Abstract
For efficient water splitting, it is essential to develop inexpensive and super-efficient electrocatalysts for the oxygen evolution reaction (OER). Herein, we report a phosphate-based electrocatalyst [Fe3Co(PO4)4@reduced-graphene-oxide(rGO)] showing outstanding OER performance (much higher than state-of-the-art Ir/C catalysts), the design of which was aided by first-principles calculations. This electrocatalyst displays low overpotential (237 mV at high current density 100 mA cm−2 in 1 M KOH), high turnover frequency (TOF: 0.54 s−1), high Faradaic efficiency (98%), and long-term durability. Its remarkable performance is ascribed to the optimal free energy for OER at Fe sites and efficient mass/charge transfer. When a Fe3Co(PO4)4@rGO anodic electrode is integrated with a Pt/C cathodic electrode, the electrolyzer requires only 1.45 V to achieve 10 mA cm−2 for whole water splitting in 1 M KOH (1.39 V in 6 M KOH), which is much smaller than commercial Ir-C//Pt-C electrocatalysts. This cost-effective powerful oxygen production material with carbon-supporting substrates offers great promise for water splitting.
Subject terms: Catalyst synthesis, Electrocatalysis, Graphene
The sluggish kinetics of the oxygen evolution reaction (OER) is the main obstacle in water splitting which is generally catalyzed by precious metals. Here, authors report a DFT predicted non-precious bimetallic phosphate electrocatalyst that displays high OER activity and stability.
Introduction
The oxygen evolution reaction (OER) is a fundamental reaction in electrochemical energy conversion process, which is the basis of water splitting, batteries, and photoelectrochemical cells1–3. The water splitting is considered as a promising and renewable method for producing hydrogen and oxygen gases4–7. However, the efficiency of water splitting in basic electrolyte is largely hindered by sluggish kinetics of the oxidative half-cell OER reaction2,7 and so commercial water splitting usually works at a high voltage of 1.8–2.0 V8. Recently, noble metal-based compounds such as IrO2 and RuO2 exhibit good catalytic activities toward OER9,10. However, the widespread practical application of these noble metal-based compounds is restricted due to their skyrocketing price and scarcity5,9. Therefore, the development of cost-effective catalysts with high electrocatalytic activity and stability for OER is in high demand, which would lead to a cost-effective production of oxygen via water splitting. In this regard, inexpensive earth-abundant transition metal-based OER electrocatalysts would be a good choice not only because of their high abundance and low cost but also due to their high electrocatalytic activity and stability in wide pH ranges11–13.
Over the past decade, transition metal-based OER electrocatalysts (for instance, cobalt phosphate, surface-oxidized steels, NiFe-layered double hydroxide/nickel foam, oxy-hydroxides, oxide, perovskites, cobalt phosphate composites, and Co3O4, etc.) have been explored due to their high potential for water oxidation, high durability under basic condition, and their benign environmental nature5,7–9,12–14. Nevertheless, these materials exhibit large overpotential (η) for OER5,7–9. Therefore, effective designing of state-of-the-art electrocatalyst and clear understanding of OER catalytic mechanism remain challenging tasks.
Herein, we report a phosphate-based electrocatalyst of Fe3Co(PO4)4/reduced-graphene-oxide (rGO) (1) for OER, which is predicted to be highly active by density functional theory (DFT). The as-synthesized 1 indeed serves as a highly active electrocatalyst for OER in basic media with overpotential of ~237 mV at 100 mA cm−2, and long-term durability (5000 cycles). On the basis of theoretical modeling and experimental observations, the high OER activity of the designed electrocatalyst is ascribed to the PO4-induced positive shift of the redox potential. The efficient mass and charge transfer due to defects/dislocations in the PO4-induced mix phase and large Brunauer–Emmett–Teller (BET) surface area also help in the OER activity. When it was integrated into asymmetric two-electrode water-splitting cells, the electrolyzer required a potential ~1.45 V in 1 M KOH (or ~1.39 V in 6 M KOH), to drive a current density of 10 mA cm−2 for whole water splitting, which is much smaller than that of the integrated commercial Ir-C//Pt-C electrocatalysts (~1.53 V in 1 M KOH).
Results and discussion
Theoretical model
Inexpensive Fe and Co hybrids with inorganic species (such as P or O) can show good OER performance15–17 in that the covalent strength of Fe/Co-X in a Fe/Co-X-Y linkage is controlled by the inductive effect16. Positive shift of the redox potential for transition metal oxide catalysts can lead to high catalytic effect18. In consideration of the inductive effect, we have considered various phosphorus oxides PxOy as a better alternative for P/O. Given that O is highly electronegative, substituting O with phosphate would be a good choice for OER. Thus, tuning the catalytic effect would be possible by substituting O with phosphate and further fine-tuning by optimizing the Fe/Co ratio. In many cases, Fe and Co behave similarly with similar ionization potentials EIP(Fe/Co) = 7.87/7.86 eV but they show a large difference in valence electron configurations [Ar]3d64s2/[Ar]3d74s2 and electron affinities EEA(Fe/Co) = 0.15/0.66 eV. Therefore, their cations with varying Fe/Co ratio give different electrochemical properties with different induction effects. This led us to theoretically investigate the OER performance of stable cage structures of FemCo8-mO12 (m = 0,2,4,6,8) and FenCo4-n(PO4)4 (n = 0–4) (Fig. 1a) at varying compositions of Fe and Co (a few varying Fe/Co ratios of 4/0, 3/1, 2/2, 1/3, and 0/4). DFT calculations were performed to understand their electronic structure (Supplementary Figs. 1–4) and *O/*OH free energies (ΔGO/ΔGOH) and theoretical overpotentials (ηtheory) required for OER (Fig. 1) at various compositions (Supplementary Table 1), where * denotes an active site. We found that the metal substrate of rGO, although significantly beneficial for durability and conductivity (Supplementary Fig. 5), does not give significant effects on H-adsorption energies of FenCo4-n(PO4)4 (n = 0–4). To study the catalytic effect, here we have focused on the most stable (010) surface of FenCo4-n(PO4)4 (Supplementary Table 2) rather than FenCo4-n(PO4)4@rGO for the realistic model.
