PMC free article] [PubMed] [Google Scholar]
Garg M. Jain N. K. J. Drug Targeting. 2006;14:1–11. doi: 10.1080/10611860500525370. [DOI] [PubMed] [Google Scholar]
Elkateb H. Tatham L. M. Cauldbeck H. Niezabitowska E. Owen A. Rannard S. McDonald T. Int. J. Pharm. 2020;588:119794. doi: 10.1016/j.ijpharm.2020.119794. [DOI] [PubMed] [Google Scholar]
Priya Dharshini K. Fang H. Ramya Devi D. Yang J. X. Luo R. H. Zheng Y. T. Brzeziński M. Vedha Hari B. N. Carbohydr. Polym. 2021;256:117440. doi: 10.1016/j.carbpol.2020.117440. [DOI] [PubMed] [Google Scholar]
Belgamwar A. V. Khan S. A. Yeole P. G. J. Drug Delivery Sci. Technol. 2019;52:1008–1020. [Google Scholar]
Rozana R. Yulizar Y. Saefumillah A. Apriandanu D. O. B. AIP Conf. Proc. 2020;2242:040004. [Google Scholar]
Makwana V. Jain R. Patel K. Nivsarkar M. Joshi A. Int. J. Pharm. 2015;495:439–446. doi: 10.1016/j.ijpharm.2015.09.014. [DOI] [PubMed] [Google Scholar]
Gaur P. K. Mishra S. Bajpai M. Mishra A. BioMed Res. Int. 2014;2014:363404. doi: 10.1155/2014/363404. [DOI] [PMC free article] [PubMed] [Google Scholar]
Tshweu L. Katata L. Kalombo L. Chiappetta D. A. Hocht C. Sosnik A. Swai H. Nanomedicine. 2014;9:1821–1833. doi: 10.2217/nnm.13.167. [DOI] [PubMed] [Google Scholar]
Kotta S. Khan A. W. Ansari S. H. Sharma R. K. Ali J. Int. J. Pharm. 2014;462:129–134. doi: 10.1016/j.ijpharm.2013.12.038. [DOI] [PubMed] [Google Scholar]
Shibata A. McMullen E. Pham A. Belshan M. Sanford B. Zhou Y. Goede M. Date A. A. Destache C. J. AIDS Res. Hum. Retroviruses. 2013;29:746–754. doi: 10.1089/aid.2012.0301. [DOI] [PMC free article] [PubMed] [Google Scholar]
de Sousa M. Pessine F. B. T. Adv. Sci., Eng. Med. 2014;6:1135–1142. [Google Scholar]
Gong Y. Zhi K. Nagesh P. K. B. Sinha N. Chowdhury P. Chen H. Gorantla S. Yallapu M. M. Kumar S. Viruses. 2020;12:564. doi: 10.3390/v12050564. [DOI] [PMC free article] [PubMed] [Google Scholar]
Gong Y. Chowdhury P. Midde N. M. Rahman M. A. Yallapu M. M. Kumar S. Biochem. Biophys. Rep. 2017;12:214–219. doi: 10.1016/j.bbrep.2017.10.005. [DOI] [PMC free article] [PubMed] [Google Scholar]
Figueira T. N. Domingues M. M. Illien F. Cadima-Couto I. Todorovski T. Andreu D. Sagan S. Castanho M. A. R. B. Walrant A. Veiga A. S. ACS Infectious Diseases. 2020;6:224–236. doi: 10.1021/acsinfecdis.9b00285. [DOI] [PubMed] [Google Scholar]
Russo E. Gaglianone N. Baldassari S. Parodi B. Cafaggi S. Zibana C. Donalisio M. Cagno V. Lembo D. Caviglioli G. Colloids Surf., B. 2014;118:117–125. doi: 10.1016/j.colsurfb.2014.03.037. [DOI] [PubMed] [Google Scholar]
Tyo K. M. Lasnik A. B. Zhang L. Mahmoud M. Jenson A. B. Fuqua J. L. Palmer K. E. Steinbach-Rankins J. M. J. Controlled Release. 2020;321:84–99. doi: 10.1016/j.jconrel.2020.02.006. [DOI] [PMC free article] [PubMed] [Google Scholar]
Karami Z. Saghatchi Zanjani M. R. Rezaee S. Rostamizadeh K. Hamidi M. Drug Dev. Ind. Pharm. 2019;45:736–744. doi: 10.1080/03639045.2019.1569039. [DOI] [PubMed] [Google Scholar]
Surnar B. Kamran M. Z. Shah A. S. Basu U. Kolishetti N. Deo S. Jayaweera D. T. Daunert S. Dhar S. ACS Nano. 2019;13:11034–11048. doi: 10.1021/acsnano.9b02807. [DOI] [PMC free article] [PubMed] [Google Scholar]
Joshi G. Kumar A. Sawant K. Drug Delivery. 2016;23:3492–3504. doi: 10.1080/10717544.2016.1199605. [DOI] [PubMed] [Google Scholar]
Ravi P. R. Vats R. Dalal V. Gadekar N. Aditya N. Drug Dev. Ind. Pharm. 2015;41:131–140. doi: 10.3109/03639045.2013.850710. [DOI] [PubMed] [Google Scholar]
Alex A. Paul W. Chacko A. J. Sharma C. P. Ther. Delivery. 2011;2:25–35. doi: 10.4155/tde.10.96. [DOI] [PubMed] [Google Scholar]
Perazzolo S. Shireman L. M. Koehn J. McConnachie L. A. Kraft J. C. Shen D. D. Ho R. J. Y. J. Pharm. Sci. 2018;107:3153–3162. doi: 10.1016/j.xphs.2018.07.032. [DOI] [PMC free article] [PubMed] [Google Scholar]
Fotooh Abadi L. Kumar P. Gajbhiye V. Paknikar K. M. Kulkarni S. Colloids Surf., B. 2020;194:111227. doi: 10.1016/j.colsurfb.2020.111227. [DOI] [PubMed] [Google Scholar]
Lahkar S. Das M. K. J. Nanopart. Res. 2020;22:109. [Google Scholar]
Varshosaz J. Taymouri S. Jafari E. Jahanian-Najafabadi A. Taheri A. J. Drug Delivery Sci. Technol. 2018;48:9–20. [Google Scholar]
Ramana L. N. Sethuraman S. Ranga U. Krishnan U. M. J. Biomed. Sci. 2010;17:1–9. doi: 10.1186/1423-0127-17-57. [DOI] [PMC free article] [PubMed] [Google Scholar]
Date A. A. Shibata A. Goede M. Sanford B. La Bruzzo K. Belshan M. Destache C. J. Antiviral Res. 2012;96:430–436. doi: 10.1016/j.antiviral.2012.09.015. [DOI] [PMC free article] [PubMed] [Google Scholar]
Javan F. Vatanara A. Azadmanesh K. Nabi-Meibodi M. shakouri M. J. Pharm. Pharmacol. 2017;69:1002–1009. doi: 10.1111/jphp.12737. [DOI] [PubMed] [Google Scholar]
Kumar S. Narayan R. Ahammed V. Nayak Y. Naha A. Nayak U. Y. J. Drug Delivery Sci. Technol. 2018;44:181–189. [Google Scholar]
Abou-El-Naga I. F. El Kerdany E. D. Mady R. F. Shalaby T. I. Zaytoun E. M. Parasitol. Int. 2017;66:735–747. doi: 10.1016/j.parint.2017.08.007. [DOI] [PubMed] [Google Scholar]
Jain S. Sharma J. M. Jain A. K. Mahajan R. R. Nanomedicine. 2013;8:1639–1655. doi: 10.2217/nnm.12.181. [DOI] [PubMed] [Google Scholar]
Bimbo L. M. Denisova O. V. Mäkilä E. Kaasalainen M. De Brabander J. K. Hirvonen J. Salonen J. Kakkola L. Kainov D. Santos H. A. ACS Nano. 2013;7:6884–6893. doi: 10.1021/nn402062f. [DOI] [PubMed] [Google Scholar]
Ramana L. N. Sharma S. Sethuraman S. Ranga U. Krishnan U. M. Biochim. Biophys. Acta, Gen. Subj. 2014;1840:476–484. doi: 10.1016/j.bbagen.2013.10.002. [DOI] [PubMed] [Google Scholar]
Kuo Y. C. Ko H. F. Biomaterials. 2013;34:4818–4830. doi: 10.1016/j.biomaterials.2013.03.013. [DOI] [PubMed] [Google Scholar]
Adlin Jino Nesalin J. Anton Smith A. J. Pharm. Res. 2013;6:268–274. [Google Scholar]
Shegokar R. Singh K. K. Pharmazie. 2011;66:264–271. [PubMed] [Google Scholar]
Garg M. Asthana A. Agashe H. B. Agrawal G. P. Jain N. K. J. Pharm. Pharmacol. 2010;58:605–616. doi: 10.1211/jpp.58.5.0005. [DOI] [PubMed] [Google Scholar]
Kuo Y. C. Chung C. Y. Colloids Surf., B. 2011;88:682–690. doi: 10.1016/j.colsurfb.2011.07.060. [DOI] [PubMed] [Google Scholar]
Chaowanachan T. Krogstad E. Ball C. Woodrow K. A. PLoS One. 2013;8:61416. doi: 10.1371/journal.pone.0061416. [DOI] [PMC free article] [PubMed] [Google Scholar]
Mandal S. Prathipati P. K. Kang G. Zhou Y. Yuan Z. Fan W. Li Q. Destache C. J. Aids. 2017;31:469–476. doi: 10.1097/QAD.0000000000001349. [DOI] [PMC free article] [PubMed] [Google Scholar]
Mandal S. Kang G. Prathipati P. K. Zhou Y. Fan W. Li Q. Destache C. J. J. Controlled Release. 2019;294:216–225. doi: 10.1016/j.jconrel.2018.12.027. [DOI] [PMC free article] [PubMed] [Google Scholar]
Shailender J. Ravi P. R. Reddy Sirukuri M. Dalvi A. Keerthi Priya O. Drug Dev. Ind. Pharm. 2018;44:1109–1119. doi: 10.1080/03639045.2018.1438459. [DOI] [PubMed] [Google Scholar]
Gourdon B. Chemin C. Moreau A. Arnauld T. Baumy P. Cisternino S. Péan J. M. Declèves X. Int. J. Pharm. 2017;529:357–370. doi: 10.1016/j.ijpharm.2017.07.024. [DOI] [PubMed] [Google Scholar]
Kumar R. Sinha V. R. AAPS PharmSciTech. 2017;18:884–894. doi: 10.1208/s12249-016-0575-2. [DOI] [PubMed] [Google Scholar]
Cavalcanti S. M. T. Nunes C. Costa Lima S. A. Soares-Sobrinho J. L. Reis S. Eur. J. Pharm. Sci. 2018;122:22–30. doi: 10.1016/j.ejps.2018.06.017. [DOI] [PubMed] [Google Scholar]
Yan J. K. Wang Y. Y. Qiu W. Y. Wu J. Y. Carbohydr. Polym. 2017;174:209–216. doi: 10.1016/j.carbpol.2017.06.082. [DOI] [PubMed] [Google Scholar]
Da Silva Barbi M. Carvalho F. C. Kiill C. P. Da Silva Barud H. Santagneli S. H. Ribeiro S. J. L. Gremião M. P. D. J. Nanosci. Nanotechnol. 2015;15:865–874. doi: 10.1166/jnn.2015.9180. [DOI] [PubMed] [Google Scholar]
Kumbhar D. D. Pokharkar V. B. Colloids Surf., A. 2013;436:714–725. [Google Scholar]
Mainardes R. M. Khalil N. M. Gremião M. P. D. Int. J. Pharm. 2010;395:266–271. doi: 10.1016/j.ijpharm.2010.05.020. [DOI] [PubMed] [Google Scholar]
Singh S. Dobhal A. K. Jain A. Pandit J. K. Chakraborty S. Chem. Pharm. Bull. 2010;58:650–655. doi: 10.1248/cpb.58.650. [DOI] [PubMed] [Google Scholar]
Kumar P. Lakshmi Y. S. Kondapi A. K. Pharm. Res. 2017;34:257–268. doi: 10.1007/s11095-016-2048-4. [DOI] [PubMed] [Google Scholar]

