MMP-sensitive PEG hydrogel modified with RGD promotes bFGF, VEGF and EPC-mediated angiogenesis

Abstract

Traumatic soft tissue defects such as bedsores, chronic skin ulcers, limb necrosis, osteonecrosis and other ischemic orthopedic diseases are the most clinically intractable and common problems in orthopedics due to unsatisfactory conventional treatments. The present study designed poly(ethylene glycol; PEG) hydrogels with covalently binded arginylglycylaspartic acid (RGD). Endothelial progenitor cells (EPCs) were encapsulated in the modified hydrogel along with vascular endothelial growth factor (VEGF) and basic fibroblast growth factor (bFGF). Results demonstrated that the modified hydrogel displayed good mechanical properties appropriate for a sustained release carrier. RGD modification significantly promoted EPC biocompatibility. VEGF and bFGF encapsulation enhanced the adhesion of EPCs, promoted the production of extracellular matrix and facilitated EPC proliferation. In addition, bFGF and VEGF induced angiogenesis. The combination of growth factors and EPCs in the hydrogel displayed a strong synergy to improve biocompatibility. The present results provided a potential novel treatment approach for soft tissue defects such as bone exposure, chronic skin ulcers, bedsores, limb necrosis, osteonecrosis and other ischemic diseases.

Introduction

Traumatic soft tissue defects such as bedsores, chronic skin ulcers, limb necrosis, osteonecrosis and other ischemic orthopedic diseases are the most clinically intractable and common issues in orthopedics due to unsatisfactory conventional treatments (1). Interest in therapeutic vasculogenesis has arisen as a potential solution to these problems where endothelial progenitor cells (EPCs) or stem cells are transplanted into the ischemic site to promote angiogenesis (2,3). EPC-mediated angiogenesis has a unique advantage of not being affected by the function of the original blood vessels and native endothelial cells (ECs). EPCs are widely present in adult bone marrow, and have sustained and pluripotent differentiation abilities. EPCs promote the development of blood vessels by differentiating into mature vascular ECs then secreting vascular growth factors (4,5). EPC-mediated angiogenesis improves blood supply to the ischemic site in both animal and clinical trials (6,7); however, injected growth factors are rapidly cleared from the body and thus any transplanted cells undergo rapid cell death in large numbers due to the lack of nutrients. This phenomenon hinders the clinical applications of EPC-mediated therapeutic angiogenesis.

Hydrogels are promising biocompatible and biodegradable biomaterials used as cell transplant vectors that also have roles as drug release systems and tissue engineered cell scaffolds (8,9). Hydrogels are water-soluble polymer networks capable of absorbing a large amount of water to swell and, after swelling, are capable of maintaining their three-dimensional polymer structure due to physical or chemical cross-linking between polymer chains (10). Due to hydrogels displaying good biocompatibility, water permeability and a high degree of swelling this makes them a promising biomaterial for implantation (11). Since 2000, arginylglycylaspartic acid (RGD) peptides have been used to modify hydrogels in order to improve their biocompatibility (8). The RGD tripeptide is the smallest amino acid sequence recognized by adherent proteins. This sequence binds specifically to cell surface integrin receptors, which mediate cell adhesion, migration and growth. Consequently, the immobilization of RGD directly onto a biomaterial promotes the adhesion of receptor-mediated cells to the surface of the material (8,9,12). In 2009, matrix-metalloproteinase (MMP)-sensitive polyethylene glycol (PEG) hydrogels were used to encapsulate human umbilical vein ECs and thymosin β-4, a human protein that promotes tissue regeneration. It was determined that the modified hydrogel provide an environment that supports human umbilical vein ECs, reduces apoptosis, increases cell survival rate and achieves a controlled release of thymosin β-4 (12).

The proliferation, differentiation, maturation, and integration of host blood vessels with EPCs require growth factor involvement such as basic fibroblast growth factor (bFGF) and vascular endothelial growth factor (VEGF) (10,11,13,14). Vascular growth factors and EPCs work synergistically to create new blood vessels, capillaries, and the formation of capillary networks in the ischemic area. Seliktar et al (15) combined RGD and multiple growth factors into the PEG hydrogel backbone by covalent binding and found that this design not only slowly releases the growth factors but also promotes the adhesion and growth of ECs on the biomaterial surface.