The optimal catalytic activity is found from the Fe/Co ratio of 3 for the FenCo4-n(PO4)4 models of clusters and (010) surfaces. For Fe/Co mixed-metal phosphates, the ηtheory at Fe sites is the smallest at n = 3, i.e., Fe3Co(PO4)4, whereas the ηtheory of Co sites is not small, remaining almost same for n = 0–4 (Supplementary Table 1). In the FemCo8-mO12 (m = 0,2,4,6,8) model, the substitution effect of Co for Fe improves the ηtheory at Fe sites but not at Co sites. Thus, in both models, a small amount of Co that substitutes Fe is effective on Fe sites but not so on Co sites, and the optimized Fe/Co ratio at Fe sites in FenCo4-n(PO4)4 is 3. The binding energies of intermediate states at Fe sites become weaker if they are surrounded by many Co atoms. As a result, those local Fe sites become less active. The Fe sites of Fe3Co(PO4)4 are predicted to show excellent activity with ηtheory = 0.24 V. The Fe and Co sites are tri-coordinated in clusters and penta-coordinated in (010) surfaces. The binding energies of intermediate states become weaker on the penta-coordinated Fe sites constantly (by ~0.5 eV) than on the tri-coordinated Fe sites. Yet, their free-energy changes between O-adsorption and OH-adsorption (ΔGO − ΔGOH) behave similarly, except for this constant difference, and so their overpotentials are similar in both models. It seems that the binding energies of all the intermediate states also become weaker at more coordinated sites on surfaces by almost the same magnitude (~0.5 eV) than on clusters.
To sum up, the electronic structure calculations reveal that the phosphate and the Fe/Co ratio (optimal value of 3/1) are important in tuning the redox potential. As compared with Fe3CoO6 (0001), the phosphate group in Fe3Co(PO4)4 (010) lowers the metal oxide antibonding state and positively shifts the redox potential with the inductive effect (Supplementary Fig. 1). As Co (which is slightly more electronegative than Fe) pulls down the metal oxide antibonding state energy levels and thereby positively shifts the redox potential (Supplementary Fig. 2), tuning the Fe/Co ratio can be exploited for better OER performance.
DFT calculations show that 1 exhibits the optimal ΔGO − ΔGOH free energy (Fig. 1a). At the O-adsorbed metal sites of 1, the bond strength between Fe/Co 3d and O 2p orbitals becomes weaker than at those of Fe6Co2O12 (Supplementary Fig. 3). Thus, we investigate the energetics of all intermediates (OH, O, OOH adsorption) and evaluate the theoretical overpotentials for OER (ηtheory) of catalyst FeCo3(PO4)4 (010) and clusters of Fe3Co(PO4)4, FeCo3(PO4)4, Fe6Co2O12, and Fe2Co6O12 (Fig. 1). Iron-cobalt oxide clusters are also studied to understand their ratio effect on catalytic activity. We calculate ηtheory for the FeCo3(PO4)4 cluster and FeCo3(PO4)4 (010) surface models, and other cases with different Fe/Co ratios. The ηtheory at Co site of FeCo3(PO4)4 (010) is 0.49 V, which is larger than the ηtheory by 0.24 V at Fe site of Fe3Co(PO4)4. The Fe site in the Fe3Co(PO4)4 (010) has a lower ΔG2 value (1.47 V) than that of the Co site (1.76 V). The improvement in ηtheory at the Fe site in 1 over other considered composites is attributed to optimal ΔGO − ΔGOH by weakend *O and *OH binding at the Fe site, whereas the same change of *O and *OH binding at Co sites affects the OER reaction only moderately (Fig. 1b,c, Supplementary Fig. 4, and Supplementary Table 1). Overall, our computation shows that 1 reduces the energy barriers for every step, thereby lowering the free energies of each elementary reaction step (Fig. 1b, c and Supplementary Table 1).
Synthesis and characterization
In light of above findings, we synthesized three catalysts of [1: (Fe3Co(PO4)4@rGO), 2: (Fe1-1.33Co(PO4)2@rGO) (or FeCo(PO4)2@rGO), and 3: (Fe1.5-2Co(PO4)3@rGO) (or Fe2Co(PO4)3@rGO)] with a one‐pot temperature‐programmed carbonization process (Fig. 2a and Methods). As 1 shows the best activity, we will focus our discussion on 1, unless otherwise specified.
The scanning electron microscopy (SEM) and low-resolution transmission electron microscopy (TEM) images of 1 show that Fe3Co(PO4)4 nanoparticles (NPs) are uniformly distributed on the rGO surface with diameters 50–70 nm (Fig. 2b). The high-resolution TEM (HRTEM) and fast Fourier transform (FT) images reveal that the Fe3Co(PO4)4 NPs are crystalline (Fig. 2c). The HRTEM images show d-spacing values of 2.98 Å, corresponding to the {020} planes for the Fe3Co(PO4)4 crystal. Plane defects and atomic dislocations (yellow dots in Fig. 2c) enhance the specific area and the electrocatalytic site for further boosting the OER activity. In addition, high-angle annular-dark-field scanning TEM (HAADF–STEM) energy-dispersive spectroscopy mapping was used to examine the elements distribution in Fe3Co(PO4)4@rGO (Fig. 2d). Composition line-scan profiles across an NP of 1 shows that Fe/Co/P elements are distributed throughout the NP (Fig. 2e). The X-ray diffraction (XRD) patterns of 1 show the peaks at 20.3°, 30.3°, 48.52°, and 52.1° (marked as “▼”) corresponding to {101}, {020}, {220}, and {222̅} crystal planes, respectively, for a monoclinic Fe3Co(PO4)4 crystal (space group: Pm) (Fig. 2f and Supplementary Fig. 6). In addition, the {020} peak has the maximum intensity, indicating that the c-axis [010] is the growth direction of Fe3Co(PO4)4 crystal. Both theoretical and experimental patterns are quite similar; however, few peaks slightly blue-shifted in experiment, indicating the volume expansion with increased lattice spacing (due to phosphate intercalation) and crystal defects/dislocations (due to strain effect during the metal cations formation). These observations are in good agreement with the HRTEM results as discussed earlier. The expanded curves of Fe3Co(PO4)4@rGO show a broad band at 26.3° (marked as “♦”) corresponding to the (002) plane of rGO, indicating the successful reduction of GO and the formation of graphitic structures with interlayer spacing of 0.34 nm19–21. A few small unmatched diffraction peaks, such as 35‒39°, 41‒42°, 55‒60°, and 63‒80°, are not clear to us, because there can be so many possible structures in small quantities, but may be resulted from a byproduct adduct Fe4.1Co2.9(PO4)6, mono-metallic iron, or cobalt phosphate during the one-pot temperature-programmed carbonization process (Supplementary Fig. 6). However, it is clear that they are not a significant issue, because all experimental results are well explained by our theoretical models.