[cit1] Kahn R. E., Ma W. and Richt J. A., in Influenza Pathogenesis and Control - Volume I, ed. R. W. Compans and M. B. A. Oldstone, Springer International Publishing, Cham, 2014, pp. 205–218 [Google Scholar]

[cit2] Qasim M. Lim D.-J. Park H. Na D. J. Nanosci. Nanotechnol. 2014;14:7374–7387. doi: 10.1166/jnn.2014.9578. [DOI] [PubMed] [Google Scholar]

[cit3] Wejse C. Patsche C. B. Kühle A. Bamba F. J. V. Mendes M. S. Lemvik G. Gomes V. F. Rudolf F. Int. J. Infect. Dis. 2015;32:128–134. doi: 10.1016/j.ijid.2014.12.015. [DOI] [PubMed] [Google Scholar]

[cit4] Braden C. R. Dowell S. F. Jernigan D. B. Hughes J. M. Emerging Infect. Dis. 2013;19:864–869. doi: 10.3201/eid1906.130192. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit5] Breitbart M. Rohwer F. Trends Microbiol. 2005;13:278–284. doi: 10.1016/j.tim.2005.04.003. [DOI] [PubMed] [Google Scholar]

[cit6] Chen L. Liang J. Mater. Sci. Eng. C. 2020;112:110924. doi: 10.1016/j.msec.2020.110924. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit7] Rivera A. Messaoudi I. ACS Infectious Diseases. 2015;1:186–197. doi: 10.1021/id5000426. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit8] Schweitzer C. J. Liang T. J. ACS Infectious Diseases. 2016;1:416–419. doi: 10.1021/acsinfecdis.5b00060. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit9] Aderibigbe B. A. Molecules. 2017;22:1370. [Google Scholar]

[cit10] Galdiero S. Falanga A. Vitiello M. Cantisani M. Marra V. Galdiero M. Molecules. 2011;16:8894–8918. doi: 10.3390/molecules16108894. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit11] Coen D. M. Whitley R. J. Curr. Opin. Virol. 2011;1:545–547. doi: 10.1016/j.coviro.2011.10.024. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit12] Corsi F. Sorrentino L. Mazzucchelli S. Truffi M. Capetti A. Rizzardini G. Fiandra L. J. Pharm. Pharmacol. 2016;4:328–339. [Google Scholar]

[cit13] Lembo D. Donalisio M. Civra A. Argenziano M. Cavalli R. Expert Opin. Drug Delivery. 2018;15:93–114. doi: 10.1080/17425247.2017.1360863. [DOI] [PubMed] [Google Scholar]