Scaffolds are critical in EPC-mediated therapeutic vasculogenesis therefore the purpose of the present study was to design modified PEG hydrogels with covalently bound RGD to encapsulate EPCs alongside VEGF and bFGF. The role of the growth factors was to maintain EPC health, integrate with the host blood vessels, and also to ensure the sustained long-term release of vascular growth factors into the wound.

Materials and methods

Animal study

Twenty male Sprague Dawley rats (6–8 weeks) weighing 180–200 g were obtained from the Experimental Animal Center of Huazhong University of Science and Technology. Animals were housed at constant room temperature with a 12-h light-dark cycle, and free access to a standard rodent diet and water. Protocols involving the use of the animals were approved by the Ethics Committee of Tongji Medical College, Huazhong University of Science and Technology (2016 Institutional Animal Care and Use Committee no. S782). Animal experiments were performed in accordance with the Guide for the Care and Use of Laboratory Animals.

Synthesis of four-arm-polyethylene glycol-vinylsulfone (PEG-VS) monomer reaction

The hydrogel synthesis method was adapted from Seliktar et al (15). Four-arm-PEG powder (cat. no. 4ARM-PEG-OH; Shanghai Jinpan Biotech Co., Ltd.) was dissolved in dichloromethane (DCM; analytical reagent, purity >99.5%) to prepare a 0.2 g/ml solution. Then PEG-OH, sodium hydride, and diVS were mixed together in a reaction molar ratio of 1:5:50, respectively. The reactor was wrapped with foil to keep it in the dark for the entire time. The reaction was kept in an argon atmosphere and stirred for 3 days at room temperature. Pure acetic acid (pH 7) was used to neutralize the solution following completion of the reaction and all residues were filtered using filter paper. Then cold pure acetic acid was then added in excess to produce a precipitate and the supernatant was discarded. The precipitate was washed using DCM, then subsequently resuspended in DCM, and filtered again to produce a precipitate. DCM was used to wash this precipitation twice to remove the excess diVS. Finally, powder was obtained by overnight freeze vacuum drying at 50°C in a lyophilizer (model no. FD-1A-50; Beijing Boyikang Laboratory Instruments Co., Ltd.). Nuclear magnetic resonance spectroscopy (¹H-NMR; AVANCE III HDNanobay 400 MHz compact NMR system; Bruker BioSpin Corporation) was conducted according to the basic NMR operational manual to assess the VS to acquire a peak at 6.1–6.4.

Formation of MMP-sensitive PEG hydrogels modified with RGD

Hydrogel formation was prepared as previously described in the literature (12,16,17). In brief, 330 mg of the prepared four-arm-PEG-VS monomer was dissolved in 2.7 ml Tris base, acetic acid and ethylenediaminetetraacetic acid (TAE; 0.3 M; pH 8) solution, with w/v of 10% at 4°C, then stored at the same temperature. A total of 4.7 mg RGD (Ac-GCRDGPQGIWGQDRCG-NH₂; Zoonbio Biotechnology, Co., Ltd.) was dissolved in 3 ml TAE buffer (0.3 M; pH 8) then 4.7 mg matrix metalloproteinase (MMP) reaction substrate peptide (Zoonbio Biotechnology, Co., Ltd.) was dissolved in 3 ml TAE buffer (0.3 M; pH 8). Following which, 30 µl of RGD TAE solution and 30 µl of MMP reaction peptide TAE solution were added to 270 µl of four-arm-PEG-VS TAE solution then mixed at 37°C for 30 min. Finally, the mixed solution was transferred into a clean penicillin bottle and kept at 37°C for 30 min to form a hydrogel.

Hydrogels with 5-carboxyfluorescein (cat. no. F5008; US Everbright, Inc.)-labeled peptide encapsulated with VEGF (cat. no. 400-31) and bFGF (cat. no. 400-29; both 1.2 ng/well; Peprotech) were manufactured in a similar manner as the aforementioned procedures but the RGD peptides were replaced with 5-carboxyfluorescein fluorescent-labeled peptides then hydrogels were soaked in PBS.

Release curve

The hydrogel was soaked in PBS then ELISAs (cat. no. E-EL-R0091 and E-EL-R0020; Elabscience Biotechnology Co., Ltd.) was used to test the content and stability of bFGF and VEGF every 12 h. MMP-2 (100 and 1,000 ng) and MMP-9 (100 and 1,000 ng) were added to the samples following 72 h, then the optical density (OD450) value was measured by ELISA. The release curve was plotted after repeating the previous method to detect the slow-release effect of bFGF and VEGF.