We conducted FT X-ray absorption fine structure (FT–EXAFS) analysis, which provided the chemical state and coordination environments22–25. The energies of both XANES Fe K-edges and Co K-edges of 1 and FeCo(PO4)2@rGO (2) are positively shifted compared with those of Fe/Co foils (Fig. 3a, d), suggesting the oxidized states of Fe/Co. The FT–EXAFS data of Fe and Co in 1 and 2 exhibit similar peak patterns, but the peak intensities and positions are slightly changed due to their different compositions. Meanwhile, Fe and Co foils show different peak positions for Fe–Fe and Co–Co bonds (Fig. 3b, e). We analyzed the EXAFS curve of 1 using least-square fit for first and second shells. Figure 3c (and Supplementary Fig. 7a) show that the major peaks at 2.0 Å (coordination number (CN): 4.1) and 2.2 Å (CN: 1.9) reflect Fe = O and Fe–O bond distances, while the minor peak reflects the overlapped peaks at Fe…P distances (via O) of 2.9/3.1/3.3 Å (CN: 1.6/1/2.4, respectively) (Supplementary Table 3). Similarly, Fig. 3f and Supplementary Fig. 7b show peaks at 2.0 Å (CN: 2) and 2.4 Å (CN: 4) for Co = O and Co–O bond distances, while a major peak at 2.8 Å (CN: 5) for the Co…P distance via O (Supplementary Table 4).
We calculated theoretical Fe and Co K-edge EXAFS of Fe3Co(PO4)4 using the FDMX package26,27. These theoretical FT–EXAFS spectra of the Co and Fe atoms are similar to the experimental FT–EXAFS spectra of 1 in r-space (Supplementary Fig. 8 and Fig. 3c, f). It seems that the difference between Fe and Co K-edge EXAFS of 1 arises from different Fe-P distances at each Fe sites in the crystal (Supplementary Tables 3 and 4). To confirm this, we calculated EXAFS of pure Fe4(PO4)4 and Co4(PO4)4, where the Co K-edge FT–EXAFS spectra of Co4(PO4)4 are similar to the Fe K-edge FT–EXAFS in r-space. This indicates that Co atoms well replace Fe sites in the Fe3Co(PO4)4 lattice.
The core level P-2p X-ray photoelectron spectroscopy (XPS) shows two major peaks at binding energies of 133.2 ± 0.1 and 134.1 ± 0.1 eV, corresponding to the 2p3/2 and 2p1/2 core levels of central phosphorus atoms in phosphate species28, respectively, which is characteristic of the tetrahedral (PO4) group29 (Supplementary Fig. 9a). Furthermore, the O-1s XPS spectra show two peaks at 531.4 and 532.5 eV, assigned to phosphate species30 (Supplementary Fig. 9b). The atomic ratio of Fe/Co are 3/1 or 3.1/1, as measured by inductively coupled plasma atomic-emission spectroscopy (ICP-AES) (Supplementary Table 5). In addition, XPS analysis provides the atomic percentage near the sample surface. As compared with ICP-AES bulk sample analysis, the XPS surface analysis increases the Fe(PO4) content, whereas the atomic content of P (or PO4) is almost the sum of Co and Fe atomic contents, indicating the charges of Co and Fe are +3 (Supplementary Table 6). The content of O is slightly larger than four times of the content of P due to environmental oxygen. An extra content of Fe(PO4), as noted from XPS over ICP-AES, could be present on the surface more than in bulk. However, the XPS data are not so reliable for accurate composition analysis as compared with ICP-AES. The Fe/Co metals composition ratio from ICP-AES is more reliable. Overall, the elemental composition turns out to be 1: Fe3Co(PO4)4@rGO (Fe/Co = 3), 2: FeCo(PO4)2@rGO (Fe4Co3(PO4)7@rGO) (Fe/Co = 1–1.33), and 3: Fe2Co(PO4)3@rGO (or Fe3Co2(PO4)5@rGO) (Fe/Co = 1.5–2). To facilitate our discussion, 2 and 3 will be simply denoted as 2: FeCo(PO4)2@rGO and 3: Fe2Co(PO4)3@rGO in consideration with the experimental component analysis.
Electrochemical performance
We performed electrochemical measurements to check the catalytic activities of catalysts 1–9 and commercial 20 wt% Ir/C for OER in 1 M KOH electrolyte (Fig. 4a and Supplementary Figs. 10–12). The OER activity of these electrocatalysts are influenced by the amount of Fe or Co in the presence of phosphate and the best activity is achieved for 1. Compound 1 exhibits very small overpotential of ~237 mV to afford a current density of 100 mA cm−2, lower than catalysts 2–9 and Ir/C (Fig. 4a and Supplementary Figs. 10–12), and other catalysts with a carbon-supporting substrate including the benchmark Ir/C catalyst (303 mV). This activity is found to be among the best OER-active catalysts (Supplementary Table 8) among which some catalysts of pure metals without the carbon-supporting substrate31–33 do not show high stability (<10 h at 10 mA cm−2), except for the special case of core-shell FeNiCu, which shows a promising result with high stability at low overpotential34. Nevertheless, in most cases the industrial application still requires carbon substrates.