[cit14] Calderón L. Harris R. Cordoba-Diaz M. Elorza M. Elorza B. Lenoir J. Adriaens E. Remon J. P. Heras A. Cordoba-Diaz D. Eur. J. Pharm. Sci. 2013;48:216–222. doi: 10.1016/j.ejps.2012.11.002. [DOI] [PubMed] [Google Scholar]

[cit15] Huy T. Q. Hien Thanh N. T. Thuy N. T. Van Chung P. Hung P. N. Le A. T. Hong Hanh N. T. J. Virol. Methods. 2017;241:52–57. doi: 10.1016/j.jviromet.2016.12.015. [DOI] [PubMed] [Google Scholar]

[cit16] Morris D. Ansar M. Speshock J. Ivanciuc T. Qu Y. Casola A. Garofalo R. Viruses. 2019;11:732. doi: 10.3390/v11080732. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit17] Li Y. Lin Z. Xu T. Wang C. Zhao M. Xiao M. Wang H. Deng N. Zhu B. RSC Adv. 2017;7:1453–1463. [Google Scholar]

[cit18] Huy T. Q. Hien Thanh N. T. Thuy N. T. Van Chung P. Hung P. N. Le A. T. Hong Hanh N. T. J. Virol. Methods. 2017;241:52–57. doi: 10.1016/j.jviromet.2016.12.015. [DOI] [PubMed] [Google Scholar]

[cit19] Szymańska E. Orłowski P. Winnicka K. Tomaszewska E. Bąska P. Celichowski G. Grobełny J. Basa A. Krzyżowska M. Int. J. Mol. Sci. 2018;19:387. doi: 10.3390/ijms19020387. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit20] El-Sheekh M. M. Shabaan M. T. Hassan L. Morsi H. H. Int. J. Environ. Health Res. 2020:1–12. doi: 10.1080/09603123.2020.1789946. [DOI] [PubMed] [Google Scholar]

[cit21] Haggag E. G. Elshamy A. M. Rabeh M. A. Gabr N. M. Salem M. Youssif K. A. Samir A. Bin Muhsinah A. Alsayari A. Abdelmohsen U. R. Int. J. Nanomed. 2019;14:6217–6229. doi: 10.2147/IJN.S214171. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit22] Sreekanth T. V. M. Nagajyothi P. C. Muthuraman P. Enkhtaivan G. Vattikuti S. V. P. Tettey C. O. Kim D. H. Shim J. Yoo K. J. Photochem. Photobiol., B. 2018;188:6–11. doi: 10.1016/j.jphotobiol.2018.08.013. [DOI] [PubMed] [Google Scholar]

[cit23] xi Xiang D. Chen Q. Pang L. long Zheng C. J. Virol. Methods. 2011;178:137–142. doi: 10.1016/j.jviromet.2011.09.003. [DOI] [PubMed] [Google Scholar]

[cit24] Xiang D. Zheng Y. Duan W. Li X. Yin J. Shigdar S. O'Connor M. L. Marappan M. Zhao X. Miao Y. Xiang B. Zheng C. Int. J. Nanomed. 2013;8:4103–4114. doi: 10.2147/IJN.S53622. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit25] Gerhardson B. Trends Biotechnol. 2002;20:338–343. doi: 10.1016/s0167-7799(02)02021-8. [DOI] [PubMed] [Google Scholar]

[cit26] Hamed Derbalah A. S. Elsharkawy M. M. J. Biotechnol. 2019;306:134–141. doi: 10.1016/j.jbiotec.2019.10.003. [DOI] [PubMed] [Google Scholar]

[cit27] Huo C. Xiao J. Xiao K. Zou S. Wang M. Qi P. Liu T. Hu Y. Int. J. Nanomed. 2020;15:661–674. doi: 10.2147/IJN.S221667. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit28] Makau J. N. Watanabe K. Mohammed M. M. D. Nishida N. J. Med. Food. 2018;21:777–784. doi: 10.1089/jmf.2017.4121. [DOI] [PubMed] [Google Scholar]

[cit29] Siddiqi K. S. ur Rahman A. Tajuddin Husen A. Nanoscale Res. Lett. 2018;13(1):1–13. doi: 10.1186/s11671-018-2532-3. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit30] Ghaffari H. Tavakoli A. Moradi A. Tabarraei A. Bokharaei-Salim F. Zahmatkeshan M. Farahmand M. Javanmard D. Kiani S. J. Esghaei M. Pirhajati-Mahabadi V. Ataei-Pirkooh A. Monavari S. H. J. Biomed. Sci. 2019;26:1–10. doi: 10.1186/s12929-019-0563-4. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit31] BAILISS K. W. Senananyake S. Plant Pathol. 1984;33:185–192. [Google Scholar]

[cit32] Hsueh Y. H. Lin K. S. Ke W. J. Te Hsieh C. Chiang C. L. Tzou D. Y. Liu S. T. PLoS One. 2015;10:e0144306. doi: 10.1371/journal.pone.0144306. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit33] Adán C. Marugán J. Sánchez E. Pablos C. Van Grieken R. Electrochim. Acta. 2016;191:521–529. [Google Scholar]

[cit34] Di Piero R. M. de Novaes Q. S. Pascholati S. F. Braz. Arch. Biol. Technol. 2010;53:269–278. [Google Scholar]

[cit35] Elsharkawy M. M. Derbalah A. Pest Manage. Sci. 2019;75:828–834. doi: 10.1002/ps.5185. [DOI] [PubMed] [Google Scholar]

[cit36] Gomaa H. Khalifa H. Selim M. M. Shenashen M. A. Kawada S. Alamoudi A. S. Azzam A. M. Alhamid A. A. El-Safty S. A. ACS Sustainable Chem. Eng. 2017;5:10826–10839. [Google Scholar]

[cit37] Jia C. Yang P. Chen H. S. Wang J. CrystEngComm. 2015;17:2940–2948. [Google Scholar]

[cit38] Nakano R. Ishiguro H. Yao Y. Kajioka J. Fujishima A. Sunada K. Minoshima M. Hashimoto K. Kubota Y. Photochem. Photobiol. Sci. 2012;11:1293–1298. doi: 10.1039/c2pp05414k. [DOI] [PubMed] [Google Scholar]

[cit39] Chen Y. N. Hsueh Y. H. Te Hsieh C. Tzou D. Y. Chang P. L. Int. J. Environ. Res. Public Health. 2016;13:4–6. doi: 10.3390/ijerph13040430. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit40] Halder A. Das S. Ojha D. Chattopadhyay D. Mukherjee A. Mater. Sci. Eng. C. 2018;89:413–421. doi: 10.1016/j.msec.2018.04.005. [DOI] [PubMed] [Google Scholar]

[cit41] Di Gianvincenzo P. Marradi M. Martínez-Ávila O. M. Bedoya L. M. Alcamí J. Penadés S. Bioorg. Med. Chem. Lett. 2010;20:2718–2721. doi: 10.1016/j.bmcl.2010.03.079. [DOI] [PubMed] [Google Scholar]

[cit42] Papp I. Sieben C. Ludwig K. Roskamp M. Böttcher C. Schlecht S. Herrmann A. Haag R. Small. 2010;6:2900–2906. doi: 10.1002/smll.201001349. [DOI] [PubMed] [Google Scholar]