Hydrogel stability and biodegradation test

A hydrogel stability test was conducted where hydrogels were transferred into a 12-well plate, and then soaked in 40 ml PBS in the dark at room temperature. PBS was replaced every day. In order to set up the standard solutions of fluorescent RGD peptides, the concentration of RGD peptide were as follows: 2, 1, 0.5, 0.25 and 0.125 µg/ml. Fluorescence intensities at OD505 for both standard solutions and the soaking PBS solution were measured with a fluorescence photometer. To test the degradation behavior of the hydrogel, wet weight hydrogel (20 mg; n=3) was dried in a lyophilizer until the weight. Then the dried hydrogels were placed in a penicillin bottle, soaked in PBS on a shaking bed at room temperature. The weight of the hydrogels after lyophilization was measured every day and was used for the degradation rate calculation.

Hydrogel enzymatic degradation test

The hydrogels with fluorescently labeled peptides were digested using a bacterial collagenase solution (0, 0.5, 1, 2 active bacterial collagenase units per ml PBS; cat. no. JS10538; Shanghai Jinsui Bio-Technology Co., Ltd.). The free fluorescence-labeled peptide concentration in solution was determined by fluorescence spectrophotometer to plot a hydrogel degradation release curve. The difference between tested weight on each day and initial weight on the first day was obtained. The degradation rate was calculated by calculating the ratio of the aforementioned difference and the initial weight.

EPC adhesion and proliferation

The EPCs isolated and used in the current study were derived from the rat bone marrow where no vascular ECs are present. EPCs were isolated from rat bone marrow cells, according to a standard procedure (18) and then von Willebrand factor (vWF; forward primer, 5′-GCTCCAGCAAGTTGAAGACC-3′, reverse primer, 5′-GCAAGTCACTGTGTGGCACT-3′), kinase insert domain receptor (KDR; forward primer, 5′-CTTTTGGTAGCGGGATGAAA-3′, reverse primer, 5′-TCCATTGAAATGGGATTGGT-3′), TEK receptor tyrosine kinase (Tek; forward primer, 5′-ACAATCGTGGACGGCTATTC-3′, reverse primer, 5′-AAGGTCTTTAGGGGCTGGAA-3′), CD34 (forward 5′-ACTTCTGTTGCCTCGGAGAA-3′; reverse 5′-ACGGTTGGGTAAGTCTGTGG-3′), CD133 (forward 5′-CCTCTGGTGGGGTATTTCTT-3′; reverse 5′-AGGTGCTGTTCATGTTCTCC-3′), and nitric oxide synthase 3 (eNOS; forward primer, 5′-CACAGGCATCACCAGGAAGAA-3′, reverse primer, 5′-ATACCAGTGGGTCCGAGCA-3′) gene expression were determined by semi-quantitative PCR to confirm the success of EPC isolation (3,19). β-actin (F240; forward primer, 5′-CACGATGGAGGGGCCGGACTCATC-3′ and R240; reverse primer, 5′-TAAAGACCTCTATGCCAACACAGT-3′) was used as the reference gene. The 25 µl PCR reaction system contained 0.5 µl 10 µM forward primer, 0.5 µl 10 µM reverse primer, 2 µl 2.5 mM dNTP (cat. no. D40300A; Takara), 0.25 µl Ex Taq (cat. no. DRR100A; Takara), 2.5 µl 10 fold Ex Taq E buffer, 1 µl cDNA and ddH₂0. The PCR conditions were as follows: Denaturation at 95°C for 4 min, then 35 cycles of denaturation at 95°C for 4 min, annealing at 54°C for 30 sec and extension at 72°C for 25 sec, and a final extension step of 72°C for 4 min. The PCR was conducted on an ABI7900 thermocycler (Applied Biosystems; Thermo Fisher Scientific, Inc.) and products were detected on a 1% agarose gel with 0.5 µg/ml ethidium bromide. Gels were observed with JY02S Gel Imager (Beijing Junyi Electrophoresis Co., Ltd.) and the acquired gel images were processed by Photoshop CS5 (Adobe Systems, Inc.).