The TOF35,36 is calculated to be 0.54 s−1 at an overpotential of 237 mV, indicating a highly active catalyst, 7.6 times that of Ir/C 0.071 s−1 (details in Methods), which further confirms the outstanding OER performance of 1. The Tafel slope is 57 mV per decade (Fig. 4b), smaller than that of Ir/C (117 mV per decade). The small overpotential at Fe sites of 1 is the key factor for the superior OER activity of 1. For achieving this optimal overpotential, other environmental factors have also been utilized as follows. The large BET surface area (238 m2/g) (Supplementary Fig. 13) with an average pore size 4.3 nm promotes the contact between 1 and an electrolyte, thereby helping in the optimal OER activity. The very low charge-transfer resistance (0.29 Ω on a nickel foam (NF) substrate, 7.5 Ω on glassy carbon electrode (GCE) substrate) promotes electron transport, thereby leading to faster kinetics (Supplementary Fig. 14a, b). The electrochemical double-layer capacitance (Cdl = 0.0162F), which is directly correlated to the catalyst’s active surface area, is very large, 8.1-fold the Cdl of Ir/C (0.002F) (Supplementary Fig. 15). The defects/dislocations (strain effect)37–39 of Fe and Co atoms in crystal help in improving the performance of active sites.
After initial and 5000 cyclic voltammogram (CV) cycles, accelerated degradation test of 1 indicates the excellent durability as demonstrated by the near overlay of OER curves (Fig. 4c). No significant changes in TEM, EDX (energy-dispersive X-ray spectroscopy), HRTEM, hard/soft XAS, XPS, and Raman spectra (except for minor increase in FeOx/FeOOH and CoOx/CoOOH40–42, which would not be so active such as Fe sites of 1, Supplementary Fig. 16) were observed before and after the test, indicating that 1 is quite durable (Supplementary Figs. 17–23). The stability of this catalyst was further assessed by chronoamperometry (CA). Compound 1 exhibited outstanding stability with no changes in current density of ~10–11 mA cm−2 (70 h on NF and 55 h on GCE) and ~210 mA cm−2 (for 45 h on NF) ((Fig. 4d and Supplementary Fig. 24). The high stability and durability of nanocrystal in 1 is ascribed to the graphene support (which is very stable in alkaline and acid media) and the strong coordination between Fe/Co and PO4. Initially and 54 h after the stability test, the Faradaic efficiency (after 1 h test) is ~98 and ~96% in alkaline electrolyte, respectively (Methods).
To evaluate the real application, an overall water-splitting cell was fabricated in which 1 M/6 M KOH was used as electrolyte and 1 served as the anode with 20 wt% Pt/C catalyst as the cathode. It required ~1.45 V in 1 M KOH (1.39 V in 6 M KOH) to facilitate overall water splitting at a current density of 10 mA cm−2 (Fig. 4e, Supplementary Fig. 25, and Supplementary Video 1), which is the lowest voltage, much lower than that of the benchmark combination (1.53 V; commercial Pt/C and Ir/C catalysts). It required nominal voltage of 1.4 V to drive overall water splitting (Supplementary Fig. 26).
We report the SEM, TEM, HRTEM, and EDX images of catalysts 2: FeCo(PO4)2@rGO] and 3: Fe2Co(PO4)3@rGO] in Supplementary Figs. 27 and 28, and Supplementary Note 2. The structural and compositional characterizations of 2, 3, and 5–9 (XRD and XPS) are also provided in Supplementary Figs. 29–37.
Finally, for further optimization of catalysts, one may explore some other PxOy instead of PO4. Further elucidation of the clear origin for the optimal Fe/Co ratio would help in future design of other metal cations electrocatalysts.
In summary, we synthesized 1 and systematically evaluated their OER catalytic activities in alkaline conditions. This hybrid exhibited excellent OER catalytic activities (very low overpotential of 237 mV at high current density 100 mA cm−2) and outstanding stabilities, which is superior to that of the benchmark Ir/C. The remarkable performance is attributed to the PO4 groups, which reduce free-energy barrier for OER at Fe and Co sites, and increase mass/charge transfer arising from defects/dislocation in the PO4-induced mix phase. As a full water splitting, we fabricated an electrolyzer with this hybrid catalyst in alkaline condition, which afforded a current density of 10 mA cm−2 with ~1.45 V in 1 M KOH (~1.39 V in 6 M KOH). This work demonstrates the potential of large-scale structure-engineering towards low-cost, earth-abundant, and high-performance water splitting for energy applications.
Methods
Chemicals
Cobalt(II) perchlorate hexahydrate, iron (III) chloride (reagent grade, 97%), red phosphorus (reagent grade, 99.99%), 5 wt% of Nafion, and perchloric acid were purchased from Sigma-Aldrich. Benchmark 20 wt% Ir/C (commercial) and 20 wt% Pt/C (commercial) catalysts were purchased from Johnson Matthey and Premetek, Co. All the chemicals were of analytical grade and were used as received without further purification.
Synthetic procedure
In synthesis, 200 mg of graphene oxide (GO) and 70 mg of red phosphorus with different weight ratios of iron chloride (FeCl3) to cobalt perchlorate hexahydrate Co(ClO4)2.6H2O were used as starting materials. During the synthesis process, 200 mg of GO was dispersed in 100 mL double distilled water by sonication. The precursors’ weight ratios were chosen as 0.70 g FeCl3, 0.35 g Co(ClO4)2.6H2O, and 0.07 g red phosphorus for 1 [1: Fe3Co (PO4)4@rGO], 0.6 g FeCl3, 0.45 g Co(ClO4)2.6H2O, and 0.07 g red phosphorus for 2 [2: Fe1-1.33Co(PO4)2@rGO or FeCo(PO4)2@rGO], and 0.65 g FeCl3, 0.4 g Co(ClO4)2.6H2O, and 0.07 g red phosphorus for 3 [3: Fe1.5-2Co(PO4)4@rGO or Fe2Co(PO4)4@rGO]. The resulting solutions were sonicated for 10 h to obtain fine homogeneous mixture. The mixture was then dried and thoroughly ground. The ground powder was annealed at 750 °C for 3 h with a temperature ramping rate of 3 °C min−1 in nitrogen atmosphere. To remove the inactive species, the obtained product was leached with 0.1 M HClO4 for 10 h, then filtered and washed with ethanol and water, and finally dried in vacuum at 60 °C. For the synthesis of 4 and 5 (4: Fe2P2O7@rGO, 5: (CoFe2O4)(Fe2O3)@rGO), the same method was employed using 0.70 g FeCl3 and 0.07 mg red phosphorus for 4, and 0.70 g FeCl3 and 0.35 g Co(ClO4)2.6H2O for 5. To study the effect of GO and red phosphorous on the OER performance, we have synthesized catalysts with different amount of GO and red phosphorous such as 6 [6: 0.7 g FeCl3, 0.35 g Co(ClO4)2.6H2O, 100 mg GO, and 0.07 g red phosphorus], 7 [7: 0.7 g FeCl3, 0.35 g Co(ClO4)2.6H2O, 300 mg GO, and 0.07 g red phosphorus], 8 [8: 0.7 g FeCl3, 0.35 g Co(ClO4)2.6H2O, 200 mg GO, and 0.035 g red phosphorus], and 9 [9: 0.7 g FeCl3, 0.35 g Co(ClO4)2.6H2O, 200 mg GO, and 0.140 g red phosphorus]. The C and P contents obtained from XPS analysis in catalysts 6–9 are shown in Supplementary Table 7.