[cit43] Paul A. M. Shi Y. Acharya D. Douglas J. R. Cooley A. Anderson J. F. Huang F. Bai F. J. Gen. Virol. 2014;95:1712–1722. doi: 10.1099/vir.0.066084-0. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit44] Li Y. Lin Z. Guo M. Xia Y. Zhao M. Wang C. Xu T. Chen T. Zhu B. Int. J. Nanomed. 2017;12:5733–5743. doi: 10.2147/IJN.S140939. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit45] Lin Z. Li Y. Gong G. Xia Y. Wang C. Chen Y. Hua L. Zhong J. Tang Y. Liu X. Zhu B. Int. J. Nanomed. 2018;13:5787–5797. doi: 10.2147/IJN.S177658. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit46] Li Y. Xu T. Lin Z. Wang C. Xia Y. Guo M. Zhao M. Chen Y. Zhu B. ACS Omega. 2019;4:6720–6725. [Google Scholar]

[cit47] Li Y. Lin Z. Guo M. Zhao M. Xia Y. Wang C. Xu T. Zhu B. Int. J. Nanomed. 2018;13:2005–2016. doi: 10.2147/IJN.S155994. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit48] EA A. EB P. Int. J. Med. Inform. 2019;125:30–36. doi: 10.1016/j.ijmedinf.2019.02.005. [DOI] [PubMed] [Google Scholar]

[cit49] Cheng Z. Zhi X. Sun G. Guo W. Huang Y. Sun W. Tian X. Zhao F. Hu K. J. Med. Virol. 2016;88:653–663. doi: 10.1002/jmv.24366. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit50] Zhong J. Xia Y. Hua L. Liu X. Xiao M. Xu T. Zhu B. Cao H. Artif. Cells, Nanomed., Biotechnol. 2019;47:3485–3491. doi: 10.1080/21691401.2019.1640716. [DOI] [PubMed] [Google Scholar]

[cit51] Du T. Liang J. Dong N. Lu J. Fu Y. Fang L. Xiao S. Han H. ACS Appl. Mater. Interfaces. 2018;10:4369–4378. doi: 10.1021/acsami.7b13811. [DOI] [PubMed] [Google Scholar]

[cit52] Sujitha V. Murugan K. Paulpandi M. Panneerselvam C. Suresh U. Roni M. Nicoletti M. Higuchi A. Madhiyazhagan P. Subramaniam J. Dinesh D. Vadivalagan C. Chandramohan B. Alarfaj A. A. Munusamy M. A. Barnard D. R. Benelli G. Parasitol. Res. 2015;114:3315–3325. doi: 10.1007/s00436-015-4556-2. [DOI] [PubMed] [Google Scholar]

[cit53] Jampílek J. and Král’ová K., in Nanotheranostics: Applications and Limitations, Nature Publishing Group, 2019, pp. 137–178 [Google Scholar]

[cit54] Baram-Pinto D. Shukla S. Gedanken A. Sarid R. Small. 2010;6:1044–1050. doi: 10.1002/smll.200902384. [DOI] [PubMed] [Google Scholar]

[cit55] Fahmi M. Z. Sukmayani W. Khairunisa S. Q. Witaningrum A. M. Indriati D. W. Matondang M. Q. Y. Chang J. Y. Kotaki T. Kameoka M. RSC Adv. 2016;6:92996–93002. [Google Scholar]

[cit56] Łoczechin A. Séron K. Barras A. Giovanelli E. Belouzard S. Chen Y. T. Metzler-Nolte N. Boukherroub R. Dubuisson J. Szunerits S. ACS Appl. Mater. Interfaces. 2019;11:42964–42974. doi: 10.1021/acsami.9b15032. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit57] Fujimori Y. Sato T. Hayata T. Nagao T. Nakayam M. Nakayam T. Sugamat R. Suzuki K. Appl. Environ. Microbiol. 2012;78:951–955. doi: 10.1128/AEM.06284-11. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit58] Shionoiri N. Sato T. Fujimori Y. Nakayama T. Nemoto M. Matsunaga T. Tanaka T. J. Biosci. Bioeng. 2012;113:580–586. doi: 10.1016/j.jbiosc.2011.12.006. [DOI] [PubMed] [Google Scholar]

[cit59] Das Jana I. Kumbhakar P. Banerjee S. Gowda C. C. Kedia N. Kuila S. K. Banerjee S. Das N. C. Das A. K. Manna I. Tiwary C. S. Mondal A. ACS Appl. Nano Mater. 2021;4:352–362. [Google Scholar]

[cit60] Tavakoli A. Hashemzadeh M. S. J. Virol. Methods. 2020;275:113688. doi: 10.1016/j.jviromet.2019.113688. [DOI] [PubMed] [Google Scholar]

[cit61] Hang X. Peng H. Song H. Qi Z. Miao X. Xu W. J. Virol. Methods. 2015;222:150–157. doi: 10.1016/j.jviromet.2015.06.010. [DOI] [PubMed] [Google Scholar]

[cit62] Tang L. Jiang Y. Zhu M. Chen L. Zhou X. Zhou C. Ye P. Chen X. Wang B. Xu Z. Zhang Q. Xu X. Gao H. Wu X. Li D. Jiang W. Qu J. Xiang C. Li L. Front. Med. 2020;14:664–673. doi: 10.1007/s11684-020-0810-9. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit63] Kumar R. Nayak M. Sahoo G. C. Pandey K. Sarkar M. C. Ansari Y. Das V. N. R. Topno R. K. Bhawna Madhukar M. Das P. J. Infect. Chemother. 2019;25:325–329. doi: 10.1016/j.jiac.2018.12.006. [DOI] [PubMed] [Google Scholar]

[cit64] Lin Z. Li Y. Xu T. Guo M. Wang C. Zhao M. Chen H. Kuang J. Li W. Zhang Y. Lin T. Chen Y. Chen H. Zhu B. ACS Omega. 2020;5:12495–12500. doi: 10.1021/acsomega.0c01382. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit65] Balagna C. Perero S. Percivalle E. Nepita E. V. Ferraris M. Open Ceram. 2020;1:100006. [Google Scholar]

[cit66] Du T. Lu J. Liu L. Dong N. Fang L. Xiao S. Han H. ACS Appl. Bio Mater. 2018;1:1286–1293. doi: 10.1021/acsabm.8b00154. [DOI] [PubMed] [Google Scholar]

[cit67] Mazurkova N. A. Spitsyna Y. E. Shikina N. V. Ismagilov Z. R. Zagrebel’nyi S. N. Ryabchikova E. I. Nanotechnol. Russ. 2010;5:417–420. [Google Scholar]

[cit68] Pfaff F. Glück B. Hoyer T. Rohländer D. Sauerbrei A. Zell R. Lett. Appl. Microbiol. 2019;69:302–309. doi: 10.1111/lam.13208. [DOI] [PubMed] [Google Scholar]

[cit69] Mahmood S. Kiong K. C. Tham C. S. Chien T. C. Hilles A. R. Venugopal J. R. AAPS PharmSciTech. 2020;21:1–15. doi: 10.1208/s12249-020-01810-0. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit70] Ilk S. Saglam N. Özgen M. Artif. Cells, Nanomed., Biotechnol. 2017;45:907–916. doi: 10.1080/21691401.2016.1192040. [DOI] [PubMed] [Google Scholar]

[cit71] Raut S. Bhadoriya S. S. Uplanchiwar V. Mishra V. Gahane A. Jain S. K. Acta Pharm. Sin. B. 2012;2:8–15. [Google Scholar]