To investigate EPC adhesion and proliferation on the hydrogel, EPCs were inoculated on the RGD modified hydrogel surface at a seeding density of 5×10⁴ cells/cm². EPCs were cultivated in the incubator with 5% CO₂ at 37°C in the modified DMEM (Gibco; Thermo Fisher Scientific, Inc.) with 25 U/ml 10% FBS heparin, 2 mmol/l glutamine (both Sigma-Aldrich; Merck KGaA), 20 µg/l VEGF, 10 µg/l bFGF, 10 µg/l leukemia inhibitory factor and 10 µg/l epidermal growth factor (all Peprotech). The growth of EPCs on the hydrogels were observed and counted using inverted phase contrast microscope. Blank RGD-modified hydrogel was used as a control.

MTT assay for cell metabolic activity

MTT assay was used to assess the biocompatibility of hydrogels. In brief, EPC density was adjusted to a concentration of 1×10⁵ cells/ml and 100 µl cell suspension was added to the surface of RGD-modified hydrogels and non-RGD-modified hydrogels. The plates were incubated under standard conditions (37°C; 5% CO₂) overnight. Hydrogels where the cells had been inoculated were carefully removed from the wells. Then 10 µM MTT solution was added to samples to assess the adherent cells and the plates were incubated at 37°C for 4 h. The supernatant was discarded and 100 µl of DMSO was added to each well. The plates were placed on a shaking bed for 10 min. The absorbance was read at 570–595 nm at 0, 4, 12, 24, 48, and 72 h.

EPC culture experiments encapsulated in PEG hydrogel encapsulated with bFGF and VEGF

EPCs were seeded into the hydrogel as previously described (20). The hydrogel was modified according to the previous procedure. The initial EPC seeding density was 5×10⁵/well on a 12-well plate. bFGF and VEGF were added into each well at a concentration of 1.2 ng/well, respectively. MMP-mediated bFGF and VEGF release rates were detected by bFGF and VEGF ELISA kit (cat. no. E-EL-R0091 and E-EL-R0020, respectively; Elabscience Biotechnology Co., Ltd.) with the method adapted from Kraehenbuehl et al (12). For samples for flow cytometry detection, collected cells were first digested by trypsin-EDTA then washed twice with PBS. After being re-suspended with 500 µl binding buffer, 5 ml Annexin V-FITC and 5 µl propidinm iodide were added to the cells. The samples were then kept in dark for 5–15 min at room temperature. Viable cells were detected by flow cytometry with by flow cytometry with Annexin V-FITC Apoptosis kit (cat. no. KG108; Nanjing KeyGen Biotech Co., Ltd.). The percentage analysis was finished on Epics XL-4 Flow Cytometer with System II™ software (version 3.0; both from Beckman Coulter, Inc.).

Reverse transcription-quantitative (RT-q)PCR was performed to determine the expression levels of platelet/endothelial cell adhesion molecule 1 (PECAM1), CD34, KDR, Tek, angiopoietin-2 and protocadherin (pcdh12) genes after 7 days of cultivation. Total RNA from rat EPCs was isolated using TRIzol reagent (cat. no. 15596-018; Invitrogen; Thermo Fisher Scientific, Inc.) and the converted to cDNA with the RevertAid™ First Strand cDNA Synthesis kit (cat. no. K1622; Fermentas; Thermo Fisher Scientific, Inc.) following manufacturer's protocol. The cDNA was diluted 10-fold in double distilled water and the reaction conditions were: 50°C for 2 min, followed by 40 cycles of 95°C for 30 sec and 60°C for 30 sec. qPCRs were conducted on Real PCR machine (ABI7900; Applied Biosystems; Thermo Fisher Scientific, Inc.) using Maxima SYBR-Green/Fluorescein qPCR Master Mix (cat. no. K0241; Fermentas; Thermo Fisher Scientific, Inc.). The reaction system for each gene includes 4 µl 10-fold diluted cDNA of the target gene, 10 µl Maxima SYBR-Green/Fluorescein qPCR Master Mix (2X), 5.2 µl H₂O, 0.4 µl 100 µM forward primer (PECAM1: 5′-ATCAGCACCACCTCGAAATC-3′; CD34; Tek; KDR; angiopoietin-2: 5′-GGCGAGGAGTCCAACTACAG-3′; and pcdh12: 5′-TCTGGTGCTGACTGCCTATG-3′) and 0.4 µl 100 µM reverse primer (PECAM1: 5′-CTTTTTGTCCACGGTCACCT-3′; CD34; Tek; KDR; angiopoietin-2: 5′-AAGTTGGAAGGACCACATGC-3′; and pcdh12: 5′-CACATGCTTGCCAAAGAAGA-3′). β-actin 240 was used as the reference gene. The results were quantified using the 2^−ΔΔCq method (21).