Characterization techniques
The cold field-emission SEM images were taken using Hitachi High-Technologies S-4800 microscope. TEM and HRTEM images and HAADF–STEM images were taken on JEM-2100F with 200 kV acceleration voltage. XPS data were carried out on K-alpha (Thermo Fisher, UK) system. The surface area, pore size distribution, and pore volume with N2 adsorption/desorption isotherms from BET technique were measured on BELSORP-miniII (BEL Japan, Inc.) system. The atomic and weight percent of metals and non-metals in each synthesized catalyst were obtained with ICP-AES (700-ES, Varian) and XPS. EXAFS analysis was performed on ionization detectors at the Pohang Accelerator Laboratory (PAL). The X-ray absorption spectra for the Fe K-edge and Co K-edge were acquired at room temperature using beamlines 6D and 10C (PAL), where their X-ray energies from EXAFS analysis were calibrated with Fe-foil and Co-foil, respectively. Background subtraction, normalization, and FT were done by standard procedure with ATHENA program43. The extracted EXAFS signal, χ(r) and k3χ(k) were analyzed for all three metals. The Artemis program was used for EXAFS fitting. Soft XAS measurements were performed at the soft X-ray 10D XAS KIST beamline operating at 3.0 GeV with a maximum storage current of 360 mA. XAS spectra for Fe and Co L3,2-edge were collected in the total electron yield mode at room temperature in vacuum of ~1.5 × 10−8 Torr. All the spectra were background subtracted and normalized with respect to the incident photon flux measured by inserting a gold (Au) mesh in the path of the X-ray beam.
Electrochemical characterization
All electrochemical measurements were performed on VSP instrument (BioLogic Science Instruments, Inc.) with three-electrode setup using graphite rod and Hg/HgO as a counter and reference electrodes, respectively. The working electrodes in our experiment were GCE (0.0706 cm2) and NF with a geometric area of 3 cm2. For working electrode preparation, 1 mg cm−2 loading amount of the catalyst was achieved through a drop casting method. To ensure the H2O/O2 equilibrium during the electrochemical measurement for OER, the electrolyte (1 M KOH) was saturated with a continuous flow of oxygen for 20 min. For stabilizing the working electrodes, the CVs were first conducted at a sweep rate of 100 mV s−1 in the potential range of 1.1–1.7 V vs. reversible hydrogen electrode (RHE). The linear sweep voltammograms test were performed at a scan rate of 5 mV s−1 with 100% iR compensation, which was automatically derived from the electrochemical workstation. The cycling durability test was carried out at a scan rate of 100 mV s−1 for 5000 CV cycles in the potential range of 1.2–1.6 V vs. RHE. CA responses were performed on both GC (for 55 h) and NF (for 70 h) substrates at potentials on which the current densities reached to the range of 10 mA cm−2. To evaluate the durability of 1 for high current density generation, the CA response were performed on NF substrate at a current density of ~210 mA cm−2 for 45 h. All the CA response were performed without iR compensation. Polarization curves obtained before and after the durability CV cycles were collected for comparison. The current density (mA cm−2) was normalized to the electrode geometrical area and the potentials recorded vs. Hg/HgO (1 M NaOH) were converted to RHE according to the reference electrode calibration value (Supplementary Note 1 and Supplementary Fig. 38). For double-layer capacitance (Cdl) measurements, the potential in a non-Faradic region (1.059–1.174 V vs. RHE) were cycled at a different applied scan rate of 10, 20, 30, 40, and 50 mV s−1. The current from CV curves was plotted vs. applied scan rate at a potential of 1.125 V and the slope obtained from the straight line of current and scan rate were assigned to Cdl. The electrochemical impedance spectroscopy (EIS) was performed at an overpotential of 0.30 V vs. RHE in a frequency range of 100 kHz to 0.01 Hz with a modulation amplitude of 10 mV in 1 M KOH solution. The full water splitting was measured in a two-electrode setup with 1 as an OER electrode and Pt/C as a HER catalyst in 1 M KOH (the catalyst loading was 1.5 mg cm−2) and 6 M KOH (the catalyst loading was 5 mg cm−2) solutions.
The Tafel plots and slopes were calculated according to the Eq. (1):
1 |
where η, j, b, and C represent overpotential, current density, Tafel slope, and intercept, respectively.
The overpotential was calculated according to the Eq. (2):
2 |
TOF of catalyst: The number of oxygen turnovers was calculated from the current density using the Eq. (3)35:
3 |
The number of Fe and Co ions in 1 was obtained from the ICP analysis ~28.9 wt%. Consequently, the density of active sites based on bulk Fe and Co is:
The TOF of the catalyst at an overpotential of 237 mV (current density 100 mA cm−2) was calculated as:
Faradaic efficiency: Faradaic efficiency was calculated using the Eq. (4):
4 |
The theoretical amount of O2 gas was calculated from Faraday’s law Eq. (5):
5 |
where n is the number of mol, I is the current in ampere, t is the time in seconds, z is the transfer of electrons (for O2 z = 4), and F is the Faraday constant (96,485 C mol−1).