[cit72] Tan Q. Liu W. Guo C. Zhai G. Int. J. Nanomed. 2011;6:1621. doi: 10.2147/IJN.S22411. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit73] Verhoef J. J. F. Anchordoquy T. J. Drug Delivery Transl. Res. 2013;3:499–503. doi: 10.1007/s13346-013-0176-5. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit74] Mahmood S. Kiong K. C. Tham C. S. Chien T. C. Hilles A. R. Venugopal J. R. AAPS PharmSciTech. 2020;21(7):1–15. doi: 10.1208/s12249-020-01810-0. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit75] Saifi Z. Rizwanullah M. Mir S. R. Amin S. J. Drug Delivery Sci. Technol. 2020;57:101634. [Google Scholar]

[cit76] Fangueiro J. F. Andreani T. Fernandes L. Garcia M. L. Egea M. A. Silva A. M. Souto E. B. Colloids Surf., B. 2014;123:452–460. doi: 10.1016/j.colsurfb.2014.09.042. [DOI] [PubMed] [Google Scholar]

[cit77] Cholkar K. Patel S. P. Vadlapudi A. D. Mitra A. K. J. Ocul. Pharmacol. Ther. 2013;29:106–123. doi: 10.1089/jop.2012.0200. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit78] Warsi M. H. Anwar M. Garg V. Jain G. K. Talegaonkar S. Ahmad F. J. Khar R. K. Colloids Surf., B. 2014;122:423–431. doi: 10.1016/j.colsurfb.2014.07.004. [DOI] [PubMed] [Google Scholar]

[cit79] Bhosale U. V. Kusum Devi V. Jain N. J. Young Pharm. 2011;3:275–283. doi: 10.4103/0975-1483.90236. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit80] Suwannoi P. Chomnawang M. Tunsirikongkon A. Phongphisutthinan A. Müller-Goymann C. C. Sarisuta N. J. Drug Delivery Sci. Technol. 2019;52:624–631. [Google Scholar]

[cit81] Alkholief M. Albasit H. Alhowyan A. Alshehri S. Raish M. Abul Kalam M. Alshamsan A. Saudi Pharm. J. 2019;27:293–302. doi: 10.1016/j.jsps.2018.11.011. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit82] Vedula V. B. Chopra M. Joseph E. Mazumder S. Appl. Nanosci. 2016;6:197–208. [Google Scholar]

[cit83] Belgamwar A. Khan S. Yeole P. Artif. Cells, Nanomed., Biotechnol. 2018;46:374–386. doi: 10.1080/21691401.2017.1313266. [DOI] [PubMed] [Google Scholar]

[cit84] Hari B. N. V. Narayanan N. Dhevendaran K. Ramyadevi D. Mater. Sci. Eng. C. 2016;67:522–532. doi: 10.1016/j.msec.2016.05.064. [DOI] [PubMed] [Google Scholar]

[cit85] Kumar P. Lakshmi Y. S. Kondapi A. K. HIV Med. 2017;18:452–462. doi: 10.1111/hiv.12475. [DOI] [PubMed] [Google Scholar]

[cit86] Joshy K. S. George A. Snigdha S. Joseph B. Kalarikkal N. Pothen L. A. Thomas S. Mater. Sci. Eng. C. 2018;93:864–872. doi: 10.1016/j.msec.2018.08.015. [DOI] [PubMed] [Google Scholar]

[cit87] Joshy K. S. Snigdha S. Anne G. Nandakumar K. Laly A. P. Sabu T. Chem. Phys. Lipids. 2018;210:82–89. doi: 10.1016/j.chemphyslip.2017.11.003. [DOI] [PubMed] [Google Scholar]

[cit88] Joshy K. S. Susan M. A. Snigdha S. Nandakumar K. Laly A. P. Sabu T. Int. J. Biol. Macromol. 2018;107:929–937. doi: 10.1016/j.ijbiomac.2017.09.078. [DOI] [PubMed] [Google Scholar]

[cit89] Joshy K. S. Snigdha S. Kalarikkal N. Pothen L. A. Thomas S. Chem. Phys. Lipids. 2017;207:24–37. doi: 10.1016/j.chemphyslip.2017.07.002. [DOI] [PubMed] [Google Scholar]

[cit90] Joshy K. S. Snigdha S. George A. Kalarikkal N. Pothen L. A. Thomas S. Cellulose. 2017;24:4759–4771. [Google Scholar]

[cit91] Carvalho A. L. M. da Silva J. A. Lira A. A. M. Conceição T. M. F. Nunes R. de S. de Albuquerque Junior R. L. C. Sarmento V. H. V. Leal L. B. de Santana D. P. J. Pharm. Sci. 2016;105:2188–2193. doi: 10.1016/j.xphs.2016.04.013. [DOI] [PubMed] [Google Scholar]

[cit92] Joshy K. S. Sharma C. P. Kalarikkal N. Sandeep K. Thomas S. Pothen L. A. Mater. Sci. Eng. C. 2016;66:40–50. doi: 10.1016/j.msec.2016.03.031. [DOI] [PubMed] [Google Scholar]

[cit93] Laux A. Gouws C. Hamman J. H. Expert Opin. Drug Delivery. 2019;16:1283–1285. doi: 10.1080/17425247.2019.1675633. [DOI] [PubMed] [Google Scholar]

[cit94] Gomez-Orellana I. Expert Opin. Drug Delivery. 2005;2:419–433. doi: 10.1517/17425247.2.3.419. [DOI] [PubMed] [Google Scholar]

[cit95] Pather S. I. Rathbone M. J. Senel S. Expert Opin. Drug Delivery. 2008;5:531–542. doi: 10.1517/17425247.5.5.531. [DOI] [PubMed] [Google Scholar]

[cit96] Prausnitz M. R. Langer R. Nat. Biotechnol. 2008;26:1261–1268. doi: 10.1038/nbt.1504. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit97] Ernest T. B. Elder D. P. Martini L. G. Roberts M. Ford J. L. J. Pharm. Pharmacol. 2010;59:1043–1055. doi: 10.1211/jpp.59.8.0001. [DOI] [PubMed] [Google Scholar]

[cit98] Cram A. Breitkreutz J. Desset-Brèthes S. Nunn T. Tuleu C. Int. J. Pharm. 2009;365:1–3. doi: 10.1016/j.ijpharm.2008.09.015. [DOI] [PubMed] [Google Scholar]

[cit99] P. N.-W. D. Information and U. 2012, WHO Drug Information International Regulatory Harmonization

[cit100] Pham K. Li D. Guo S. Penzak S. Dong X. J. Controlled Release. 2016;226:88–97. doi: 10.1016/j.jconrel.2016.02.001. [DOI] [PubMed] [Google Scholar]

[cit101] Ravi P. R. Vats R. J. Pharm. Pharmacol. 2017;69:823–833. doi: 10.1111/jphp.12716. [DOI] [PubMed] [Google Scholar]

[cit102] Negi J. S. Chattopadhyay P. Sharma A. K. Ram V. Eur. J. Pharm. Sci. 2013;48:231–239. doi: 10.1016/j.ejps.2012.10.022. [DOI] [PubMed] [Google Scholar]

[cit103] Ravi P. R. Vats R. Balija J. Adapa S. P. N. Aditya N. Carbohydr. Polym. 2014;110:320–328. doi: 10.1016/j.carbpol.2014.03.099. [DOI] [PubMed] [Google Scholar]

[cit104] Dodiya S. S. Chavhan S. S. Sawant K. K. Korde A. G. J. Microencapsulation. 2011;28:515–527. doi: 10.3109/02652048.2011.590612. [DOI] [PubMed] [Google Scholar]

[cit105] Krieser K. Emanuelli J. Daudt R. M. Bilatto S. Willig J. B. Guterres S. S. Pohlmann A. R. Buffon A. Correa D. S. Külkamp-Guerreiro I. C. Mater. Sci. Eng. C. 2020;117:111315. doi: 10.1016/j.msec.2020.111315. [DOI] [PubMed] [Google Scholar]