The chick chorioallantoic membrane (CAM) method was adapted from Valdes et al (22) to investigate the function of bFGF and VEGF encapsulated within the hydrogel on angiogenesis by scoring the newly formed angiogenic vessels (23). Chicken embryos (Wuhan Institute of Bioloigcal Products, Co., Ltd.) with similar weights were obtained from fresh fertilized eggs (50±5 g) after they were opened on a cleaned surface without breaking the embryos. Experimental samples were divided into three groups: Control, modified hydrogel without bFGF or VEGF, and modified hydrogel with both bFGF and VEGF. Each group had three biological replicates. The tested hydrogels were carefully placed in an avascular region between two main blood vessels in each chicken embryo. The hydrogels were replaced with fresh gels every three days. After 11 days, angiogenic vessels were counted after the removal of the transparent tested hydrogel, then a 2.5 ml methanol and acetone mixture (equal volume) was added to fix the vessels at room temperature for 20 min. The vessel numbers were counted under a dissecting microscope with a 10-fold magnification (model no. MZFLIII; Leica Microsystems GmbH).

Statistical analysis

All studies had three replicates for every tested group. Statistical analysis was performed using SPSS v20.0 statistical software platform (IBM Corp.). The cell count data was described by the number of cases and examined by Fisher's exact test. Measurement data were expressed as the mean ± standard deviation, comparisons between three groups were analyzed by ANOVA, followed by the Tukey's Honest Significant Difference post hoc test, and Student's t-test was used to compare the two groups. P<0.05 was considered to indicate a statistically significant difference.

Results

Hydrogel degradation profile

PEG hydrogels, which present non-adhesive characteristics to proteins and cells, have been widely used to form a thin coating on the injury site of carotid arteries in vivo (15,24,25). The present results demonstrated that the PEG hydrogels were stable for 6 days, then underwent gradual degradation at a relatively constant rate with ~30% of the gels degraded by 14 days (Fig. 1A). In the enzymatic degradation test, gels were decomposed by bacterial collagenase. The higher the concentration of bacterial collagenase the faster the rate of enzymatic hydrolysis. The hydrogels stored in buffer without collagenase were not decomposed in first 72 h, and the gels kept in the 2 active U/ml collagenase were decomposed by >95% in the first 72 h (Fig. 1B).

Figure 1.

Hydrogel degradation profile. (A) Degradation rate of polyethylene glycol hydrogel over 15 days. (B) Enzymatic hydrolysis rate of different concentrations of collagenase (0, 0.5, 1 and 2 active U/ml) over 72 h.

RGD-modified hydrogel significantly increases EPC adhesion and viability

EPCs were inoculated onto the surface of RGD modified hydrogels at 5×10⁴ cell/cm². The growth of the EPCs and their adhesion to the hydrogel were observed using an inverted phase contrast microscope. The average number of EPCs on the surface of the well in the RGD-modified hydrogel group was significantly higher compared with that of the control group (P<0.001; Table I). In addition, the viability of EPCs on the gels was assessed with the MTT assay. The number of adherent cells was higher in the RGD-modified group compared with the control one (P<0.05). In summary, the RGD-modified PEG hydrogel significantly promoted the adhesion and growth of the EPCs.

Table I.

Endothelial progenitor cell number counted in the wells with polyethylene glycol hydrogel.

Well number	RGD-modified	Non RGD-modified
1	305	34
2	321	42
3	318	49
Mean	314.67	41.67a

^aP<0.05 vs. RGD-modified. RGD, arginylglycylaspartic acid.

Release of bFGF and VEGF from hydrogels

Growth factor-based cell therapies are considered to be potentially curative treatment options (16,26). The main limitation of growth factor application in biomedical therapies is their high diffusibility and short half-life in vivo (16). The present study prepared enzyme-sensitive PEG hydrogels containing RGD using the Michael-type addition reaction method (12). The growth factors bFGF and VEGF were encapsulated in the hydrogel and the concentrations in the supernatant were detected by ELISA every 12 h and compared with standard curves. The standard curves of bFGF and VEGF were drawn by establishing a relationship between actual OD values (the difference between measured OD values and blank OD values) and paired standard concentrations (Fig. 2A and B). The release % of bFGF and VEGF were both maintained at 41% over 72 h (Fig. 2C and D).

Figure 2.