The theoretical amount of O2 gas before stability = 19.52 µmol.
The theoretical amount of O2 gas after stability = 19.00 µmol.
The experimental amount of O2 gas was evaluated from the water displacement method using the following protocol:
In our calculations, the pressure is converted into units of an atmosphere by Dalton’s law of partial pressure Eq. (6):
6 |
At ambient conditions, the vapor pressure of water is 21.1 mm Hg (this valve was chosen from vapor pressure table).
The pressure in our calculations with respect to one atmosphere was:
Finally, the number of mol oxygen gas produced in water displacement is calculated by the Eq. (7):
7 |
V is the volume of produced gas in liters, T is the temperature in kelvin, and R is the ideal gas constant (0.0821 L atm/mol K).
The number of moles oxygen gas produced in water displacement before the stability:
The number of mol oxygen gas produced in water displacement after the stability:
Faradaic efficiency before stability.
Faradaic efficiency after stability.
The Faradaic efficiency before stability was 98%, whereas it was 96% after the 54 h of chronoamperometric stability test.
Computational method: Spin-polarized calculations were performed to obtain ground DFT energies of FemCo8-mO12 (m = 0,2,4,6,8) clusters, FenCo4-n(PO4)4 (n = 0–4) clusters, and FenCo4-n(PO4)4 (010) surfaces using Vienna ab initio simulation package44 with projected augmented wave functional45,46. The exchange-correlation potential was corrected by Perdew, Burke, and Ernzerhof (PBE)47 for generalized gradient approximation with Tkatchenko–Scheffler48 (TS) dispersion correction (PBE + TS). For structure optimization, a 2 × 2 k-grid (1 × 1 k-grid for clusters) was used to sample the first Brillouin zone and the cut-off energy was set to 500 eV. Self-consistent field calculations were used to optimize electronic and ionic steps until the energy difference between two successive steps becomes 0.01 meV and the force constant on each ion reaches to 0.02 eV Å−1. Calculations were optimized with spin-polarized method, resulting in the high-spin ferromagnetic configuration for FenCo4-n(PO4)4 (010) surfaces (Supplementary Table 9) and the most stable magnetic configuration was also considered for clusters models. These ferromagnetic configurations are in agreement with the experimentally verified ferromagnetic magnetic materials of catalysts 1–3.
The Gibbs free-energy changes (ΔG) for OER mechanism in alkaline environment are as follows (equations 8–11):
8 |
9 |
10 |
11 |
where ∆GO, ∆GOH, and ∆GOOH are the Gibbs free energies of *O, *OH, and *OOH intermediate reactions, respectively. Corrections to the Gibbs free energies were adopted from ref. 13. Theoretical overpotentials of all considered structures were calculated at the given pH by the following equation49,50: ηtheory = max[∆G1, ∆G2, ∆G3, ∆G4]/e − 1.23 [V], whereas the pH effect is canceled out in evaluating the overpotential.
Supplementary information
Acknowledgements
This work was supported by NRF (National Honor Scientist Program: 2010-0020414) and KISTI (KSC-2018-CRE-0077, KSC-2018-CHA-0057, KSC-2019-CRE-0103, KSC-2018-CRE-0071, KSC-2019-CRE-0139, KSC-2018-CRE-0044, and KSC-2019-CRE-0021). The EXAFS, hard XAS, and soft XAS experiments were performed in Pohang Accelerator Lab beamline (6D C&S UNIST-PAL, 10C-wide XAFS-PAL, and 10D XAS KIST-PAL).
Author contributions
S.S. performed synthesis, electrochemical measurements, and characterization. M.H., D.Y.K., and C.W.M. performed calculations, analyzed experimental EXAFS/XAS/XRD data, and elucidated the material structures, active sites, and OER mechanism. J.N.T. planned the experiment and performed electrochemical measurements and characterization. S.S. and T.J.S. obtained hard XAS data. K.H.C. obtained soft XAS data. A.M. helped in materials characterization. S.S., M.H., D.Y.K., J.N.T., C.W.M., and K.S.K. wrote the manuscript. K.S.K. supervised the project.
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request. The source data underlying Figs. 1a, c, 2e, f, 3a–f, and 4a, c–e, and Supplementary Figs. 6a, b, 7a, b, 9a, b, 10, 11a, 12a, b, 13a, b, 19a, b, 20a–c, 21a–d, 22a–d, 23, 24a, b, 29, and 30–37 are provided as a Source Data file.
Competing interests
The authors declare no competing interests.
Footnotes
Peer review information Nature Communications thanks the anonymous reviewers for their contributions to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
These authors contributed equally:Siraj Sultan, Miran Ha, Dong Yeon Kim.
Contributor Information
Jitendra N. Tiwari, Email: jitendra@unist.ac.kr
Chang Woo Myung, Email: cwmyung@unist.ac.kr.
Kwang S. Kim, Email: kimks@unist.ac.kr
Supplementary information
Supplementary information is available for this paper at 10.1038/s41467-019-13050-3.