[cit106] He Y. Xia D. N. Li Q. X. Tao J. S. Gan Y. Wang C. Acta Pharmacol. Sin. 2015;36:1151–1160. doi: 10.1038/aps.2015.53. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit107] Kurd M. Malvajerd S. S. Rezaee S. Hamidi M. Derakhshandeh K. Artif. Cells, Nanomed., Biotechnol. 2019;47:2123–2133. doi: 10.1080/21691401.2019.1616553. [DOI] [PubMed] [Google Scholar]

[cit108] Bianchin M. D. Prebianca G. Immich M. F. Teixeira M. L. Colombo M. Koester L. S. de Araújo B. V. Poletto F. Külkamp-Guerreiro I. C. Drug Dev. Ind. Pharm. 2021;47:83–91. doi: 10.1080/03639045.2020.1862167. [DOI] [PubMed] [Google Scholar]

[cit109] Prabhakar K. Afzal S. M. Surender G. Kishan V. Acta Pharm. Sin. B. 2013;3:345–353. [Google Scholar]

[cit110] Pompei R. Flore O. Marccialis M. A. Pani A. Loddo B. Nature. 1979;281:689–690. doi: 10.1038/281689a0. [DOI] [PubMed] [Google Scholar]

[cit111] Cinatl J. Morgenstern B. Bauer G. Chandra P. Rabenau H. Doerr H. W. Lancet. 2003;361:2045–2046. doi: 10.1016/S0140-6736(03)13615-X. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit112] Chew J. L. Wolfowicz C. B. Mao H. Q. Leong K. W. Chua K. Y. Vaccine. 2003;21:2720–2729. doi: 10.1016/s0264-410x(03)00228-7. [DOI] [PubMed] [Google Scholar]

[cit113] Wu Y. Yang W. Wang C. Hu J. Fu S. Int. J. Pharm. 2005;295:235–245. doi: 10.1016/j.ijpharm.2005.01.042. [DOI] [PubMed] [Google Scholar]

[cit114] Depan D. Girase B. Shah J. S. Misra R. D. K. Acta Biomater. 2011;7:3432–3445. doi: 10.1016/j.actbio.2011.05.019. [DOI] [PubMed] [Google Scholar]

[cit115] Depan D. Venkata Surya P. K. C. Girase B. Misra R. D. K. Acta Biomater. 2011;7:2163–2175. doi: 10.1016/j.actbio.2011.01.029. [DOI] [PubMed] [Google Scholar]

[cit116] Yuan Q. Hein S. Misra R. D. K. Acta Biomater. 2010;6:2732–2739. doi: 10.1016/j.actbio.2010.01.025. [DOI] [PubMed] [Google Scholar]

[cit117] Mishra D. Jain N. Rajoriya V. Jain A. K. J. Pharm. Pharmacol. 2014;66:1082–1093. doi: 10.1111/jphp.12235. [DOI] [PubMed] [Google Scholar]

[cit118] Cavalcanti S. M. T. Nunes C. Lima S. A. C. Soares-Sobrinho J. L. Reis S. Pharm. Res. 2017;34:1204–1216. doi: 10.1007/s11095-017-2136-0. [DOI] [PubMed] [Google Scholar]

[cit119] Woodsong C. Holt J. D. S. Adv. Drug Delivery Rev. 2015;92:146–154. doi: 10.1016/j.addr.2015.02.004. [DOI] [PubMed] [Google Scholar]

[cit120] Machado A. Cunha-Reis C. Araújo F. Nunes R. Seabra V. Ferreira D. das Neves J. Sarmento B. Acta Biomater. 2016;44:332–340. doi: 10.1016/j.actbio.2016.08.018. [DOI] [PubMed] [Google Scholar]

[cit121] Timur S. S. Şahin A. Aytekin E. Öztürk N. Polat K. H. Tezel N. Gürsoy R. N. Çalış S. Pharm. Dev. Technol. 2018;23:301–310. doi: 10.1080/10837450.2017.1329835. [DOI] [PubMed] [Google Scholar]

[cit122] Meng J. Zhang T. Agrahari V. Ezoulin M. J. Youan B. B. C. Nanomedicine. 2014;9:1595–1612. doi: 10.2217/nnm.13.136. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit123] Meng J. Agrahari V. Ezoulin M. J. Zhang C. Purohit S. S. Molteni A. Dim D. Oyler N. A. Youan B. B. C. Mol. Pharm. 2016;13:4129–4140. doi: 10.1021/acs.molpharmaceut.6b00739. [DOI] [PubMed] [Google Scholar]

[cit124] Parthiban R. Shanmugapriya Indhu Sathishkumar Surendhar Prakash R. Drug Invent. Today. 2020;14:108–111. [Google Scholar]

[cit125] Mahboobian M. M. Mohammadi M. Mansouri Z. J. Drug Delivery Sci. Technol. 2020;55:101400. [Google Scholar]

[cit126] Gandhi A. Jana S. Sen K. K. Int. J. Biol. Macromol. 2014;67:478–482. doi: 10.1016/j.ijbiomac.2014.04.019. [DOI] [PubMed] [Google Scholar]

[cit127] Calderón L. Harris R. Cordoba-Diaz M. Elorza M. Elorza B. Lenoir J. Adriaens E. Remon J. P. Heras A. Cordoba-Diaz D. Eur. J. Pharm. Sci. 2013;48:216–222. doi: 10.1016/j.ejps.2012.11.002. [DOI] [PubMed] [Google Scholar]

[cit128] Rajendran N. Natrajan R. Kumar R. Selvaraj S. Asian J. Pharm. 2010;4:220–226. [Google Scholar]

[cit129] Peira E. Chirio D. Carlotti M. E. Spagnolo R. Trotta M. J. Drug Delivery Sci. Technol. 2009;19:191–196. [Google Scholar]

[cit130] Cavalli R. Donalisio M. Civra A. Ferruti P. Ranucci E. Trotta F. Lembo D. J. Controlled Release. 2009;137:116–122. doi: 10.1016/j.jconrel.2009.04.004. [DOI] [PubMed] [Google Scholar]

[cit131] Alsarra I. A. Hamed A. Y. Alanazi F. K. Drug Delivery. 2008;15:313–321. doi: 10.1080/10717540802035251. [DOI] [PubMed] [Google Scholar]

[cit132] Suwannoi P. Chomnawang M. Sarisuta N. Reichl S. Müller-Goymann C. C. J. Ocul. Pharmacol. Ther. 2017;33:743–752. doi: 10.1089/jop.2017.0057. [DOI] [PubMed] [Google Scholar]

[cit133] Xing-Guo Z. Jing M. Min-Wei L. Sai-Ping J. Fu-Qiang H. Yong-Zhong D. J. Zhejiang Univ., Sci., B. 2008;9:506–510. doi: 10.1631/jzus.B0820047. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit134] Singh G. Pai R. S. Drug Delivery. 2016;23:532–539. doi: 10.3109/10717544.2014.930760. [DOI] [PubMed] [Google Scholar]

[cit135] Duan J. Freeling J. P. Koehn J. Shu C. Ho R. J. Y. J. Pharm. Sci. 2014;103:2520–2529. doi: 10.1002/jps.24046. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit136] Nowacek A. S. McMillan J. Miller R. Anderson A. Rabinow B. Gendelman H. E. J Neuroimmune Pharmacol. 2010;5:592–601. doi: 10.1007/s11481-010-9198-7. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit137] Garg M. Jain N. K. J. Drug Targeting. 2006;14:1–11. doi: 10.1080/10611860500525370. [DOI] [PubMed] [Google Scholar]