Release of bFGF and VEGF from polyethylene glycol hydrogels up to 148 h. (A) Standard curve of increasing concentrations of bFGF. (B) Standard curve of increasing concentrations of VEGF. (C) bFGF release % over 148 h with addition of MMP-9 (100 and 1,000 ng) at 72 h. (D) VEGF release % over 148 h with addition of MMP-9 (100 and 1,000 ng) at 72 h. *P<0.05 vs. MMP 100 ng group. bFGF, basic fibroblast growth factor; VEGF, vascular endothelial growth factor; MMP, matrix metalloproteinase; OD, optical density.

Following the first 72 h, MMP-2 and MMP-9 were added to the hydrogels. The release % of bFGF and VEGF both increased steadily. At 148 h, >90% of bFGF and VEGF had been released into the supernatant (Fig. 2C and D). In addition, it was determined that the greater the initial MMP-2 and MMP-9 concentration then the higher the growth factor release % (Fig. 2). Results suggested that the MMP-sensitive PEG hydrogels maintained a stable release of bFGF and VEGF.

EPC isolation confirmation by semi-quantitative gene expression

The expression of VWF, KDR, Tek, CD34 and eNOS genes are used to determine isolation of EPCs (27). The present gene expression results visualized by 1.5% agarose gel electrophoresis indicated that EPCs were successfully isolated due to upregulation of the aforementioned genes (Fig. 3).

Figure 3.

Semi-quantitative PCR results for EPC-related gene expression. Gene expression results confirmed the successful isolation of EPCs from rat bone marrow. EPC, endothelial progenitor cells; VWF, von Willebrand factor; KDR, kinase insert domain receptor; Tek, TEK receptor tyrosine kinase; eNOS, nitric oxide synthase 3.

Encapsulation of bFGF and VEGF within hydrogels significantly increases EPC survival rate

Flow cytometry demonstrated that EPC survival rate in hydrogels encapsulated with bFGF and VEGF was 38.69% compared with 4.14% in hydrogels without bFGF and VEGF (P<0.05; Fig. 4). Typically, cells that do not aggregate have a high mortality rate following the first 7 days; however the present results demonstrated that the growth factors promoted EPC cell survival in hydrogels.

Figure 4.

Survival rates of EPCs in PEG hydrogels determined by flow cytometry. (A) PEG hydrogels encapsulated with EPCs, bFGF and VEGF demonstrating 38.69% surival rate. (B) PEG hydrogels encapsulated with EPCs only demonstrating 4.14% surival rate. EPC, endothelial progenitor cells; PEG, polyethylene glycol; bFGF, basic fibroblast growth factor; VEGF, vascular endothelial growth factor; UL, upper left; UR, upper right, LL, lower left; LR, lower right; SSC-H, side scatter height; FSC-H, forward scatter height; FITC, fluorescein isothiocyanate; PI, propidium iodide.

Encapsulation of bFGF and VEGF within hydrogels significantly increases EPC adhesion

The mean number of viable EPCs observed in the hydrogel containing bFGF and VEGF was 378.3 compared with 302.3 in the hydrogels without bFGF and VEGF in hydrogel (P<0.05). Results suggested that the growth factors significantly increased EPC adhesion.

Encapsulation of bFGF and VEGF within hydrogels significantly increases MMP release

The concentrations of both MMP-2 and MMP-9 in the supernatant were significantly higher for the hydrogels encapsulated with growth factors compared with those without them (P<0.05; Fig. 5).

Figure 5.

Effect of bFGF and VEGF encapsulation in polyethylene glycol hydrogels on release of MMPs. (A) Release of MMP-2 and of (B) MMP-9 from hydrogels encapsulated with and without bFGF and VEGF. **P<0.05 vs. control. bFGF, basic fibroblast growth factor; VEGF, vascular endothelial growth factor; MMP, matrix metalloproteinase.

VEGF and bFGF promotes EPC differentiation

Differentiation determines the success of the implanted EPCs in the transplanted tissue. EPCs were incubated in the hydrogels with or without bFGF and VEGF. Following 7 days of culture, RT-qPCR was used to determine the expression of PECAM1, CD34, KDR, Tek, angiopoietin-2 and pcdh12 genes. Results demonstrated that hydrogels encapsulated with bFGF and VEGF had significantly higher PECAM1, CD34, KDR, Tek, angiopoietin-2 and pcdh12 gene expression compared with hydrogels without bFGF and VEGF (P<0.05; Table II). The significant difference in gene expression demonstrated that VEGF and bFGF promoted the differentiation and maturation of EPCs.