References
- 1.Park J, et al. Hollow nanoparticles as emerging electrocatalysts for renewable energy conversion reactions. Chem. Soc. Rev. 2018;47:8173–8202. doi: 10.1039/C8CS00336J. [DOI] [PubMed] [Google Scholar]
- 2.Roy C, et al. Impact of nanoparticle size and lattice oxygen on water oxidation on NiFeOxHy. Nat. Catal. 2018;1:820–829. doi: 10.1038/s41929-018-0162-x. [DOI] [Google Scholar]
- 3.Guan J, et al. Water oxidation on a mononuclear manganese heterogeneous catalyst. Nat. Catal. 2018;1:870–877. doi: 10.1038/s41929-018-0158-6. [DOI] [Google Scholar]
- 4.Tiwari JN, et al. Multicomponent electrocatalyst with ultralow Pt loading and high hydrogen evolution activity. Nat. Energy. 2018;3:773–782. doi: 10.1038/s41560-018-0209-x. [DOI] [Google Scholar]
- 5.Hunter BM, Gray HB, Müller AM. Earth-abundant heterogeneous water oxidation catalysts. Chem. Rev. 2016;116:14120–14136. doi: 10.1021/acs.chemrev.6b00398. [DOI] [PubMed] [Google Scholar]
- 6.Tiwari JN, et al. High-performance hydrogen evolution by Ru single atoms and nitrided-Ru nanoparticles implanted on N-doped graphitic sheet. Adv. Energy Mater. 2019;9:1900931. doi: 10.1002/aenm.201900931. [DOI] [Google Scholar]
- 7.Suen NT, et al. Electrocatalysis for the oxygen evolution reaction: recent development and future perspectives. Chem. Soc. Rev. 2017;46:337–365. doi: 10.1039/C6CS00328A. [DOI] [PubMed] [Google Scholar]
- 8.Luo J, et al. Water photolysis at 12.3% efficiency via perovskite photovoltaics and Earth-abundant catalysts. Science. 2014;345:1593. doi: 10.1126/science.1258307. [DOI] [PubMed] [Google Scholar]
- 9.Vij V, et al. Nickel-based electrocatalysts for energy-related applications: oxygen reduction, oxygen evolution, and hydrogen evolution reactions. ACS Catal. 2017;7:7196–7225. doi: 10.1021/acscatal.7b01800. [DOI] [Google Scholar]
- 10.Fan K, et al. Nickel–vanadium monolayer double hydroxide for efficient electrochemical water oxidation. Nat. Commun. 2016;7:11981. doi: 10.1038/ncomms11981. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 11.Sultan S, et al. Single atoms and clusters based nanomaterials for hydrogen evolution, oxygen evolution reactions, and Full Water Splitting. Adv. Energy Mater. 2019;9:1900624. doi: 10.1002/aenm.201900624. [DOI] [Google Scholar]
- 12.She ZW, et al. Combining theory and experiment in electrocatalysis: Insights into materials design. Science. 2017;355:eaad4998. doi: 10.1126/science.aad4998. [DOI] [PubMed] [Google Scholar]
- 13.Zhang B, et al. Homogeneously dispersed multimetal oxygen-evolving catalysts. Science. 2016;352:333. doi: 10.1126/science.aaf1525. [DOI] [PubMed] [Google Scholar]
- 14.Jiang J, et al. Highly active and durable electrocatalytic water oxidation by a NiB0.45/NiOx core-shell heterostructured nanoparticulate film. Nano Energy. 2017;38:175–184. doi: 10.1016/j.nanoen.2017.05.045. [DOI] [Google Scholar]
- 15.Kanan MW, Nocera DG. In situ formation of an oxygen-evolving catalyst in neutral water containing phosphate and Co<sup>2+</sup>. Science. 2008;321:1072. doi: 10.1126/science.1162018. [DOI] [PubMed] [Google Scholar]
- 16.Yuan C-Z, et al. Cobalt phosphate nanoparticles decorated with nitrogen-doped carbon layers as highly active and stable electrocatalysts for the oxygen evolution reaction. J. Mater. Chem. A. 2016;4:8155–8160. doi: 10.1039/C6TA01929C. [DOI] [Google Scholar]
- 17.Liu K, et al. High-performance transition metal phosphide alloy catalyst for oxygen evolution reaction. ACS Nano. 2018;12:158–167. doi: 10.1021/acsnano.7b04646. [DOI] [PubMed] [Google Scholar]
- 18.Padhi AK, Nanjundaswamy KS, Masquelier C, Okada S, Goodenough JB. Effect of structure on the Fe3+/Fe2+ couple in iron phosphates. J. Electrochem. Soc. 1997;144:1609–1613. doi: 10.1149/1.1837649. [DOI] [Google Scholar]
- 19.Wen Y, et al. Expanded graphite as superior anode for sodium-ion batteries. Nat. Commun. 2014;5:4033. doi: 10.1038/ncomms5033. [DOI] [PubMed] [Google Scholar]
- 20.Tiwari JN, et al. High-affinity-assisted nanoscale alloys as remarkable bifunctional catalyst for alcohol oxidation and oxygen reduction reactions. ACS Nano. 2017;11:7729–7735. doi: 10.1021/acsnano.7b01073. [DOI] [PubMed] [Google Scholar]
- 21.Georgakilas V, Perman JA, Tucek J, Zboril R. Broad family of carbon nanoallotropes: classification, chemistry, and applications of fullerenes, carbon dots, nanotubes, graphene, nanodiamonds, and combined superstructures. Chem. Rev. 2015;115:4744–4822. doi: 10.1021/cr500304f. [DOI] [PubMed] [Google Scholar]
- 22.Fei H, et al. General synthesis and definitive structural identification of MN4C4 single-atom catalysts with tunable electrocatalytic activities. Nat. Catal. 2018;1:63–72. doi: 10.1038/s41929-017-0008-y. [DOI] [Google Scholar]
- 23.Sultan S, et al. Highly efficient oxygen reduction reaction activity of graphitic tube encapsulating nitrided CoxFey alloy. Adv. Energy Mater. 2018;8:1801002. doi: 10.1002/aenm.201801002. [DOI] [Google Scholar]
- 24.Fabbri E, et al. Dynamic surface self-reconstruction is the key of highly active perovskite nano-electrocatalysts for water splitting. Nat. Mater. 2017;16:925. doi: 10.1038/nmat4938. [DOI] [PubMed] [Google Scholar]
- 25.Li H, et al. Synergetic interaction between neighbouring platinum monomers in CO2 hydrogenation. Nat. Nanotechnol. 2018;13:411–417. doi: 10.1038/s41565-018-0089-z. [DOI] [PubMed] [Google Scholar]