[cit138] Elkateb H. Tatham L. M. Cauldbeck H. Niezabitowska E. Owen A. Rannard S. McDonald T. Int. J. Pharm. 2020;588:119794. doi: 10.1016/j.ijpharm.2020.119794. [DOI] [PubMed] [Google Scholar]

[cit139] Priya Dharshini K. Fang H. Ramya Devi D. Yang J. X. Luo R. H. Zheng Y. T. Brzeziński M. Vedha Hari B. N. Carbohydr. Polym. 2021;256:117440. doi: 10.1016/j.carbpol.2020.117440. [DOI] [PubMed] [Google Scholar]

[cit140] Belgamwar A. V. Khan S. A. Yeole P. G. J. Drug Delivery Sci. Technol. 2019;52:1008–1020. [Google Scholar]

[cit141] Rozana R. Yulizar Y. Saefumillah A. Apriandanu D. O. B. AIP Conf. Proc. 2020;2242:040004. [Google Scholar]

[cit142] Makwana V. Jain R. Patel K. Nivsarkar M. Joshi A. Int. J. Pharm. 2015;495:439–446. doi: 10.1016/j.ijpharm.2015.09.014. [DOI] [PubMed] [Google Scholar]

[cit143] Gaur P. K. Mishra S. Bajpai M. Mishra A. BioMed Res. Int. 2014;2014:363404. doi: 10.1155/2014/363404. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit144] Tshweu L. Katata L. Kalombo L. Chiappetta D. A. Hocht C. Sosnik A. Swai H. Nanomedicine. 2014;9:1821–1833. doi: 10.2217/nnm.13.167. [DOI] [PubMed] [Google Scholar]

[cit145] Kotta S. Khan A. W. Ansari S. H. Sharma R. K. Ali J. Int. J. Pharm. 2014;462:129–134. doi: 10.1016/j.ijpharm.2013.12.038. [DOI] [PubMed] [Google Scholar]

[cit146] Shibata A. McMullen E. Pham A. Belshan M. Sanford B. Zhou Y. Goede M. Date A. A. Destache C. J. AIDS Res. Hum. Retroviruses. 2013;29:746–754. doi: 10.1089/aid.2012.0301. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit147] de Sousa M. Pessine F. B. T. Adv. Sci., Eng. Med. 2014;6:1135–1142. [Google Scholar]

[cit148] Gong Y. Zhi K. Nagesh P. K. B. Sinha N. Chowdhury P. Chen H. Gorantla S. Yallapu M. M. Kumar S. Viruses. 2020;12:564. doi: 10.3390/v12050564. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit149] Gong Y. Chowdhury P. Midde N. M. Rahman M. A. Yallapu M. M. Kumar S. Biochem. Biophys. Rep. 2017;12:214–219. doi: 10.1016/j.bbrep.2017.10.005. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit150] Figueira T. N. Domingues M. M. Illien F. Cadima-Couto I. Todorovski T. Andreu D. Sagan S. Castanho M. A. R. B. Walrant A. Veiga A. S. ACS Infectious Diseases. 2020;6:224–236. doi: 10.1021/acsinfecdis.9b00285. [DOI] [PubMed] [Google Scholar]

[cit151] Russo E. Gaglianone N. Baldassari S. Parodi B. Cafaggi S. Zibana C. Donalisio M. Cagno V. Lembo D. Caviglioli G. Colloids Surf., B. 2014;118:117–125. doi: 10.1016/j.colsurfb.2014.03.037. [DOI] [PubMed] [Google Scholar]

[cit152] Tyo K. M. Lasnik A. B. Zhang L. Mahmoud M. Jenson A. B. Fuqua J. L. Palmer K. E. Steinbach-Rankins J. M. J. Controlled Release. 2020;321:84–99. doi: 10.1016/j.jconrel.2020.02.006. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit153] Karami Z. Saghatchi Zanjani M. R. Rezaee S. Rostamizadeh K. Hamidi M. Drug Dev. Ind. Pharm. 2019;45:736–744. doi: 10.1080/03639045.2019.1569039. [DOI] [PubMed] [Google Scholar]

[cit154] Surnar B. Kamran M. Z. Shah A. S. Basu U. Kolishetti N. Deo S. Jayaweera D. T. Daunert S. Dhar S. ACS Nano. 2019;13:11034–11048. doi: 10.1021/acsnano.9b02807. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit155] Joshi G. Kumar A. Sawant K. Drug Delivery. 2016;23:3492–3504. doi: 10.1080/10717544.2016.1199605. [DOI] [PubMed] [Google Scholar]

[cit156] Ravi P. R. Vats R. Dalal V. Gadekar N. Aditya N. Drug Dev. Ind. Pharm. 2015;41:131–140. doi: 10.3109/03639045.2013.850710. [DOI] [PubMed] [Google Scholar]

[cit157] Alex A. Paul W. Chacko A. J. Sharma C. P. Ther. Delivery. 2011;2:25–35. doi: 10.4155/tde.10.96. [DOI] [PubMed] [Google Scholar]

[cit158] Perazzolo S. Shireman L. M. Koehn J. McConnachie L. A. Kraft J. C. Shen D. D. Ho R. J. Y. J. Pharm. Sci. 2018;107:3153–3162. doi: 10.1016/j.xphs.2018.07.032. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit159] Fotooh Abadi L. Kumar P. Gajbhiye V. Paknikar K. M. Kulkarni S. Colloids Surf., B. 2020;194:111227. doi: 10.1016/j.colsurfb.2020.111227. [DOI] [PubMed] [Google Scholar]

[cit160] Lahkar S. Das M. K. J. Nanopart. Res. 2020;22:109. [Google Scholar]

[cit161] Varshosaz J. Taymouri S. Jafari E. Jahanian-Najafabadi A. Taheri A. J. Drug Delivery Sci. Technol. 2018;48:9–20. [Google Scholar]

[cit162] Ramana L. N. Sethuraman S. Ranga U. Krishnan U. M. J. Biomed. Sci. 2010;17:1–9. doi: 10.1186/1423-0127-17-57. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit163] Date A. A. Shibata A. Goede M. Sanford B. La Bruzzo K. Belshan M. Destache C. J. Antiviral Res. 2012;96:430–436. doi: 10.1016/j.antiviral.2012.09.015. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit164] Javan F. Vatanara A. Azadmanesh K. Nabi-Meibodi M. shakouri M. J. Pharm. Pharmacol. 2017;69:1002–1009. doi: 10.1111/jphp.12737. [DOI] [PubMed] [Google Scholar]

[cit165] Kumar S. Narayan R. Ahammed V. Nayak Y. Naha A. Nayak U. Y. J. Drug Delivery Sci. Technol. 2018;44:181–189. [Google Scholar]

[cit166] Abou-El-Naga I. F. El Kerdany E. D. Mady R. F. Shalaby T. I. Zaytoun E. M. Parasitol. Int. 2017;66:735–747. doi: 10.1016/j.parint.2017.08.007. [DOI] [PubMed] [Google Scholar]

[cit167] Jain S. Sharma J. M. Jain A. K. Mahajan R. R. Nanomedicine. 2013;8:1639–1655. doi: 10.2217/nnm.12.181. [DOI] [PubMed] [Google Scholar]