Table II.

Endothelial progenitor cell differentiation-associated gene expression.

Group	PECAM1	CD34	KDR	Angio	Tek	Pdch12
With bFGF and VEGF	1.024	1.008	1.032	0.335	1.032	1.014
Without bFGF and VEGF	0.311a	0.266a	0.440a	0.206a	0.175a	0.371a

^aP<0.05 vs. With bFGF and VEGF. The two groups were compared using a paired Student's t-test. bFGF, basic fibroblast growth factor; VEGF, vascular endothelial growth factor; PECAM1, platelet/endothelial cell adhesion molecule 1; KDR, kinase insert domain receptor; Tek, TEK receptor tyrosine kinase; angio, angiopoietin-2; Pdch12, protocadherin.

VEGF and bFGF facilitates the neovascularization process

EPCs form new capillaries via vasculogenesis in the center of the infarct (28). By comparison, other primitive cells, such as hematopoietic stem cells, secrete important growth factors such as VEGF, and stimulate healthy small blood vessel generation in the infarcted marginal zone by angiogenesis through ‘germination’ growth (29,30). Vasculogenesis and angiogenesis work synergistically to establish a new blood supply for the infarction area. In the present study, the CAM assay was used to determine the effect of bFGF and VEGF on angiogenesis induction in vitro. The number of vessels in the hydrogels encapsulated with bFGF and VEGF was significantly higher than the number of vessels in the blank group and hydrogels without bFGF and VEGF encapsulation (P<0.05; Table III). Results indicated that the hydrogel encapsulated with bFGF and VEGF facilitated the neovascularization process, in which both vasculogenesis and angiogenesis are involved.

Table III.

Chick chorioallantoic membrane angiogenesis assay.

Group	Large blood vessels	Medium blood vessels	Small blood vessels	Total
Blank control	1	5	3	9a
PEG hydrogel without bFGF and VEGF	2	7	16	25a
PEG hydrogel with bFGF and VEGF	4	10	26	36

^aP<0.05 vs. PEG hydrogel with bFGF and VEGF. PEG, polyethylene glycol; bFGF, basic fibroblast growth factor; VEGF, vascular endothelial growth factor.

Discussion

The present study designed a MMP-sensitive PEG hydrogel modified with RGD then encapsulated bFGF, VEGF and EPCs within the biomaterial to observe and assess its function as a cell transplantation vector and a release system. Hydrogels have good biocompatibility, high water permeability and can be manufactured to produce different microstructures and properties. Therefore, hydrogels can be applied widely in the biomedical field (31). PEG hydrogels display good biocompatibility, histocompatibility and the chemical structure can be adjusted to meet the needs of different biomedical applications (24,25,32). PEG hydrogels also promote the integration of implant and recipient tissue (33). In the current study, inoculated cells were initially suspended to overcome the uneven cell density and weak adhesion. The release of MMPs from cells gradually degraded the hydrogel therefore cell proliferation and hydrogel degradation had a combined effect. The modified PEG hydrogel system serves an important role in assisting and protecting against the above process. Results indicated that the initial hydrogel structure was maintained for 7 days, which makes it appropriate for a role as a sustained release carrier.

RGD is one of the smallest amino acid sequence recognized by many adherent proteins (8). This sequence binds specifically to cell surface integrin receptors, thereby mediating cell adhesion, migration and growth (34–37). Directly immobilizing RGD to the surface of a material can promote the adhesion of the receptor-mediated cells. In the present study, EPCs were isolated from rat bone marrow cells with this cell source excluding the possibility of contamination from vascular ECs. Semi-quantitative PCR for EPC related markers confirmed successful EPC isolation. Several other robust tools for confirmation of EPC isolation include western blot analysis, phase contrast microscopy and morphological assessment. The average number of EPCs observed on the surface of the RGD-modified hydrogel group was significantly higher compared with the non-RGD modified group. In addition, EPCs were determined to rapidly adhere to the hydrogel with the cells and material forming contacting points. EPCs dispersed radially in the modified hydrogels. The RGD-modified hydrogel significantly increased the adhesion and proliferation of EPCs, which suggested that the presence of RGD significantly promoted biocompatibility.