- 26.Bunău O, Joly Y. Self-consistent aspects of x-ray absorption calculations. J. Phys. Condens. Matter. 2009;21:345501. doi: 10.1088/0953-8984/21/34/345501. [DOI] [PubMed] [Google Scholar]
- 27.Bourke JD, Chantler CT, Joly Y. FDMX: extended X-ray absorption fine structure calculations using the finite difference method. J. Synchrotron Radiat. 2016;23:551–559. doi: 10.1107/S1600577516001193. [DOI] [PubMed] [Google Scholar]
- 28.Cobo S, et al. A Janus cobalt-based catalytic material for electro-splitting of water. Nat. Mater. 2012;11:802. doi: 10.1038/nmat3385. [DOI] [PubMed] [Google Scholar]
- 29.Liu W, et al. A highly active and stable hydrogen evolution catalyst based on pyrite-structured cobalt phosphosulfide. Nat. Commun. 2016;7:10771. doi: 10.1038/ncomms10771. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 30.Jiao L, Zhou Y-X, Jiang H-L. Metal–organic framework-based CoP/reduced graphene oxide: high-performance bifunctional electrocatalyst for overall water splitting. Chem. Sci. 2016;7:1690–1695. doi: 10.1039/C5SC04425A. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 31.You B, Sun Y. Hierarchically porous nickel sulfide multifunctional superstructures. Adv. Energy Mater. 2016;6:1502333. doi: 10.1002/aenm.201502333. [DOI] [Google Scholar]
- 32.Xu X, Song F, Hu X. A nickel iron diselenide-derived efficient oxygen-evolution catalyst. Nat. Commun. 2016;7:12324. doi: 10.1038/ncomms12324. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 33.Amin BG, Swesi AT, Masud J, Nath M. CoNi2Se4 as an efficient bifunctional electrocatalyst for overall water splitting. Chem. Commun. 2017;53:5412–5415. doi: 10.1039/C7CC01489A. [DOI] [PubMed] [Google Scholar]
- 34.Zhang P, et al. Dendritic core-shell nickel-iron-copper metal/metal oxide electrode for efficient electrocatalytic water oxidation. Nat. Commun. 2018;9:381. doi: 10.1038/s41467-017-02429-9. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 35.Ng JWD, et al. Gold-supported cerium-doped NiOx catalysts for water oxidation. Nat. Energy. 2016;1:16053. doi: 10.1038/nenergy.2016.53. [DOI] [Google Scholar]
- 36.Hou Y, et al. Bioinspired molecular co-catalysts bonded to a silicon photocathode for solar hydrogen evolution. Nat. Mater. 2011;10:434. doi: 10.1038/nmat3008. [DOI] [PubMed] [Google Scholar]
- 37.Zhang R, et al. Engineering cobalt defects in cobalt oxide for highly efficient electrocatalytic oxygen evolution. ACS Catal. 2018;8:3803–3811. doi: 10.1021/acscatal.8b01046. [DOI] [Google Scholar]
- 38.Stevens MB, Trang CDM, Enman LJ, Deng J, Boettcher SW. Reactive Fe-sites in Ni/Fe (oxy)hydroxide are responsible for exceptional oxygen electrocatalysis activity. J. Am. Chem. Soc. 2017;139:11361–11364. doi: 10.1021/jacs.7b07117. [DOI] [PubMed] [Google Scholar]
- 39.Sun. W, et al. Effect of lattice strain on the electro-catalytic activity of IrO2 for water splitting. Chem. Commun. 2018;54:996–999. doi: 10.1039/C7CC09580E. [DOI] [PubMed] [Google Scholar]
- 40.Xiong D, Wang X, Li W, Liu L. Facile synthesis of iron phosphide nanorods for efficient and durable electrochemical oxygen evolution. Chem. Commun. 2016;52:8711–8714. doi: 10.1039/C6CC04151E. [DOI] [PubMed] [Google Scholar]
- 41.Zhang G, et al. Highly active and stable catalysts of phytic acid-derivative transition metal phosphides for full water splitting. J. Am. Chem. Soc. 2016;138:14686–14693. doi: 10.1021/jacs.6b08491. [DOI] [PubMed] [Google Scholar]
- 42.Pan Y, et al. Core–shell ZIF-8@ZIF-67-derived CoP nanoparticle-embedded N-doped carbon nanotube hollow polyhedron for efficient overall water splitting. J. Am. Chem. Soc. 2018;140:2610–2618. doi: 10.1021/jacs.7b12420. [DOI] [PubMed] [Google Scholar]
- 43.Ravel B, Newville M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 2005;12:537–541. doi: 10.1107/S0909049505012719. [DOI] [PubMed] [Google Scholar]
- 44.Kresse G, Furthmüller J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B. 1996;54:11169–11186. doi: 10.1103/PhysRevB.54.11169. [DOI] [PubMed] [Google Scholar]
- 45.Blöchl PE. Projector augmented-wave method. Phys. Rev. B. 1994;50:17953–17979. doi: 10.1103/PhysRevB.50.17953. [DOI] [PubMed] [Google Scholar]
- 46.Kresse G, Joubert D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B. 1999;59:1758–1775. doi: 10.1103/PhysRevB.59.1758. [DOI] [Google Scholar]
- 47.Perdew JP, Burke K, Ernzerhof M. Generalized gradient approximation made simple. Phys. Rev. Lett. 1996;77:3865–3868. doi: 10.1103/PhysRevLett.77.3865. [DOI] [PubMed] [Google Scholar]
- 48.Tkatchenko A, Scheffler M. Accurate molecular van der waals interactions from ground-state electron density and free-atom reference data. Phys. Rev. Lett. 2009;102:073005. doi: 10.1103/PhysRevLett.102.073005. [DOI] [PubMed] [Google Scholar]
- 49.Rossmeisl J, Logadottir A, Nørskov JK. Electrolysis of water on (oxidized) metal surfaces. Chem. Phys. 2005;319:178–184. doi: 10.1016/j.chemphys.2005.05.038. [DOI] [Google Scholar]
- 50.Man IC, et al. Universality in oxygen evolution electrocatalysis on oxide surfaces. ChemCatChem. 2011;3:1159–1165. doi: 10.1002/cctc.201000397. [DOI] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.
Supplementary Materials
Data Availability Statement
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request. The source data underlying Figs. 1a, c, 2e, f, 3a–f, and 4a, c–e, and Supplementary Figs. 6a, b, 7a, b, 9a, b, 10, 11a, 12a, b, 13a, b, 19a, b, 20a–c, 21a–d, 22a–d, 23, 24a, b, 29, and 30–37 are provided as a Source Data file.