[cit168] Bimbo L. M. Denisova O. V. Mäkilä E. Kaasalainen M. De Brabander J. K. Hirvonen J. Salonen J. Kakkola L. Kainov D. Santos H. A. ACS Nano. 2013;7:6884–6893. doi: 10.1021/nn402062f. [DOI] [PubMed] [Google Scholar]

[cit169] Ramana L. N. Sharma S. Sethuraman S. Ranga U. Krishnan U. M. Biochim. Biophys. Acta, Gen. Subj. 2014;1840:476–484. doi: 10.1016/j.bbagen.2013.10.002. [DOI] [PubMed] [Google Scholar]

[cit170] Kuo Y. C. Ko H. F. Biomaterials. 2013;34:4818–4830. doi: 10.1016/j.biomaterials.2013.03.013. [DOI] [PubMed] [Google Scholar]

[cit171] Adlin Jino Nesalin J. Anton Smith A. J. Pharm. Res. 2013;6:268–274. [Google Scholar]

[cit172] Shegokar R. Singh K. K. Pharmazie. 2011;66:264–271. [PubMed] [Google Scholar]

[cit173] Garg M. Asthana A. Agashe H. B. Agrawal G. P. Jain N. K. J. Pharm. Pharmacol. 2010;58:605–616. doi: 10.1211/jpp.58.5.0005. [DOI] [PubMed] [Google Scholar]

[cit174] Kuo Y. C. Chung C. Y. Colloids Surf., B. 2011;88:682–690. doi: 10.1016/j.colsurfb.2011.07.060. [DOI] [PubMed] [Google Scholar]

[cit175] Chaowanachan T. Krogstad E. Ball C. Woodrow K. A. PLoS One. 2013;8:61416. doi: 10.1371/journal.pone.0061416. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit176] Mandal S. Prathipati P. K. Kang G. Zhou Y. Yuan Z. Fan W. Li Q. Destache C. J. Aids. 2017;31:469–476. doi: 10.1097/QAD.0000000000001349. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit177] Mandal S. Kang G. Prathipati P. K. Zhou Y. Fan W. Li Q. Destache C. J. J. Controlled Release. 2019;294:216–225. doi: 10.1016/j.jconrel.2018.12.027. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit178] Shailender J. Ravi P. R. Reddy Sirukuri M. Dalvi A. Keerthi Priya O. Drug Dev. Ind. Pharm. 2018;44:1109–1119. doi: 10.1080/03639045.2018.1438459. [DOI] [PubMed] [Google Scholar]

[cit179] Gourdon B. Chemin C. Moreau A. Arnauld T. Baumy P. Cisternino S. Péan J. M. Declèves X. Int. J. Pharm. 2017;529:357–370. doi: 10.1016/j.ijpharm.2017.07.024. [DOI] [PubMed] [Google Scholar]

[cit180] Kumar R. Sinha V. R. AAPS PharmSciTech. 2017;18:884–894. doi: 10.1208/s12249-016-0575-2. [DOI] [PubMed] [Google Scholar]

[cit181] Cavalcanti S. M. T. Nunes C. Costa Lima S. A. Soares-Sobrinho J. L. Reis S. Eur. J. Pharm. Sci. 2018;122:22–30. doi: 10.1016/j.ejps.2018.06.017. [DOI] [PubMed] [Google Scholar]

[cit182] Yan J. K. Wang Y. Y. Qiu W. Y. Wu J. Y. Carbohydr. Polym. 2017;174:209–216. doi: 10.1016/j.carbpol.2017.06.082. [DOI] [PubMed] [Google Scholar]

[cit183] Da Silva Barbi M. Carvalho F. C. Kiill C. P. Da Silva Barud H. Santagneli S. H. Ribeiro S. J. L. Gremião M. P. D. J. Nanosci. Nanotechnol. 2015;15:865–874. doi: 10.1166/jnn.2015.9180. [DOI] [PubMed] [Google Scholar]

[cit184] Kumbhar D. D. Pokharkar V. B. Colloids Surf., A. 2013;436:714–725. [Google Scholar]

[cit185] Mainardes R. M. Khalil N. M. Gremião M. P. D. Int. J. Pharm. 2010;395:266–271. doi: 10.1016/j.ijpharm.2010.05.020. [DOI] [PubMed] [Google Scholar]

[cit186] Singh S. Dobhal A. K. Jain A. Pandit J. K. Chakraborty S. Chem. Pharm. Bull. 2010;58:650–655. doi: 10.1248/cpb.58.650. [DOI] [PubMed] [Google Scholar]

[cit187] Kumar P. Lakshmi Y. S. Kondapi A. K. Pharm. Res. 2017;34:257–268. doi: 10.1007/s11095-016-2048-4. [DOI] [PubMed] [Google Scholar]

PERMALINK

Antiviral role of nanomaterials: a material scientist's perspective

Muhammad Aanish Ali

Nagina Rehman

Tae Joo Park

Muhammad Abdul Basit

Abstract

1. Introduction

Fig. 1. An overview of applications of nanoparticles and their combinations with a variety of antiviral drugs.

2. Metal-based nanoparticles as effective antivirals

2.1. Ag-based NPs

2.2. NiO nanostructures (NONS)

Fig. 3. (a) FESEM micrograph of NONS. (b) FESEM micrograph showing uniform formation of head and trunk. (c) XRD pattern of NONS. (d) Raman spectroscopy results of NONS (reprinted with permission from ref. 26 Copyrights 2019 Elsevier).

2.3. Zirconia NPs

2.4. ZnO NPs

2.5. TiO2-based NPs

2.6. GO-Ag NPs

Fig. 6. Schematic illustration of antiviral mechanism of (a) GO; (b) GO-Ag against enveloped viruses; (c) GO and (d) GO-Ag against non-enveloped viruses (reprinted with permission from ref. 39 Copyrights 2016 MDPI).

2.7. Gold nanoparticles (AuNPs)

2.8. Selenium NPs

Antiviral activity of different metallic and functional nanoparticles against a broad spectrum of viruses along with key parameters reported.

3. Nanoparticles for enhancing the efficacy of antiviral drugs

3.1. Acyclovir

3.1.1. Oral delivery

3.1.2. Ocular delivery

3.1.3. Intravenous delivery

3.2. Efavirenz (EFV)

3.2.1. Intravenous/intranasal delivery

3.2.2. Oral delivery

3.3. Zidovudine (AZT)

3.3.1. Intravenous delivery

3.3.2. Oral delivery

3.3.3. Transdermal delivery

3.3.4. Possible routes for aloe vera based administrations

3.4. Lopinavir (LPN)

3.4.1. Oral delivery

3.5. Saquinavir (SQV)

3.5.1. Oral delivery

3.6. Indinavir (IDV)

3.6.1. Oral delivery

3.6.2. Intravenous delivery

3.7. Lamivudine

3.8. Tenofovir (TFV)

3.8.1. Vaginal route

Results of various studies over the past decade showing efficacies of different drug carrier systems with relevant parameters. (EE1: encapsulation efficiency, EE2: entrapment efficiency).

4. Conclusion

5. Future perspectives

Author contributions

Conflicts of interest

Supplementary Material

Acknowledgments

Biographies

Biography

Muhammad Aanish Ali.

Biography

Nagina Rehman.

Biography

Tae Joo Park.

Biography

Muhammad Abdul Basit.

References

ACTIONS

PERMALINK

RESOURCES

Similar articles

Cited by other articles

Links to NCBI Databases

2.5. TiO₂-based NPs

Results of various studies over the past decade showing efficacies of different drug carrier systems with relevant parameters. (EE₁: encapsulation efficiency, EE₂: entrapment efficiency).