Many studies have identified VEGF and bFGF as the most important growth factors for therapeutic angiogenesis (12,13). However, maintaining EPC activity and integration with host blood vessels, and ensuring sustained release of vascular growth factor in the wound long-term have not yet been solved in angiogenesis research. Therefore, in the present study, hydrogels were encapsulated with bFGF, VEGF and EPCs to determine the sustained release effect of bFGF and VEGF, and also to observe the culture of EPCs. Following addition of MMP-2 and MMP-9 at 72 h, the release % of bFGF and VEGF increased steadily and reached >95%. These results suggested that the MMP-sensitive PEG hydrogels released bFGF and VEGF in a stable manner. The results also imply that VEGF and bFGF have a synergistic role in the formation of neovascularization. In addition, following 7 days of culture, 38.69% of EPCs survived, suggesting that the modified hydrogels supported EPC proliferation, reduced apoptosis and improved the survival rate.

VEGF and bFGF participate in all aspects of angiogenesis and promote the degradation of capillary basement membrane, facilitate EC proliferation and migration, and the formation of tubular structures (38). This process eventually leads to capillary angiogenesis and microcirculation improvement (39). The effect of bFGF and VEGF on the proliferation, differentiation, maturation and vascularization of EPCs in hydrogels has yet to be fully elucidated therefore the present study investigated encapsulation of EPC and growth factors within a PEG hydrogel. RGD-modified hydrogels encapsulated with VEGF and bFGF displayed ~40% EPCs attachment at 7 days compared with ~4% EPC attachment for RGD hydrogels without VEGF and bFGF. These results suggested that VEGF and bFGF enhanced the adhesion of EPCs, and facilitated the proliferation of EPCs. Gene expression analysis determined that EPC-related gene expression was higher in hydrogels encapsulated with bFGF and VEGF compared with the group without bFGF and VEGF. These results suggested that VEGF and bFGF promoted the differentiation and maturation of EPCs.

There are several cell types suitable for angiogenesis studies, including HUVECs and EPCs. In the present study, EPCs were chosen due to their important roles in both angiogenesis and vasculogenesis, as well as their ability to migrate into the blood system stream and ability to differentiate into a variety of mature vascular EC types. The concentration of VEGF in vitro is positively correlated with the proliferation rate of EPCs (40–43). bFGF can facilitate EC proliferation and migration. When bFGF functions together with VEGF, this synergistic pair promotes the splitting of ECs into capillary-like structures inducing angiogenesis in vivo (44,45). For the present CAM study, new blood vessels grew markedly. The number of blood vessels in the bFGF and VEGF group was significantly higher than the control group. These results suggested that the hydrogels containing bFGF and VEGF induced CAM angiogenesis. Sustained release of bFGF and VEGF is capable of stimulating EC proliferation and budding, but also capable of promoting transplantation of EPCs hyperplasia and vascularization. Transplanted EPCs are able to overcome the limitations of EC aging and dysfunction, indicating that the two components in the hydrogel have a strong synergistic association.

In conclusion, the RGD-modified hydrogel displayed good mechanical properties suitable for a role as a sustained release carrier. The presence of RGD in the hydrogel significantly promoted its biocompatibility as EPC proliferation was supported, apoptosis was reduced and EPC survival rate was improved. In addition, hydrogels encapsulated with VEGF and bFGF enhanced the adhesion of ECs, promoted the production of extracellular matrices and facilitated EPC proliferation. The differentiation and maturation of EPCs were also facilitated in the RGD-modified hydrogels. Furthermore, the hydrogels encapsulated with bFGF and VEGF induced angiogenesis with the two growth factors and EPCs displaying a strong synergy. The present results may provide a potential treatment for soft tissue defects such as bone exposure, chronic skin ulcers, bedsores, limb necrosis, osteonecrosis and other ischemic diseases.

Funding

The present study was supported by the National Key R&D Program of China (grant no. 2017YFC1103800) and Natural Science Fund of Hubei (grant no. 2016CFB657).

Availability of data and materials

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.

Authors' contribution

LO, YD and DD conceived of the current study. LO and YD designed the current study. LO, YD, ZS, GL and SY obtained the relevant data. CY, GL and DD drafted the manuscript. CY revised the manuscript critically for important intellectual content. All authors analyzed and interpreted the data, and also read and approved the final manuscript.

Ethics approval and consent to participate

Protocols involving the use of the animals were approved by the Ethics Committee of Tongji Medical College, Huazhong University of Science and Technology (2016 IACUC Number: S782). Animal experiments were performed in accordance with the Guide for the Care and Use of Laboratory Animals.

Patient consent for publication

Not applicable.

Competing interests

The authors declare that they have no competing interests.